Synthesis and characterisation of poly(hydroxamic acid and amidoxime) grafted sago starch cheating resin for extraction of some metal ions
Sago starch (AGU, anhydro glucose unit) was used to prepared a poly(hydroxamic acid-amidoxime) chelating resin. Methyl acrylate (MA) and acrylonitrile (AN) were firstly graft copolymerized onto sago starch by using a free radical initiating process in which eerie ammonium nitrate was used as an in...
| Main Author: | |
|---|---|
| Format: | Thesis |
| Language: | English |
| Published: |
2010
|
| Subjects: | |
| Online Access: | http://eprints.ums.edu.my/17502/ http://eprints.ums.edu.my/17502/1/Synthesis%20and%20characterisation.pdf |
| id |
ums-17502 |
|---|---|
| recordtype |
eprints |
| spelling |
ums-175022017-11-20T02:15:53Z http://eprints.ums.edu.my/17502/ Synthesis and characterisation of poly(hydroxamic acid and amidoxime) grafted sago starch cheating resin for extraction of some metal ions Tan, Boon Teong QD Chemistry Sago starch (AGU, anhydro glucose unit) was used to prepared a poly(hydroxamic acid-amidoxime) chelating resin. Methyl acrylate (MA) and acrylonitrile (AN) were firstly graft copolymerized onto sago starch by using a free radical initiating process in which eerie ammonium nitrate was used as an initiator. The percentage of grafting was significantly dependent upon the concentration d mineral add (H₂SO₄), eerie ammonium nitrate (CAN), MA, AN, as well as the reaction temperature and period. The highest yield was obtained when the concentrations of H₂SO₄, CAN, AN and MA were used at 0.7090 mol/L. 4 x 10⁻³) moI/L, 0.6016 mol/L and 0.4392 moI/L, respectively. The optimum temperature and reaction period were 50⁰C and 90 min, respectively. The conversion of ester and nitrile groups of the poIy(methyl acrylate-co-acrylonitrile) (PMA-co-AN) grafted AGU Into hydroxamie acid and amidoxime functional groups was then prepared via treatment of hydroxylamine under alkaline solution. The optimum poly(hydroxamic acidamidoxime) (PHA-PA) chelating resin was obtained when concentration of hydroxylamine hydrochloride was used at 0.8634 mol/L; reaction temperature at 75⁰C; 2 hours of reaction period; while the varying pH value was pH 13. The optimization of the PHA-PA chelating resin was evaluated by measured the sorption capacity of the resin towards copper metal ion with batch method. The PMA-co-AN grafted AGU and PHA-PA were characterized by FT-IR spectroscopy. The chelating behavior of the prepared resin towards cadmium, chromium, copper and zinc metal ions were investigated by using batch method. The binding capacities of the optimum chelating resin towards these metal ions were observed and it exhibited high sorption capacity for copper which observed at 3.576 mmol/g, at pH 6 after 24 hours of reaction period. The maximum binding capacities of the optimum chelating resin towards cadmium, chromium and zinc metal ions were observed at l.585 mmol/g, 1.658 mmol/g and 1.817 mmol/g, respectively; at pH 6 after 24 hours of reaction period. The optimum resin obtained also showed that it was capable to form a chelate complex when reacted with metal ions in trace level. 2010 Thesis NonPeerReviewed text en http://eprints.ums.edu.my/17502/1/Synthesis%20and%20characterisation.pdf Tan, Boon Teong (2010) Synthesis and characterisation of poly(hydroxamic acid and amidoxime) grafted sago starch cheating resin for extraction of some metal ions. Masters thesis, Universiti Malaysia Sabah. |
| repository_type |
Digital Repository |
| institution_category |
Local University |
| institution |
Universiti Sabah Malaysia |
| building |
UMS Institutional Repository |
| collection |
Online Access |
| language |
English |
| topic |
QD Chemistry |
| spellingShingle |
QD Chemistry Tan, Boon Teong Synthesis and characterisation of poly(hydroxamic acid and amidoxime) grafted sago starch cheating resin for extraction of some metal ions |
| description |
Sago starch (AGU, anhydro glucose unit) was used to prepared a poly(hydroxamic acid-amidoxime) chelating resin. Methyl acrylate (MA) and acrylonitrile (AN) were
firstly graft copolymerized onto sago starch by using a free radical initiating process
in which eerie ammonium nitrate was used as an initiator. The percentage of
grafting was significantly dependent upon the concentration d mineral add
(H₂SO₄), eerie ammonium nitrate (CAN), MA, AN, as well as the reaction
temperature and period. The highest yield was obtained when the concentrations
of H₂SO₄, CAN, AN and MA were used at 0.7090 mol/L. 4 x 10⁻³) moI/L, 0.6016
mol/L and 0.4392 moI/L, respectively. The optimum temperature and reaction
period were 50⁰C and 90 min, respectively. The conversion of ester and nitrile
groups of the poIy(methyl acrylate-co-acrylonitrile) (PMA-co-AN) grafted AGU Into
hydroxamie acid and amidoxime functional groups was then prepared via treatment
of hydroxylamine under alkaline solution. The optimum poly(hydroxamic acidamidoxime)
(PHA-PA) chelating resin was obtained when concentration of
hydroxylamine hydrochloride was used at 0.8634 mol/L; reaction temperature at 75⁰C; 2 hours of reaction period; while the varying pH value was pH 13. The
optimization of the PHA-PA chelating resin was evaluated by measured the sorption
capacity of the resin towards copper metal ion with batch method. The PMA-co-AN
grafted AGU and PHA-PA were characterized by FT-IR spectroscopy. The chelating
behavior of the prepared resin towards cadmium, chromium, copper and zinc metal
ions were investigated by using batch method. The binding capacities of the
optimum chelating resin towards these metal ions were observed and it exhibited
high sorption capacity for copper which observed at 3.576 mmol/g, at pH 6 after 24
hours of reaction period. The maximum binding capacities of the optimum chelating
resin towards cadmium, chromium and zinc metal ions were observed at l.585
mmol/g, 1.658 mmol/g and 1.817 mmol/g, respectively; at pH 6 after 24 hours of
reaction period. The optimum resin obtained also showed that it was capable to
form a chelate complex when reacted with metal ions in trace level. |
| format |
Thesis |
| author |
Tan, Boon Teong |
| author_facet |
Tan, Boon Teong |
| author_sort |
Tan, Boon Teong |
| title |
Synthesis and characterisation of
poly(hydroxamic acid and amidoxime)
grafted sago starch cheating resin
for extraction of some metal ions |
| title_short |
Synthesis and characterisation of
poly(hydroxamic acid and amidoxime)
grafted sago starch cheating resin
for extraction of some metal ions |
| title_full |
Synthesis and characterisation of
poly(hydroxamic acid and amidoxime)
grafted sago starch cheating resin
for extraction of some metal ions |
| title_fullStr |
Synthesis and characterisation of
poly(hydroxamic acid and amidoxime)
grafted sago starch cheating resin
for extraction of some metal ions |
| title_full_unstemmed |
Synthesis and characterisation of
poly(hydroxamic acid and amidoxime)
grafted sago starch cheating resin
for extraction of some metal ions |
| title_sort |
synthesis and characterisation of
poly(hydroxamic acid and amidoxime)
grafted sago starch cheating resin
for extraction of some metal ions |
| publishDate |
2010 |
| url |
http://eprints.ums.edu.my/17502/ http://eprints.ums.edu.my/17502/1/Synthesis%20and%20characterisation.pdf |
| first_indexed |
2018-09-05T09:16:31Z |
| last_indexed |
2018-09-05T09:16:31Z |
| _version_ |
1610758479544320000 |