Thermal Diffusivity of Zinc Aluminum – Layered Double Hydroxide Using Photoflash Technique
Thermal diffusivity of zinc aluminum layered double hydroxide (Zn-Al-LDH) was measured by using photoflash technique. It used a simple camera flash and polyvinlidene diflouride (PVDF) film as signal generating source and detector respectively. Three series of sample were prepared at pH 7, 8 and...
| Main Author: | |
|---|---|
| Format: | Thesis |
| Language: | English English |
| Published: |
2009
|
| Subjects: | |
| Online Access: | http://psasir.upm.edu.my/id/eprint/5712/ http://psasir.upm.edu.my/id/eprint/5712/1/FS_2009_3_abstract.pdf |
| _version_ | 1848840175852978176 |
|---|---|
| author | Ghaziean, Maryam Ranjbar |
| author_facet | Ghaziean, Maryam Ranjbar |
| author_sort | Ghaziean, Maryam Ranjbar |
| building | UPM Institutional Repository |
| collection | Online Access |
| description | Thermal diffusivity of zinc aluminum layered double hydroxide (Zn-Al-LDH) was
measured by using photoflash technique. It used a simple camera flash and
polyvinlidene diflouride (PVDF) film as signal generating source and detector
respectively.
Three series of sample were prepared at pH 7, 8 and 10 and with molar ratios of Zn to Al
in a range from 2 to 6 (Zn/Al = 2, 3, 4, 5 and 6).
The ZnO peaks appeared in x-ray diffraction pattern for all samples except for samples
prepared at pH 7 with ratio 2 and 3 (Zn/Al = 2 and 3) and sample prepared at pH 8 with
ratio 4. The ZnO peaks observed were between 2 = 30° to 2 = 37°. Thermal diffusivity for all three series samples (pHs 7, 8 and 10) was measured at room
temperature. The thermal diffusivity for all three series of samples was found to increase
for the case of molar ratio 2 to 6.
The thermal diffusivity for Zn-Al-LDH at different ratios of Zn-Al-LDH increased with
increasing ratio of Zn to Al. The increasing of thermal diffusivity is due to increasing of
ZnO. Thermal diffusivity at pH 7, increased from 0.15 10−6m2 / s × to 0.22 10−6m2 / s × .
Thermal diffusivity of sample prepared at pH 8 increased from 0.16 10−6m2 / s × to
0.20 10−6m2 / s × while at pH 10, if increased from 0.20 10−6m2 / s × to 0.25 10−6m2 / s × .
Thermal diffusivity at pH 7 has the lowest value and at pH 10 has the highest value.
The sample prepared at pH 7 with ratio 4 (Zn/Al = 4) was heat-treated at different
temperature from 200°C to 600°C, prior to thermal diffusivity measurement at room
temperature.
In the case of heat treated samples, the thermal diffusivity increased from
0.25 10−6m2 / s × to 0.40 10−6m2 / s × with increasing treatment temperature. |
| first_indexed | 2025-11-15T07:23:10Z |
| format | Thesis |
| id | upm-5712 |
| institution | Universiti Putra Malaysia |
| institution_category | Local University |
| language | English English |
| last_indexed | 2025-11-15T07:23:10Z |
| publishDate | 2009 |
| recordtype | eprints |
| repository_type | Digital Repository |
| spelling | upm-57122013-05-27T07:24:37Z http://psasir.upm.edu.my/id/eprint/5712/ Thermal Diffusivity of Zinc Aluminum – Layered Double Hydroxide Using Photoflash Technique Ghaziean, Maryam Ranjbar Thermal diffusivity of zinc aluminum layered double hydroxide (Zn-Al-LDH) was measured by using photoflash technique. It used a simple camera flash and polyvinlidene diflouride (PVDF) film as signal generating source and detector respectively. Three series of sample were prepared at pH 7, 8 and 10 and with molar ratios of Zn to Al in a range from 2 to 6 (Zn/Al = 2, 3, 4, 5 and 6). The ZnO peaks appeared in x-ray diffraction pattern for all samples except for samples prepared at pH 7 with ratio 2 and 3 (Zn/Al = 2 and 3) and sample prepared at pH 8 with ratio 4. The ZnO peaks observed were between 2 = 30° to 2 = 37°. Thermal diffusivity for all three series samples (pHs 7, 8 and 10) was measured at room temperature. The thermal diffusivity for all three series of samples was found to increase for the case of molar ratio 2 to 6. The thermal diffusivity for Zn-Al-LDH at different ratios of Zn-Al-LDH increased with increasing ratio of Zn to Al. The increasing of thermal diffusivity is due to increasing of ZnO. Thermal diffusivity at pH 7, increased from 0.15 10−6m2 / s × to 0.22 10−6m2 / s × . Thermal diffusivity of sample prepared at pH 8 increased from 0.16 10−6m2 / s × to 0.20 10−6m2 / s × while at pH 10, if increased from 0.20 10−6m2 / s × to 0.25 10−6m2 / s × . Thermal diffusivity at pH 7 has the lowest value and at pH 10 has the highest value. The sample prepared at pH 7 with ratio 4 (Zn/Al = 4) was heat-treated at different temperature from 200°C to 600°C, prior to thermal diffusivity measurement at room temperature. In the case of heat treated samples, the thermal diffusivity increased from 0.25 10−6m2 / s × to 0.40 10−6m2 / s × with increasing treatment temperature. 2009 Thesis NonPeerReviewed application/pdf en http://psasir.upm.edu.my/id/eprint/5712/1/FS_2009_3_abstract.pdf Ghaziean, Maryam Ranjbar (2009) Thermal Diffusivity of Zinc Aluminum – Layered Double Hydroxide Using Photoflash Technique. Masters thesis, Universiti Putra Malaysia. Zinc coating - Case studies English |
| spellingShingle | Zinc coating - Case studies Ghaziean, Maryam Ranjbar Thermal Diffusivity of Zinc Aluminum – Layered Double Hydroxide Using Photoflash Technique |
| title | Thermal Diffusivity of Zinc Aluminum – Layered Double Hydroxide Using Photoflash Technique |
| title_full | Thermal Diffusivity of Zinc Aluminum – Layered Double Hydroxide Using Photoflash Technique |
| title_fullStr | Thermal Diffusivity of Zinc Aluminum – Layered Double Hydroxide Using Photoflash Technique |
| title_full_unstemmed | Thermal Diffusivity of Zinc Aluminum – Layered Double Hydroxide Using Photoflash Technique |
| title_short | Thermal Diffusivity of Zinc Aluminum – Layered Double Hydroxide Using Photoflash Technique |
| title_sort | thermal diffusivity of zinc aluminum – layered double hydroxide using photoflash technique |
| topic | Zinc coating - Case studies |
| url | http://psasir.upm.edu.my/id/eprint/5712/ http://psasir.upm.edu.my/id/eprint/5712/1/FS_2009_3_abstract.pdf |