Failure behavior of sandwich honeycomb composite beam containing crack at the skin

QR Code

Failure behavior of sandwich honeycomb composite beam containing crack at the skin

Skin crack defects can develop in sandwich honeycomb composite structures during service life due to static and impact loads. In this study, the fracture behavior of sandwich honeycomb composite (SHC) beams containing crack at the skin was investigated experimentally and numerically under four-point...

Full description

Bibliographic Details
Main Authors:	Al-Fasih, M. Y., Kueh, A. B. H., W.Ibrahim, M. H.
Format:	Article
Language:	English
Published:	Public Library of Science 2020
Subjects:	T Technology (General) TA401-492 Materials of engineering and construction. Mechanics of materials
Online Access:	http://eprints.uthm.edu.my/4989/ http://eprints.uthm.edu.my/4989/1/AJ%202020%20%2865%29.pdf

Similar Items

The Velocity Impact Response Of Filled And Unfilled Polypropylene Honeycomb Core Sandwich Structure
by: Ahmad, Mohamad Ibrahim
Published: (2016)

Mode i stress intensity factors of slanted cracks
by: Ismail, Al Emran, et al.
Published: (2017)

Structural performance of precast self-compacting concrete beam consisiting banana skin powder and coir fibre under flexural load
by: Tahir, Muhammad
Published: (2018)

Failure mechanism of prepacked concrete
by: Abdul Awal, A. S. M.
Published: (1988)

Sputter deposition and characterization of metal sandwiched indium tin oxide/silicon for solar cell application
by: Kabiru Isiyaku, Aliyu
Published: (2020)

Crack propagation trajectory for kenaf fibre composite under quasi static loading
by: Nurul Alya Zahari, Nurul Alya Zahari, et al.
Published: (2020)

Oblique impact behavior of unidirectional natural fiber reinforced composites
by: Salim, Yusuf, et al.
Published: (2018)

Structural behaviour of precast concrete sandwich panel using recycled aggregate concrete under transverse load
by: Al. Mabrouk Khalifa, Hamza Masaud
Published: (2013)

Abrasive wear failure analysis of tungsten carbide hard facing on carbon steel blade
by: Mohd Tobi, A. L., et al.
Published: (2017)

Stress intensity factors for surface cracks in round bar under single and combined loadings
by: Ismail, Al Emran, et al.
Published: (2012)

Experimental study on ballistic resistance of sandwich panel protection structure with kenaf foam as a core material against small arm bullet
by: Zainol Abidin, Mohamad Hafiz, et al.
Published: (2013)

Identifying the Crack Nature Using b-Value Acoustic Emission Signal Analysis
by: Saiful Bahari, Miera, et al.
Published: (2020)

Finite element analysis of j-integral for surface cracks in round bars under combined mode i loading
by: Ismail, Al Emran, et al.
Published: (2017)

EBB307 Failure Analysis And Non-Destructive Testing 2024
by: PPKBSM, Pusat Pengajian Kejuruteraan Bahan dan Sumber Mineral
Published: (2024)

Evaluation of heat of hydration of concrete containing high volume palm oil fuel ash
by: Abdul Awal, A.S.M., et al.
Published: (2013)

Performance of composite sand cement brick containing recycled concrete aggregate and waste polyethylene terepthalate
by: Azmi, Nurul Bazilah
Published: (2018)

EBP400-3 - PRODUCT DESIGN AND FAILURE ANALYSIS - NOVEMBER 2008.
by: PPKBSM, Pusat Pengajian Kejuruteraan Bahan dan Sumber Mineral
Published: (2008)

Solving cracking phenomenon in premium transparent toilet soap production using Stretched LLDPE Film Wrap
by: Mat Sharif, Zainon, et al.
Published: (2017)

EBB405-3 - FAILURE ANALYSIS AND NON-DESTRUCTIVE TESTING - NOVEMBER 2008.
by: PPKBSM, Pusat Pengajian Kejuruteraan Bahan dan Sumber Mineral
Published: (2008)

Analysing method for acoustic emission clustering system on reinforced concrete beam
by: Saiful Bahari, Nur Amira Afiza
Published: (2018)

Performance evaluation of concrete containing high volume palm oil fuel ash exposed to elevated temperature
by: Abdul Awal, A.S.M., et al.
Published: (2015)

A new empirical model to predict stress intensity factor for double interacting surface cracks located in hollow cylinder
by: Fakhri, Omar Mohammed
Published: (2021)

Effect Of Leaching Agents On Polyurethane Composite Scaffolds Containing Bioactive Glass
by: Lee, Angie
Published: (2017)

EBP311 Polymer Analytical Methods And Failure Analysis SEM 2 SA 2023.2024
by: PPKBSM, Pusat Pengajian Kejuruteraan Bahan dan Sumber Mineral
Published: (2024)

EBP311 Polymer Analytical Methods And Failure Analysis SEM 2 SA 2022.2023
by: PPKBSM, Pusat Pengajian Kejuruteraan Bahan dan Sumber Mineral
Published: (2023)

EBP311 - Polymer Analytical Methods And Failure Analysis
by: PPKBSM, Pusat Pengajian Kejuruteraan Bahan dan Sumber Mineral

EBB307 - Failure Analysis And Non-Destructive Testing
by: PPKBSM, Pusat Pengajian Kejuruteraan Bahan dan Sumber Mineral

Time Domain Reflection Method To Detect Copper Wire Micro Crack Weld Defect
by: Robin, Ong Su Kiat
Published: (2016)

Preliminary Study On Bioceramics Containing Gallic Acid
by: Kamarudin, Farrah Izzatul Ain
Published: (2020)

Strength and water permeability of concrete containing coal bottom ash as cement and fine aggregate replacement material
by: Basirun, Nurul Fasihah
Published: (2019)

Self compacting concrete containing polypropylene fibre and its behaviour as wall panel under cyclic load
by: Khalaf Al-Alwani, Anas Qasim
Published: (2018)

Assessing low thermal conductivity of bricks which contain rice husk, corn cob and waste tea as an additive material
by: Mat Saman, Nor Sarwani
Published: (2017)

Strength prediction and durability performance of concrete containing coal bottom ash as supplementary cementitious material under aggressive environment
by: Ali, Sajjad
Published: (2019)

Sound absorption of lightweight brick containing expanded polystyrene beads and palm oil fuel ash
by: Adnan1, S H, et al.
Published: (2020)

Experimental study on ballistic resistance of sandwich panel protection structure with kenaf foam as a core material against small arm bullet
by: Zainol Abidin, Mohamad Hafiz, et al.
Published: (2013)

Effects of adhesion failure on moisture damage of warm mix asphalt containing cecabase additive
by: Khan Kakar, Muhammad Rafiq
Published: (2015)

Performance of modified mortar containing epoxy
by: Abdul Latip, Arisya, et al.
Published: (2020)

Behavior of chopped strand mat and woven roving under bending
by: Tajul Arifin, Ahmad Mubarak, et al.
Published: (2014)

Electrophoretic deposition of Ba0.5Sr0.5Co0.8Fe0.2O3−∞SDC carbonate composite coating on solid oxide fuel cell interconnect
by: Tan, K. H., et al.
Published: (2018)

Fabrication And Optimization Of Cyanoacrylate Nanocomposites For Ion Beam Etching Process On Hard Disk Slider
by: Teoh, Hui Chiang
Published: (2018)