Nio Modification Using Zr4+ And Ca2+ For Dielectric Improvement
In this research, the effect of Zirconium ions (Zr4+) and Calcium ions (Ca2+) dopant on NiO was investigated. The electroceramic of Ni(l_;c)ZrxO, Ni(l_x)CaxO and Nio.9SZrO.o2CaO.OI was prepared by using solid state reaction method. Three main raw materials ofNiO, Zr02 and CaO were mixed for 24 ho...
| Main Author: | |
|---|---|
| Format: | Thesis |
| Language: | English |
| Published: |
2014
|
| Subjects: | |
| Online Access: | http://eprints.usm.my/61091/ http://eprints.usm.my/61091/1/24%20Pages%20from%2000001780807.pdf |
| _version_ | 1848884616689090560 |
|---|---|
| author | Syedsalim, Sharifah Aishah |
| author_facet | Syedsalim, Sharifah Aishah |
| author_sort | Syedsalim, Sharifah Aishah |
| building | USM Institutional Repository |
| collection | Online Access |
| description | In this research, the effect of Zirconium ions (Zr4+) and Calcium ions (Ca2+)
dopant on NiO was investigated. The electroceramic of Ni(l_;c)ZrxO, Ni(l_x)CaxO and
Nio.9SZrO.o2CaO.OI was prepared by using solid state reaction method. Three main raw
materials ofNiO, Zr02 and CaO were mixed for 24 hours, then were calcined at 1000°C.
Ni(l_x)Zr. |
| first_indexed | 2025-11-15T19:09:32Z |
| format | Thesis |
| id | usm-61091 |
| institution | Universiti Sains Malaysia |
| institution_category | Local University |
| language | English |
| last_indexed | 2025-11-15T19:09:32Z |
| publishDate | 2014 |
| recordtype | eprints |
| repository_type | Digital Repository |
| spelling | usm-610912024-09-11T02:20:14Z http://eprints.usm.my/61091/ Nio Modification Using Zr4+ And Ca2+ For Dielectric Improvement Syedsalim, Sharifah Aishah TN1-997 Mining engineering. Metallurgy In this research, the effect of Zirconium ions (Zr4+) and Calcium ions (Ca2+) dopant on NiO was investigated. The electroceramic of Ni(l_;c)ZrxO, Ni(l_x)CaxO and Nio.9SZrO.o2CaO.OI was prepared by using solid state reaction method. Three main raw materials ofNiO, Zr02 and CaO were mixed for 24 hours, then were calcined at 1000°C. Ni(l_x)Zr. 2014-01 Thesis NonPeerReviewed application/pdf en http://eprints.usm.my/61091/1/24%20Pages%20from%2000001780807.pdf Syedsalim, Sharifah Aishah (2014) Nio Modification Using Zr4+ And Ca2+ For Dielectric Improvement. Masters thesis, Perpustakaan Hamzah Sendut. |
| spellingShingle | TN1-997 Mining engineering. Metallurgy Syedsalim, Sharifah Aishah Nio Modification Using Zr4+ And Ca2+ For Dielectric Improvement |
| title | Nio Modification Using Zr4+ And Ca2+ For Dielectric Improvement |
| title_full | Nio Modification Using Zr4+ And Ca2+ For Dielectric Improvement |
| title_fullStr | Nio Modification Using Zr4+ And Ca2+ For Dielectric Improvement |
| title_full_unstemmed | Nio Modification Using Zr4+ And Ca2+ For Dielectric Improvement |
| title_short | Nio Modification Using Zr4+ And Ca2+ For Dielectric Improvement |
| title_sort | nio modification using zr4+ and ca2+ for dielectric improvement |
| topic | TN1-997 Mining engineering. Metallurgy |
| url | http://eprints.usm.my/61091/ http://eprints.usm.my/61091/1/24%20Pages%20from%2000001780807.pdf |