Study On Fracture Toughness In Low Carbon Steel Using Compact Specimens With And Without Carburizing
Study on Fracture Toughness in Low Carbon Steel carries the objectives to analyze the effect on fracture toughness on Low Carbon Steel in two conditions; with and without carburizing. Other than that is to compare the effect on fracture toughness between carburizing and without carburizing. Carbo...
| id |
utem-4308 |
|---|---|
| recordtype |
eprints |
| spelling |
utem-43082015-05-28T02:41:03Z Study On Fracture Toughness In Low Carbon Steel Using Compact Specimens With And Without Carburizing Khairul Idzham, Hasni T Technology (General) TA Engineering (General). Civil engineering (General) Study on Fracture Toughness in Low Carbon Steel carries the objectives to analyze the effect on fracture toughness on Low Carbon Steel in two conditions; with and without carburizing. Other than that is to compare the effect on fracture toughness between carburizing and without carburizing. Carbon Steel type AISI 1020 is the selected material for this study. Compact Tension (CT) specimen is the type of specimen used for this study with standard constraint followed by ASTM E399. Ten specimens will be prepared through manufacturing processes and five of will be carburized using pack carburizing process. There are three types of testing methods will be conducted starts with Tensile Test to get the maximum load and yield strength for both conditions. Fatigue Pre-Cracking Test will be conducted after Tensile Test to prepare the specimens with pre-crack in the range of 2mm to 2.5mm. Next, Fracture Toughness Test is the last method to carry out to complete the finding of the study. Universal Testing Machine; Instron 8802 will be used to conduct all testing methods. The results between both conditions will be compared in analitical method in order to achieve the desired target of this study. UTeM 2008 Monograph NonPeerReviewed application/pdf http://eprints.utem.edu.my/4308/1/Study_On_Fracture_Toughness_In_Low_Carbon_Steel_Using_Compact...._-_24_pages.pdf application/pdf http://eprints.utem.edu.my/4308/2/Study_On_Fracture_Toughness_In_Low_Carbon_Steel_Using_Compact.._TA479.C37_.K42_2008.pdf http://library.utem.edu.my:8000/elmu/index.jsp?module=webopac-d&action=fullDisplayRetriever.jsp&szMaterialNo=0000051108 Khairul Idzham, Hasni (2008) Study On Fracture Toughness In Low Carbon Steel Using Compact Specimens With And Without Carburizing. Project Report. UTeM, Melaka, Malaysia. (Submitted) http://eprints.utem.edu.my/4308/ |
| repository_type |
Digital Repository |
| institution_category |
Local University |
| institution |
Universiti Teknikal Malaysia Melaka |
| building |
UTeM Institutional Repository |
| collection |
Online Access |
| topic |
T Technology (General) TA Engineering (General). Civil engineering (General) |
| spellingShingle |
T Technology (General) TA Engineering (General). Civil engineering (General) Khairul Idzham, Hasni Study On Fracture Toughness In Low Carbon Steel Using Compact Specimens With And Without Carburizing |
| description |
Study on Fracture Toughness in Low Carbon Steel carries the objectives to analyze the
effect on fracture toughness on Low Carbon Steel in two conditions; with and without
carburizing. Other than that is to compare the effect on fracture toughness between
carburizing and without carburizing. Carbon Steel type AISI 1020 is the selected
material for this study. Compact Tension (CT) specimen is the type of specimen used
for this study with standard constraint followed by ASTM E399. Ten specimens will be
prepared through manufacturing processes and five of will be carburized using pack
carburizing process. There are three types of testing methods will be conducted starts
with Tensile Test to get the maximum load and yield strength for both conditions.
Fatigue Pre-Cracking Test will be conducted after Tensile Test to prepare the specimens
with pre-crack in the range of 2mm to 2.5mm. Next, Fracture Toughness Test is the last
method to carry out to complete the finding of the study. Universal Testing Machine;
Instron 8802 will be used to conduct all testing methods. The results between both
conditions will be compared in analitical method in order to achieve the desired target
of this study. |
| format |
Monograph |
| author |
Khairul Idzham, Hasni |
| author_facet |
Khairul Idzham, Hasni |
| author_sort |
Khairul Idzham, Hasni |
| title |
Study On Fracture Toughness In Low Carbon Steel Using Compact Specimens With And Without Carburizing |
| title_short |
Study On Fracture Toughness In Low Carbon Steel Using Compact Specimens With And Without Carburizing |
| title_full |
Study On Fracture Toughness In Low Carbon Steel Using Compact Specimens With And Without Carburizing |
| title_fullStr |
Study On Fracture Toughness In Low Carbon Steel Using Compact Specimens With And Without Carburizing |
| title_full_unstemmed |
Study On Fracture Toughness In Low Carbon Steel Using Compact Specimens With And Without Carburizing |
| title_sort |
study on fracture toughness in low carbon steel using compact specimens with and without carburizing |
| publisher |
UTeM |
| publishDate |
2008 |
| url |
http://library.utem.edu.my:8000/elmu/index.jsp?module=webopac-d&action=fullDisplayRetriever.jsp&szMaterialNo=0000051108 http://library.utem.edu.my:8000/elmu/index.jsp?module=webopac-d&action=fullDisplayRetriever.jsp&szMaterialNo=0000051108 http://eprints.utem.edu.my/4308/1/Study_On_Fracture_Toughness_In_Low_Carbon_Steel_Using_Compact...._-_24_pages.pdf http://eprints.utem.edu.my/4308/2/Study_On_Fracture_Toughness_In_Low_Carbon_Steel_Using_Compact.._TA479.C37_.K42_2008.pdf |
| first_indexed |
2018-09-05T10:20:54Z |
| last_indexed |
2018-09-05T10:20:54Z |
| _version_ |
1610762530440871936 |