The Uv-Shielding Property Of Zr0.7ce0.3o2-Kaolinite/Exfoliated Kaolinite Composites Prepared By Differentsynthesis Methods
Kaolinite was obtained by elutriation of tin slime, which was then exfoliated by planetary ball milling with 40 wt. % of urea for 1, 3 and 5 hours. Then the kaolinite and urea-treated kaolinite samples were characterized by using XRD, XRF, SEM, FTIR, and BET. The characterization results of kaoli...
| Main Author: | |
|---|---|
| Format: | Thesis |
| Language: | English |
| Published: |
2013
|
| Subjects: | |
| Online Access: | http://eprints.usm.my/43559/ http://eprints.usm.my/43559/1/Kry%20Nallis24.pdf |
| _version_ | 1848879842681946112 |
|---|---|
| author | Nallis, Kry |
| author_facet | Nallis, Kry |
| author_sort | Nallis, Kry |
| building | USM Institutional Repository |
| collection | Online Access |
| description | Kaolinite was obtained by elutriation of tin slime, which was then exfoliated by
planetary ball milling with 40 wt. % of urea for 1, 3 and 5 hours. Then the kaolinite
and urea-treated kaolinite samples were characterized by using XRD, XRF, SEM,
FTIR, and BET. The characterization results of kaolinite and urea-treated kaolinite
samples for 1, 3 and 5 hours proved that kaolinite was successfully exfoliated by urea
treatment for 5 hours and the XRD result of kaolinite showed minor gibbsite and
muscovite as impurities. Composites of Zr0.7Ce0.3O2-kaolinite/exfoliated kaolinite
were prepared by three different in-situ synthesis methods and one solid mixing
method. The first in-situ synthesis method was a citric acid complexing method, with
and without NH3 added; the second in-situ synthesis method was a soft solution
chemical method; and the third in-situ synthesis method was a hydrothermal
treatment method with and without sodium oleate added. For the solid mixing
method, Zr0.7Ce0.3O2, which was prepared by the three different synthesis methods
such as a citric acid complexing method without NH3 added, a soft solution chemical
method and a hydrothermal treatment without sodium oleate added, was solid mixed
with kaolinite/exfoliated kaolinite using an agate mortar and pestle. The resulting
composites were characterized by using XRD, FESEM and UV-Vis. |
| first_indexed | 2025-11-15T17:53:40Z |
| format | Thesis |
| id | usm-43559 |
| institution | Universiti Sains Malaysia |
| institution_category | Local University |
| language | English |
| last_indexed | 2025-11-15T17:53:40Z |
| publishDate | 2013 |
| recordtype | eprints |
| repository_type | Digital Repository |
| spelling | usm-435592019-04-12T05:26:16Z http://eprints.usm.my/43559/ The Uv-Shielding Property Of Zr0.7ce0.3o2-Kaolinite/Exfoliated Kaolinite Composites Prepared By Differentsynthesis Methods Nallis, Kry TN1-997 Mining engineering. Metallurgy Kaolinite was obtained by elutriation of tin slime, which was then exfoliated by planetary ball milling with 40 wt. % of urea for 1, 3 and 5 hours. Then the kaolinite and urea-treated kaolinite samples were characterized by using XRD, XRF, SEM, FTIR, and BET. The characterization results of kaolinite and urea-treated kaolinite samples for 1, 3 and 5 hours proved that kaolinite was successfully exfoliated by urea treatment for 5 hours and the XRD result of kaolinite showed minor gibbsite and muscovite as impurities. Composites of Zr0.7Ce0.3O2-kaolinite/exfoliated kaolinite were prepared by three different in-situ synthesis methods and one solid mixing method. The first in-situ synthesis method was a citric acid complexing method, with and without NH3 added; the second in-situ synthesis method was a soft solution chemical method; and the third in-situ synthesis method was a hydrothermal treatment method with and without sodium oleate added. For the solid mixing method, Zr0.7Ce0.3O2, which was prepared by the three different synthesis methods such as a citric acid complexing method without NH3 added, a soft solution chemical method and a hydrothermal treatment without sodium oleate added, was solid mixed with kaolinite/exfoliated kaolinite using an agate mortar and pestle. The resulting composites were characterized by using XRD, FESEM and UV-Vis. 2013-05 Thesis NonPeerReviewed application/pdf en http://eprints.usm.my/43559/1/Kry%20Nallis24.pdf Nallis, Kry (2013) The Uv-Shielding Property Of Zr0.7ce0.3o2-Kaolinite/Exfoliated Kaolinite Composites Prepared By Differentsynthesis Methods. PhD thesis, Universiti Sains Malaysia. |
| spellingShingle | TN1-997 Mining engineering. Metallurgy Nallis, Kry The Uv-Shielding Property Of Zr0.7ce0.3o2-Kaolinite/Exfoliated Kaolinite Composites Prepared By Differentsynthesis Methods |
| title | The Uv-Shielding Property Of
Zr0.7ce0.3o2-Kaolinite/Exfoliated Kaolinite
Composites Prepared By Differentsynthesis
Methods |
| title_full | The Uv-Shielding Property Of
Zr0.7ce0.3o2-Kaolinite/Exfoliated Kaolinite
Composites Prepared By Differentsynthesis
Methods |
| title_fullStr | The Uv-Shielding Property Of
Zr0.7ce0.3o2-Kaolinite/Exfoliated Kaolinite
Composites Prepared By Differentsynthesis
Methods |
| title_full_unstemmed | The Uv-Shielding Property Of
Zr0.7ce0.3o2-Kaolinite/Exfoliated Kaolinite
Composites Prepared By Differentsynthesis
Methods |
| title_short | The Uv-Shielding Property Of
Zr0.7ce0.3o2-Kaolinite/Exfoliated Kaolinite
Composites Prepared By Differentsynthesis
Methods |
| title_sort | uv-shielding property of
zr0.7ce0.3o2-kaolinite/exfoliated kaolinite
composites prepared by differentsynthesis
methods |
| topic | TN1-997 Mining engineering. Metallurgy |
| url | http://eprints.usm.my/43559/ http://eprints.usm.my/43559/1/Kry%20Nallis24.pdf |