The effect of thermal to the diameter of Nd : YAG crystal during growth process
The Nd:YAG crystal grown in a pure argon atmosphere using Czochralski method with ADC (Automatic Diameter Control) r.f. heating is reported.The conditions required to grow Nd:YAG single crystals are described. The pull rate was 0.75 mm/h with a seed rotation of 15 rpm. All runs were made with growth...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Faculty of Science University Teknologi Malaysia
2008
|
| Subjects: | |
| Online Access: | http://eprints.utm.my/8547/ http://eprints.utm.my/8547/1/WanHairulAnuarKamaruddin2008_TheEffectOfThermalTo.pdf |
| Summary: | The Nd:YAG crystal grown in a pure argon atmosphere using Czochralski method with ADC (Automatic Diameter Control) r.f. heating is reported.The conditions required to grow Nd:YAG single crystals are described. The pull rate was 0.75 mm/h with a seed rotation of 15 rpm. All runs were made with growth along the c-axis <111> direction. |
|---|