Microstructure and Properties of Aluminium-Aluminium Oxide Graded Composite Materials
In this research works, four-layered aluminium-aluminium oxide (Al-Al2O3) graded composite materials were fabricated using powder metallurgy (PM) method. In processing, metal-ceramic graded composite materials of 0%, 10%, 20% and 30% weight percentage of ceramic concentration were prepared under 30...
| Main Authors: | , , , , , |
|---|---|
| Format: | Conference or Workshop Item |
| Language: | English English |
| Published: |
2017
|
| Subjects: | |
| Online Access: | http://umpir.ump.edu.my/id/eprint/19639/ http://umpir.ump.edu.my/id/eprint/19639/1/fkp-2017-fariza-Microstructure%20and%20properties%20of%20aluminium-aluminium1.pdf http://umpir.ump.edu.my/id/eprint/19639/2/fkp-2017-fariza-Microstructure%20and%20properties%20of%20aluminium-aluminium.pdf |
| Summary: | In this research works, four-layered aluminium-aluminium oxide (Al-Al2O3) graded composite materials were fabricated using powder metallurgy (PM) method. In processing, metal-ceramic graded composite materials of 0%, 10%, 20% and 30% weight percentage of ceramic concentration were prepared under 30 ton compaction load using a cylindrical die-punch set made of steel. After that, two-step pressureless sintering was carried out at sintering temperature and time 600oC and 3 hours respectively. It was observed that the sintered cylindrical specimens of 30 mm diameter were prepared successfully. The graded composite specimens were analysed and the properties such as density, microstructure and hardness were measured. It was found that after sintering process, the diameter of the graded cylindrical structure was decreased. Using both Archimedes method and rule of mixture (ROM), he density of structure was measured. The obtained results revealed that the microvickers hardness was increased as the ceramic component increases in the graded layer. Moreover, it was observed that the interface of the graded structure is clearly distinguished within the multilayer stack and the ceramic particles are almost uniformly distributed in the Al matrix. |
|---|