Preparation Of Activated Carbon From Mangrove Pile Leftover Via Physiochemical Activation
Activated production from mangrove pile leftover from solid waste from construction site is one of the most environment-friendly solutions by transforming waste to valuable product with high surface area. Thus, the main objective of this research was to prepare activated carbon from mangrove timber...
| Main Author: | |
|---|---|
| Format: | Monograph |
| Language: | English |
| Published: |
Universiti Sains Malaysia
2017
|
| Subjects: | |
| Online Access: | http://eprints.usm.my/53213/ http://eprints.usm.my/53213/1/Preparation%20Of%20Activated%20Carbon%20From%20Mangrove%20Pile%20Leftover%20Via%20Physiochemical%20Activation_Mohammad%20Fareez%20Adam%20Ramli_K4_2017.pdf |
| _version_ | 1848882465345634304 |
|---|---|
| author | Ramli, Mohammad Fareez Adam |
| author_facet | Ramli, Mohammad Fareez Adam |
| author_sort | Ramli, Mohammad Fareez Adam |
| building | USM Institutional Repository |
| collection | Online Access |
| description | Activated production from mangrove pile leftover from solid waste from construction site is one of the most environment-friendly solutions by transforming waste to valuable product with high surface area. Thus, the main objective of this research was to prepare activated carbon from mangrove timber using two-step physiochemical activation method. The carbonization process was carried out at 600oC for 1 hour under nitrogen flow rate of 150 ml/min. After the carbonization process, the char were impregnated with potassium hydroxide (KOH) at different impregnation ratios (0.5, 1, 1.5). After the char were impregnated, the char were then proceed to activation process with the different activation temperature (750oC, 800oC and 850oC) for 1 hour.. The effect of different preparation of precursor on the activated carbon yield and adsorption capacity on methylene blue were investigated. The optimal activated carbon was found at activation temperature of 750oC with impregnation ratio 0.5, namely as AC 750(0.5).The metyhlene blue adsorption capacity is 243.90 mg/g. The experimental data of adsorption is well fitted to Temkin isotherm with a R2 value of 0.9909. The result of adsorption study showed that the activated carbon prepared from mangrove timber is suitable for methylene removal from aqueous soluti |
| first_indexed | 2025-11-15T18:35:21Z |
| format | Monograph |
| id | usm-53213 |
| institution | Universiti Sains Malaysia |
| institution_category | Local University |
| language | English |
| last_indexed | 2025-11-15T18:35:21Z |
| publishDate | 2017 |
| publisher | Universiti Sains Malaysia |
| recordtype | eprints |
| repository_type | Digital Repository |
| spelling | usm-532132022-06-30T13:31:31Z http://eprints.usm.my/53213/ Preparation Of Activated Carbon From Mangrove Pile Leftover Via Physiochemical Activation Ramli, Mohammad Fareez Adam T Technology TP155-156 Chemical engineering Activated production from mangrove pile leftover from solid waste from construction site is one of the most environment-friendly solutions by transforming waste to valuable product with high surface area. Thus, the main objective of this research was to prepare activated carbon from mangrove timber using two-step physiochemical activation method. The carbonization process was carried out at 600oC for 1 hour under nitrogen flow rate of 150 ml/min. After the carbonization process, the char were impregnated with potassium hydroxide (KOH) at different impregnation ratios (0.5, 1, 1.5). After the char were impregnated, the char were then proceed to activation process with the different activation temperature (750oC, 800oC and 850oC) for 1 hour.. The effect of different preparation of precursor on the activated carbon yield and adsorption capacity on methylene blue were investigated. The optimal activated carbon was found at activation temperature of 750oC with impregnation ratio 0.5, namely as AC 750(0.5).The metyhlene blue adsorption capacity is 243.90 mg/g. The experimental data of adsorption is well fitted to Temkin isotherm with a R2 value of 0.9909. The result of adsorption study showed that the activated carbon prepared from mangrove timber is suitable for methylene removal from aqueous soluti Universiti Sains Malaysia 2017-05-01 Monograph NonPeerReviewed application/pdf en http://eprints.usm.my/53213/1/Preparation%20Of%20Activated%20Carbon%20From%20Mangrove%20Pile%20Leftover%20Via%20Physiochemical%20Activation_Mohammad%20Fareez%20Adam%20Ramli_K4_2017.pdf Ramli, Mohammad Fareez Adam (2017) Preparation Of Activated Carbon From Mangrove Pile Leftover Via Physiochemical Activation. Project Report. Universiti Sains Malaysia, Pusat Pengajian Kejuruteraan Kimia. (Submitted) |
| spellingShingle | T Technology TP155-156 Chemical engineering Ramli, Mohammad Fareez Adam Preparation Of Activated Carbon From Mangrove Pile Leftover Via Physiochemical Activation |
| title | Preparation Of Activated Carbon From Mangrove Pile Leftover Via Physiochemical Activation |
| title_full | Preparation Of Activated Carbon From Mangrove Pile Leftover Via Physiochemical Activation |
| title_fullStr | Preparation Of Activated Carbon From Mangrove Pile Leftover Via Physiochemical Activation |
| title_full_unstemmed | Preparation Of Activated Carbon From Mangrove Pile Leftover Via Physiochemical Activation |
| title_short | Preparation Of Activated Carbon From Mangrove Pile Leftover Via Physiochemical Activation |
| title_sort | preparation of activated carbon from mangrove pile leftover via physiochemical activation |
| topic | T Technology TP155-156 Chemical engineering |
| url | http://eprints.usm.my/53213/ http://eprints.usm.my/53213/1/Preparation%20Of%20Activated%20Carbon%20From%20Mangrove%20Pile%20Leftover%20Via%20Physiochemical%20Activation_Mohammad%20Fareez%20Adam%20Ramli_K4_2017.pdf |