Through-thickness variations in recrystallization behavior in an Al-based ARB composite sheet
A composite sheet of commercially pure aluminum and an Al-0.3 wt.% Sc alloy (in the supersaturated solid solution condition) was produced by accumulative roll bonding at 200°C. The material was then subjected to isothermal annealing at 300°C for 1-30 minutes and cold water quenched. The transverse s...