Fabrication Of TiC-Reinforced Iron Based Composite Through Mechanical Activation And Carbothermal Reduction On Hematite And Anatase
In this research, the influence of milling time and sintering temperature on TiCreinforced iron composite formation by carbothermal reduction of hematite (Fe2O3) and anatase (TiO2) mixture was investigated. Mixtures of Fe2O3, TiO2 and graphite powders with composition of Fe-30%TiC were mechanically...
| Main Author: | |
|---|---|
| Format: | Thesis |
| Language: | English |
| Published: |
2012
|
| Subjects: | |
| Online Access: | http://eprints.usm.my/44849/ http://eprints.usm.my/44849/1/MOHD%20SALIHIN%20BIN%20HASSIN.pdf |
| _version_ | 1848880170183688192 |
|---|---|
| author | Hassin, Mohd Salihin |
| author_facet | Hassin, Mohd Salihin |
| author_sort | Hassin, Mohd Salihin |
| building | USM Institutional Repository |
| collection | Online Access |
| description | In this research, the influence of milling time and sintering temperature on TiCreinforced iron composite formation by carbothermal reduction of hematite (Fe2O3)
and anatase (TiO2) mixture was investigated. Mixtures of Fe2O3, TiO2 and graphite powders with composition of Fe-30%TiC were mechanically activated in a high energy ball mill at various milling times (0 hour-60 hours). X-ray diffraction (XRD) analysis of as-milled powder showed broadening of Fe2O3 peaks with disappearance of TiO2 and graphite peaks due to powder refinement and diffusion of graphite. |
| first_indexed | 2025-11-15T17:58:52Z |
| format | Thesis |
| id | usm-44849 |
| institution | Universiti Sains Malaysia |
| institution_category | Local University |
| language | English |
| last_indexed | 2025-11-15T17:58:52Z |
| publishDate | 2012 |
| recordtype | eprints |
| repository_type | Digital Repository |
| spelling | usm-448492019-07-04T01:30:47Z http://eprints.usm.my/44849/ Fabrication Of TiC-Reinforced Iron Based Composite Through Mechanical Activation And Carbothermal Reduction On Hematite And Anatase Hassin, Mohd Salihin TN1-997 Mining engineering. Metallurgy In this research, the influence of milling time and sintering temperature on TiCreinforced iron composite formation by carbothermal reduction of hematite (Fe2O3) and anatase (TiO2) mixture was investigated. Mixtures of Fe2O3, TiO2 and graphite powders with composition of Fe-30%TiC were mechanically activated in a high energy ball mill at various milling times (0 hour-60 hours). X-ray diffraction (XRD) analysis of as-milled powder showed broadening of Fe2O3 peaks with disappearance of TiO2 and graphite peaks due to powder refinement and diffusion of graphite. 2012-06 Thesis NonPeerReviewed application/pdf en http://eprints.usm.my/44849/1/MOHD%20SALIHIN%20BIN%20HASSIN.pdf Hassin, Mohd Salihin (2012) Fabrication Of TiC-Reinforced Iron Based Composite Through Mechanical Activation And Carbothermal Reduction On Hematite And Anatase. Masters thesis, Universiti Sains Malaysia. |
| spellingShingle | TN1-997 Mining engineering. Metallurgy Hassin, Mohd Salihin Fabrication Of TiC-Reinforced Iron Based Composite Through Mechanical Activation And Carbothermal Reduction On Hematite And Anatase |
| title | Fabrication Of TiC-Reinforced Iron Based Composite Through Mechanical Activation And Carbothermal Reduction On Hematite And Anatase |
| title_full | Fabrication Of TiC-Reinforced Iron Based Composite Through Mechanical Activation And Carbothermal Reduction On Hematite And Anatase |
| title_fullStr | Fabrication Of TiC-Reinforced Iron Based Composite Through Mechanical Activation And Carbothermal Reduction On Hematite And Anatase |
| title_full_unstemmed | Fabrication Of TiC-Reinforced Iron Based Composite Through Mechanical Activation And Carbothermal Reduction On Hematite And Anatase |
| title_short | Fabrication Of TiC-Reinforced Iron Based Composite Through Mechanical Activation And Carbothermal Reduction On Hematite And Anatase |
| title_sort | fabrication of tic-reinforced iron based composite through mechanical activation and carbothermal reduction on hematite and anatase |
| topic | TN1-997 Mining engineering. Metallurgy |
| url | http://eprints.usm.my/44849/ http://eprints.usm.my/44849/1/MOHD%20SALIHIN%20BIN%20HASSIN.pdf |