Magnetoresistance of CuCoNi, CuCo and AlFeNi Granular Thin Films Prepared by RF Magnetron Sputtering
In this project, a series of Cu-based and AI-based granular thin films have been prepared using the RF magnetron sputtering system. The effect of the temperature, magnetic field and annealing temperature on the magnetoresisatnce (MR.) of the samples prepared has been discussed. It has been demons...
| Main Author: | |
|---|---|
| Format: | Thesis |
| Language: | English English |
| Published: |
2002
|
| Subjects: | |
| Online Access: | http://psasir.upm.edu.my/id/eprint/9469/ http://psasir.upm.edu.my/id/eprint/9469/1/FSAS_2002_26.pdf |
| _version_ | 1848841154217377792 |
|---|---|
| author | Yu, Ong Sing |
| author_facet | Yu, Ong Sing |
| author_sort | Yu, Ong Sing |
| building | UPM Institutional Repository |
| collection | Online Access |
| description | In this project, a series of Cu-based and AI-based granular thin films have
been prepared using the RF magnetron sputtering system. The effect of the
temperature, magnetic field and annealing temperature on the magnetoresisatnce
(MR.) of the samples prepared has been discussed. It has been demonstrated that the
MR is composition, thickness and temperature dependent.
For Cu-based sample which has been prepared under ambient
temperature, the highest MR of 1.35% is 'observed for sample CU80.46CO19.54 (CC6).
The samples with different compositions of magnetic entities show the different
optimum thickness that would give the highest MR. The samples CU72.41CO19.62Ni7.97
and CU75.63CO19.56N4.51 have the maximum MR when the deposition time is 80
minutes whereas for sample CU8O.46CO19.54, the maximum occurs when the deposition
is 60 minutes.Upon annealing, the MR of samples also changes. In this study, all of the
Cu-based samples prepared at ambient temperature have been annealed at the
temperature of 300°C, 350°C, 400°C, 450°C for 10 minutes in the argon
environment. Among the samples, CU80.46CO19.54 shows the highest MR of 1.8%
when it is annealed at 450°C. |
| first_indexed | 2025-11-15T07:38:43Z |
| format | Thesis |
| id | upm-9469 |
| institution | Universiti Putra Malaysia |
| institution_category | Local University |
| language | English English |
| last_indexed | 2025-11-15T07:38:43Z |
| publishDate | 2002 |
| recordtype | eprints |
| repository_type | Digital Repository |
| spelling | upm-94692024-03-06T02:18:43Z http://psasir.upm.edu.my/id/eprint/9469/ Magnetoresistance of CuCoNi, CuCo and AlFeNi Granular Thin Films Prepared by RF Magnetron Sputtering Yu, Ong Sing In this project, a series of Cu-based and AI-based granular thin films have been prepared using the RF magnetron sputtering system. The effect of the temperature, magnetic field and annealing temperature on the magnetoresisatnce (MR.) of the samples prepared has been discussed. It has been demonstrated that the MR is composition, thickness and temperature dependent. For Cu-based sample which has been prepared under ambient temperature, the highest MR of 1.35% is 'observed for sample CU80.46CO19.54 (CC6). The samples with different compositions of magnetic entities show the different optimum thickness that would give the highest MR. The samples CU72.41CO19.62Ni7.97 and CU75.63CO19.56N4.51 have the maximum MR when the deposition time is 80 minutes whereas for sample CU8O.46CO19.54, the maximum occurs when the deposition is 60 minutes.Upon annealing, the MR of samples also changes. In this study, all of the Cu-based samples prepared at ambient temperature have been annealed at the temperature of 300°C, 350°C, 400°C, 450°C for 10 minutes in the argon environment. Among the samples, CU80.46CO19.54 shows the highest MR of 1.8% when it is annealed at 450°C. 2002-06 Thesis NonPeerReviewed text en http://psasir.upm.edu.my/id/eprint/9469/1/FSAS_2002_26.pdf Yu, Ong Sing (2002) Magnetoresistance of CuCoNi, CuCo and AlFeNi Granular Thin Films Prepared by RF Magnetron Sputtering. Masters thesis, Universiti Putra Malaysia. Magnetoresistance Thin films - Magnetic properties Thin films - Effect of temperature on English |
| spellingShingle | Magnetoresistance Thin films - Magnetic properties Thin films - Effect of temperature on Yu, Ong Sing Magnetoresistance of CuCoNi, CuCo and AlFeNi Granular Thin Films Prepared by RF Magnetron Sputtering |
| title | Magnetoresistance of CuCoNi, CuCo and AlFeNi Granular Thin Films Prepared by RF Magnetron Sputtering |
| title_full | Magnetoresistance of CuCoNi, CuCo and AlFeNi Granular Thin Films Prepared by RF Magnetron Sputtering |
| title_fullStr | Magnetoresistance of CuCoNi, CuCo and AlFeNi Granular Thin Films Prepared by RF Magnetron Sputtering |
| title_full_unstemmed | Magnetoresistance of CuCoNi, CuCo and AlFeNi Granular Thin Films Prepared by RF Magnetron Sputtering |
| title_short | Magnetoresistance of CuCoNi, CuCo and AlFeNi Granular Thin Films Prepared by RF Magnetron Sputtering |
| title_sort | magnetoresistance of cuconi, cuco and alfeni granular thin films prepared by rf magnetron sputtering |
| topic | Magnetoresistance Thin films - Magnetic properties Thin films - Effect of temperature on |
| url | http://psasir.upm.edu.my/id/eprint/9469/ http://psasir.upm.edu.my/id/eprint/9469/1/FSAS_2002_26.pdf |