Microwave irradiation technique for synthesis of zeolite A
Synthesization of Zeolite A from colloidal silica was performed by means of microwave irradiation technique under different conditions and was compared with hydrothermal technique. The molar composition at 1 Al203: 1.96 SiO2: 3.165 Na2O: 128 H2O. X-Ray Diffraction (XRD) and Scanning Electron Microsc...
| Main Authors: | , , , |
|---|---|
| Format: | Conference or Workshop Item |
| Language: | English |
| Published: |
2007
|
| Subjects: | |
| Online Access: | http://eprints.utm.my/5697/ http://eprints.utm.my/5697/1/H.M.Razif2007_MicrowaveIrradiationTechniqueForSynthesisOfZeoliteA.pdf |
| Summary: | Synthesization of Zeolite A from colloidal silica was performed by means of microwave irradiation technique under different conditions and was compared with hydrothermal technique. The molar composition at 1 Al203: 1.96 SiO2: 3.165 Na2O: 128 H2O. X-Ray Diffraction (XRD) and Scanning Electron Microscope (SEM) were used to characterize zeolite A. XRD results for all samples demonstrated a typical diffraction peak of zeolite A. SEM images show almost no-different in crystal size of zeolite A synthesized by microwave irradiation and hydrothermal technique. Thus, we concluded that crystallization of zeolite A has occurred rapidly by microwave irradiation. Microwave technique is a time and energy saving due to crystallization time and higher heating rate as compared to hydrothermal technique. |
|---|