Effect Of Chromium Carbide (Cr23C6) Formation On Microstructure And Corrosion Passivity Behavior Of AISI 304 Stainless Steel

Effect Of Chromium Carbide (Cr23C6) Formation On Microstructure And Corrosion Passivity Behavior Of AISI 304 Stainless Steel

This project aimed to study the effect of chromium carbide, Cr23C6 formation on the microstructure and corrosion resistance behavior of AISI 304 stainless steels in 3.5 % NaCl solution. Five specimens of AISI 304, 15 mm x 15 mm x 2 mm each size with various heating time, 5 seconds, 10 seconds, 20...

Full description

Bibliographic Details
Main Author: Siti Faizah , Mad Asasaari
Format: Monograph
Published: UTeM 2010
Subjects:
T Technology (General)
TA Engineering (General). Civil engineering (General)
Online Access:http://library.utem.edu.my:8000/elmu/index.jsp?module=webopac-d&action=graphicFullDisplayRetriever.jsp&szMaterialNo=0000063485
http://library.utem.edu.my:8000/elmu/index.jsp?module=webopac-d&action=graphicFullDisplayRetriever.jsp&szMaterialNo=0000063485
http://eprints.utem.edu.my/2467/1/Effect_Of_Chromium_Carbide_%28Cr23C6%29_Formation_On_Microstructure_And_Corrosion_Passivity_Behavior_Of_AISI_304_Stainless_Steel_-_24_pages.pdf
http://eprints.utem.edu.my/2467/2/Effect_Of_Chromium_Carbide_%28Cr23C6%29_Formation_On_Microstructure_And_Corrosion_Passivity_Behavior_Of_AISI_304_Stainless_Steel_-_Full_Text.pdf
id utem-2467
recordtype eprints
spelling utem-24672015-05-28T02:29:17Z Effect Of Chromium Carbide (Cr23C6) Formation On Microstructure And Corrosion Passivity Behavior Of AISI 304 Stainless Steel Siti Faizah , Mad Asasaari T Technology (General) TA Engineering (General). Civil engineering (General) This project aimed to study the effect of chromium carbide, Cr23C6 formation on the microstructure and corrosion resistance behavior of AISI 304 stainless steels in 3.5 % NaCl solution. Five specimens of AISI 304, 15 mm x 15 mm x 2 mm each size with various heating time, 5 seconds, 10 seconds, 20 seconds, 40 seconds, and 60 seconds respectively are used. All specimens are immersed in 3.5 % NaCl solution, for cyclic potentiodynamic polarization technique with a scan rate of 0.5 mV/s, then, the corrosion behavior of AISI 304 was analyzed. The Cr23C6 formation on the microstructure of AISI 304 to resist pitting corrosion is studied by exposed the specimens to the heating time and five different pH solutions which is pH 3, pH 5, pH 7, pH 9, and pH 12. The number of Cr23C6 formation is high at 60 s of heating time by observing on the optical microscope. X-ray diffraction (XRD) analysis is used to study the Cr23C6 formation that presence on the structure of AISI 304. The increase in number and size of Cr23C6 performed in the structure of AISI 304, the corrosion resistance of the specimens decrease. At high heating time and more acidic solution, the pitting corrosion attack is increased. Based on the cyclic polarization scan, it is clear that at 60 s, the value of high potential stress is 0.325 V, decreases from 0.420 V as performed by 5 s heating time. While for the effect of pH solution, specimen immersed in pH 3 shows the lowest potential, 0.32 V as performed by specimen number one. UTeM 2010 Monograph NonPeerReviewed application/pdf http://eprints.utem.edu.my/2467/1/Effect_Of_Chromium_Carbide_%28Cr23C6%29_Formation_On_Microstructure_And_Corrosion_Passivity_Behavior_Of_AISI_304_Stainless_Steel_-_24_pages.pdf application/pdf http://eprints.utem.edu.my/2467/2/Effect_Of_Chromium_Carbide_%28Cr23C6%29_Formation_On_Microstructure_And_Corrosion_Passivity_Behavior_Of_AISI_304_Stainless_Steel_-_Full_Text.pdf http://library.utem.edu.my:8000/elmu/index.jsp?module=webopac-d&action=graphicFullDisplayRetriever.jsp&szMaterialNo=0000063485 Siti Faizah , Mad Asasaari (2010) Effect Of Chromium Carbide (Cr23C6) Formation On Microstructure And Corrosion Passivity Behavior Of AISI 304 Stainless Steel. Project Report. UTeM, Melaka, Malaysia. (Submitted) http://eprints.utem.edu.my/2467/
repository_type Digital Repository
institution_category Local University
institution Universiti Teknikal Malaysia Melaka
building UTeM Institutional Repository
collection Online Access
topic T Technology (General)
TA Engineering (General). Civil engineering (General)
spellingShingle T Technology (General)
TA Engineering (General). Civil engineering (General)
Siti Faizah , Mad Asasaari
Effect Of Chromium Carbide (Cr23C6) Formation On Microstructure And Corrosion Passivity Behavior Of AISI 304 Stainless Steel
description This project aimed to study the effect of chromium carbide, Cr23C6 formation on the microstructure and corrosion resistance behavior of AISI 304 stainless steels in 3.5 % NaCl solution. Five specimens of AISI 304, 15 mm x 15 mm x 2 mm each size with various heating time, 5 seconds, 10 seconds, 20 seconds, 40 seconds, and 60 seconds respectively are used. All specimens are immersed in 3.5 % NaCl solution, for cyclic potentiodynamic polarization technique with a scan rate of 0.5 mV/s, then, the corrosion behavior of AISI 304 was analyzed. The Cr23C6 formation on the microstructure of AISI 304 to resist pitting corrosion is studied by exposed the specimens to the heating time and five different pH solutions which is pH 3, pH 5, pH 7, pH 9, and pH 12. The number of Cr23C6 formation is high at 60 s of heating time by observing on the optical microscope. X-ray diffraction (XRD) analysis is used to study the Cr23C6 formation that presence on the structure of AISI 304. The increase in number and size of Cr23C6 performed in the structure of AISI 304, the corrosion resistance of the specimens decrease. At high heating time and more acidic solution, the pitting corrosion attack is increased. Based on the cyclic polarization scan, it is clear that at 60 s, the value of high potential stress is 0.325 V, decreases from 0.420 V as performed by 5 s heating time. While for the effect of pH solution, specimen immersed in pH 3 shows the lowest potential, 0.32 V as performed by specimen number one.
format Monograph
author Siti Faizah , Mad Asasaari
author_facet Siti Faizah , Mad Asasaari
author_sort Siti Faizah , Mad Asasaari
title Effect Of Chromium Carbide (Cr23C6) Formation On Microstructure And Corrosion Passivity Behavior Of AISI 304 Stainless Steel
title_short Effect Of Chromium Carbide (Cr23C6) Formation On Microstructure And Corrosion Passivity Behavior Of AISI 304 Stainless Steel
title_full Effect Of Chromium Carbide (Cr23C6) Formation On Microstructure And Corrosion Passivity Behavior Of AISI 304 Stainless Steel
title_fullStr Effect Of Chromium Carbide (Cr23C6) Formation On Microstructure And Corrosion Passivity Behavior Of AISI 304 Stainless Steel
title_full_unstemmed Effect Of Chromium Carbide (Cr23C6) Formation On Microstructure And Corrosion Passivity Behavior Of AISI 304 Stainless Steel
title_sort effect of chromium carbide (cr23c6) formation on microstructure and corrosion passivity behavior of aisi 304 stainless steel
publisher UTeM
publishDate 2010
url http://library.utem.edu.my:8000/elmu/index.jsp?module=webopac-d&action=graphicFullDisplayRetriever.jsp&szMaterialNo=0000063485
http://library.utem.edu.my:8000/elmu/index.jsp?module=webopac-d&action=graphicFullDisplayRetriever.jsp&szMaterialNo=0000063485
http://eprints.utem.edu.my/2467/1/Effect_Of_Chromium_Carbide_%28Cr23C6%29_Formation_On_Microstructure_And_Corrosion_Passivity_Behavior_Of_AISI_304_Stainless_Steel_-_24_pages.pdf
http://eprints.utem.edu.my/2467/2/Effect_Of_Chromium_Carbide_%28Cr23C6%29_Formation_On_Microstructure_And_Corrosion_Passivity_Behavior_Of_AISI_304_Stainless_Steel_-_Full_Text.pdf
first_indexed 2018-09-05T10:06:08Z
last_indexed 2018-09-05T10:06:08Z
_version_ 1610761600915996672

Similar Items