Aluminum Deoxidation Equilibrium in Molten Fe–Co Alloys
Aluminum deoxidation equilibrium of molten Fe–Co alloy was experimentally measured using a chemical equilibrium method and numerically assessed using a sub-regular solution model based on Darken’s quadratic formalism and a Redlich-Kister type polynomial at 1873 K. It was found that the degree of oxy...