Corrosion behavior of deformed steel for automobile parts in various environments
Corrosion behavior of three types of deformed steel sheets of automobile part have been studied as a function of shapes namely flat and curved. Three different solutions were chosen; chloride, phosphate and carbonate for the corrosion tests. A correlation between the shapes, types and environments t...
| Main Author: | |
|---|---|
| Format: | Thesis |
| Language: | English |
| Published: |
2008
|
| Subjects: | |
| Online Access: | http://eprints.utm.my/9629/ http://eprints.utm.my/9629/1/ZainalZakariaPFKKKSA2010.pdf |
| _version_ | 1848891897809993728 |
|---|---|
| author | Abd. Karim, Mohd. Fauzi |
| author_facet | Abd. Karim, Mohd. Fauzi |
| author_sort | Abd. Karim, Mohd. Fauzi |
| building | UTeM Institutional Repository |
| collection | Online Access |
| description | Corrosion behavior of three types of deformed steel sheets of automobile part have been studied as a function of shapes namely flat and curved. Three different solutions were chosen; chloride, phosphate and carbonate for the corrosion tests. A correlation between the shapes, types and environments to corrosion protection were established by employing electrochemical test using potentiodynamic polarization. Cyclic corrosion test was also performed as comparison to the electrochemical test. An almost consistent correlation was found to exist between specimen shapes and corrosion rate depends on types and exposure environments. Generally, as received samples showed the highest corrosion rate for JSC 270F type while flat shape showed the highest corrosion rate for JAC 270F and curved shape showed the highest corrosion rate for JSH 370W in all environments respectively. On the other hand phosphate solution was found to be the most corrosive environment to these three types of automobile parts. |
| first_indexed | 2025-11-15T21:05:16Z |
| format | Thesis |
| id | utm-9629 |
| institution | Universiti Teknologi Malaysia |
| institution_category | Local University |
| language | English |
| last_indexed | 2025-11-15T21:05:16Z |
| publishDate | 2008 |
| recordtype | eprints |
| repository_type | Digital Repository |
| spelling | utm-96292018-06-26T08:32:53Z http://eprints.utm.my/9629/ Corrosion behavior of deformed steel for automobile parts in various environments Abd. Karim, Mohd. Fauzi TJ Mechanical engineering and machinery Corrosion behavior of three types of deformed steel sheets of automobile part have been studied as a function of shapes namely flat and curved. Three different solutions were chosen; chloride, phosphate and carbonate for the corrosion tests. A correlation between the shapes, types and environments to corrosion protection were established by employing electrochemical test using potentiodynamic polarization. Cyclic corrosion test was also performed as comparison to the electrochemical test. An almost consistent correlation was found to exist between specimen shapes and corrosion rate depends on types and exposure environments. Generally, as received samples showed the highest corrosion rate for JSC 270F type while flat shape showed the highest corrosion rate for JAC 270F and curved shape showed the highest corrosion rate for JSH 370W in all environments respectively. On the other hand phosphate solution was found to be the most corrosive environment to these three types of automobile parts. 2008-12 Thesis NonPeerReviewed application/pdf en http://eprints.utm.my/9629/1/ZainalZakariaPFKKKSA2010.pdf Abd. Karim, Mohd. Fauzi (2008) Corrosion behavior of deformed steel for automobile parts in various environments. Masters thesis, Universiti Teknologi Malaysia, Faculty of Mechanical Engineering. |
| spellingShingle | TJ Mechanical engineering and machinery Abd. Karim, Mohd. Fauzi Corrosion behavior of deformed steel for automobile parts in various environments |
| title | Corrosion behavior of deformed steel for automobile parts in various environments |
| title_full | Corrosion behavior of deformed steel for automobile parts in various environments |
| title_fullStr | Corrosion behavior of deformed steel for automobile parts in various environments |
| title_full_unstemmed | Corrosion behavior of deformed steel for automobile parts in various environments |
| title_short | Corrosion behavior of deformed steel for automobile parts in various environments |
| title_sort | corrosion behavior of deformed steel for automobile parts in various environments |
| topic | TJ Mechanical engineering and machinery |
| url | http://eprints.utm.my/9629/ http://eprints.utm.my/9629/1/ZainalZakariaPFKKKSA2010.pdf |