Characterization physico-mechanical and chemical properties of nano-hydroxyapatite-silica added glass ionomer cement
The aim of this study was to synthesize and characterize different nanohydroxyapatite- silica (nano-HA-SiO2) particles with various silica concentrations and to investigate the effects of adding nano-HA-SiO2 to the conventional glass ionomer cement (Fuji IX GC). Nano-HA-SiO2 was synthesized using...
| Main Author: | |
|---|---|
| Format: | Thesis |
| Language: | English |
| Published: |
2020
|
| Subjects: | |
| Online Access: | http://eprints.usm.my/49400/ http://eprints.usm.my/49400/1/Imran%20Alam%20Moheet-24%20pages.pdf |
| _version_ | 1848881426246664192 |
|---|---|
| author | Moheet, Imran Alam |
| author_facet | Moheet, Imran Alam |
| author_sort | Moheet, Imran Alam |
| building | USM Institutional Repository |
| collection | Online Access |
| description | The aim of this study was to synthesize and characterize different nanohydroxyapatite-
silica (nano-HA-SiO2) particles with various silica concentrations and to
investigate the effects of adding nano-HA-SiO2 to the conventional glass ionomer cement
(Fuji IX GC). Nano-HA-SiO2 was synthesized using one-pot sol-gel technique, which was
then characterized using fourier transform infrared spectroscopy (FTIR), x-ray diffraction
(XRD), scanning electron microscope (SEM) and transmission electron microscope
(TEM). Further investigations were carried out on nano-HA-SiO2 added glass ionomer
cement (nano-HA-SiO2-GIC) to compare their mechanical (surface hardness, compressive
strength, flexural strength, and shear bond strength), chemical (fluoride ion release,
solubility and ion-exchange) and physical properties (colour stability, surface roughness,
sorption and micro-leakage) in relation to conventional glass ionomer cement (cGIC). It
was found that nano-powder consisted of a mixture of spherical silica particles (~50 nm)
and elongated hydroxyapatite particles in the range between 100-200 nm. Hardness,
compressive strength, and flexural strength of nano-HA-35SiO2-GIC was statistically
higher than that of nano-HA–21SiO2–GIC, nano-HA-11SiO2-GIC. The highest value for
Vickers hardness (64.77 6.18), compressive strength (143.42 13.94 MPa) and flexural
strength (17.68 1.81 MPa) were recorded by addition of 10% nano-HA-35SiO2 to GIC,
leading to an increase of ∼36 %, ∼19.7 % and ∼53.34 % in surface hardness, compressive
strength and flexural strength respectively as compared to conventional glass ionomer
cement (cGIC). 10% nano-HA–35SiO2-GIC also demonstrated higher shear bond strength
(∼17.54 % increase) as compared to cGIC. Nano-HA-35SiO2-GIC was more colour stable
material as it showed “slight - noticeable” change in colour as compared to cGIC that
displayed “noticeable to appreciable” change after 28 days of immersion in distilled water.
Nano-HA-35SiO2-GIC showed significantly lower surface roughness (0.13 ± 0.01 μm) as
compared to cGIC (0.16 ± 0.03 μm) on day 1. Additionally, nano-HA-35SiO2-GIC
showed highly significant difference (p=0.002) in amount of mean F+ release for all the
time intervals as compared to cGIC (p ≤ 0.05). In addition, Nano-HA-35SiO2-GIC
recorded higher values for both solubility and sorption (83.7 ± 19.04 μgmm-3 and 50.92 ±
12 μgmm-3) as compared to cGIC (56.65 ± 10.15 μgmm-3 and 42.64 ± 6.74 μgmm-3). It
also exhibited lower micro-leakage both at occlusal and gingival margins (0.2 ± 0.42 and
2.7 ± 0.67) as compared to cGIC (0.5 ± 0.71 and 3 ± 0.00). A greater ion-exchange was
displayed by nano-HA-35SiO2-GIC at ion-exchange layer (IEL) as well as the tooth
structure (enamel and dentin) as compared to cGIC. The addition of nano-HA-silica to
conventional GIC significantly enhanced the mechanical, physical and chemical
properties except sol-sorption properties of the material. Based on the findings of the
current study, nano-HA-SiO2-GIC can be suggested as a potential dental restorative
material. |
| first_indexed | 2025-11-15T18:18:50Z |
| format | Thesis |
| id | usm-49400 |
| institution | Universiti Sains Malaysia |
| institution_category | Local University |
| language | English |
| last_indexed | 2025-11-15T18:18:50Z |
| publishDate | 2020 |
| recordtype | eprints |
| repository_type | Digital Repository |
| spelling | usm-494002021-07-08T03:37:13Z http://eprints.usm.my/49400/ Characterization physico-mechanical and chemical properties of nano-hydroxyapatite-silica added glass ionomer cement Moheet, Imran Alam RK Dentistry The aim of this study was to synthesize and characterize different nanohydroxyapatite- silica (nano-HA-SiO2) particles with various silica concentrations and to investigate the effects of adding nano-HA-SiO2 to the conventional glass ionomer cement (Fuji IX GC). Nano-HA-SiO2 was synthesized using one-pot sol-gel technique, which was then characterized using fourier transform infrared spectroscopy (FTIR), x-ray diffraction (XRD), scanning electron microscope (SEM) and transmission electron microscope (TEM). Further investigations were carried out on nano-HA-SiO2 added glass ionomer cement (nano-HA-SiO2-GIC) to compare their mechanical (surface hardness, compressive strength, flexural strength, and shear bond strength), chemical (fluoride ion release, solubility and ion-exchange) and physical properties (colour stability, surface roughness, sorption and micro-leakage) in relation to conventional glass ionomer cement (cGIC). It was found that nano-powder consisted of a mixture of spherical silica particles (~50 nm) and elongated hydroxyapatite particles in the range between 100-200 nm. Hardness, compressive strength, and flexural strength of nano-HA-35SiO2-GIC was statistically higher than that of nano-HA–21SiO2–GIC, nano-HA-11SiO2-GIC. The highest value for Vickers hardness (64.77 6.18), compressive strength (143.42 13.94 MPa) and flexural strength (17.68 1.81 MPa) were recorded by addition of 10% nano-HA-35SiO2 to GIC, leading to an increase of ∼36 %, ∼19.7 % and ∼53.34 % in surface hardness, compressive strength and flexural strength respectively as compared to conventional glass ionomer cement (cGIC). 10% nano-HA–35SiO2-GIC also demonstrated higher shear bond strength (∼17.54 % increase) as compared to cGIC. Nano-HA-35SiO2-GIC was more colour stable material as it showed “slight - noticeable” change in colour as compared to cGIC that displayed “noticeable to appreciable” change after 28 days of immersion in distilled water. Nano-HA-35SiO2-GIC showed significantly lower surface roughness (0.13 ± 0.01 μm) as compared to cGIC (0.16 ± 0.03 μm) on day 1. Additionally, nano-HA-35SiO2-GIC showed highly significant difference (p=0.002) in amount of mean F+ release for all the time intervals as compared to cGIC (p ≤ 0.05). In addition, Nano-HA-35SiO2-GIC recorded higher values for both solubility and sorption (83.7 ± 19.04 μgmm-3 and 50.92 ± 12 μgmm-3) as compared to cGIC (56.65 ± 10.15 μgmm-3 and 42.64 ± 6.74 μgmm-3). It also exhibited lower micro-leakage both at occlusal and gingival margins (0.2 ± 0.42 and 2.7 ± 0.67) as compared to cGIC (0.5 ± 0.71 and 3 ± 0.00). A greater ion-exchange was displayed by nano-HA-35SiO2-GIC at ion-exchange layer (IEL) as well as the tooth structure (enamel and dentin) as compared to cGIC. The addition of nano-HA-silica to conventional GIC significantly enhanced the mechanical, physical and chemical properties except sol-sorption properties of the material. Based on the findings of the current study, nano-HA-SiO2-GIC can be suggested as a potential dental restorative material. 2020-01 Thesis NonPeerReviewed application/pdf en http://eprints.usm.my/49400/1/Imran%20Alam%20Moheet-24%20pages.pdf Moheet, Imran Alam (2020) Characterization physico-mechanical and chemical properties of nano-hydroxyapatite-silica added glass ionomer cement. Masters thesis, Universiti Sains Malaysia. |
| spellingShingle | RK Dentistry Moheet, Imran Alam Characterization physico-mechanical and chemical properties of nano-hydroxyapatite-silica added glass ionomer cement |
| title | Characterization physico-mechanical and chemical properties of nano-hydroxyapatite-silica added glass ionomer cement |
| title_full | Characterization physico-mechanical and chemical properties of nano-hydroxyapatite-silica added glass ionomer cement |
| title_fullStr | Characterization physico-mechanical and chemical properties of nano-hydroxyapatite-silica added glass ionomer cement |
| title_full_unstemmed | Characterization physico-mechanical and chemical properties of nano-hydroxyapatite-silica added glass ionomer cement |
| title_short | Characterization physico-mechanical and chemical properties of nano-hydroxyapatite-silica added glass ionomer cement |
| title_sort | characterization physico-mechanical and chemical properties of nano-hydroxyapatite-silica added glass ionomer cement |
| topic | RK Dentistry |
| url | http://eprints.usm.my/49400/ http://eprints.usm.my/49400/1/Imran%20Alam%20Moheet-24%20pages.pdf |