High-Strength Interstitial Alloys
During nitriding of Mo powder. surface hardening of the sample due to the formation of b-MoN was observed. The sintered layer of S-MoN reduced the passage of nitrogen to the interior of the sample being completely nitrided and hence prevented it from only a thin layer of Mo powder was therefore com...