Effect of stanum doping and heat treatment on Bi-Sr-Ca-Cu-O superconducting ceramics
The influence of Sn doping in calcium (Ca) and copper (Cu) sItes either temperature for 30 hours soaking time were studied For Sn-free sample. heat treatment improved the superconducting transition temperature, TC(RI)) from 100 K to 104 K, when the sintered sample was annealed at 820°C The highes...
| Main Author: | |
|---|---|
| Format: | Thesis |
| Language: | English English |
| Published: |
1999
|
| Subjects: | |
| Online Access: | http://psasir.upm.edu.my/id/eprint/8657/ http://psasir.upm.edu.my/id/eprint/8657/1/FSAS_1999_12_IR.pdf |
| _version_ | 1848840931086696448 |
|---|---|
| author | Hashim @ Ismail, Azhan |
| author_facet | Hashim @ Ismail, Azhan |
| author_sort | Hashim @ Ismail, Azhan |
| building | UPM Institutional Repository |
| collection | Online Access |
| description | The influence of Sn doping in calcium (Ca) and copper (Cu) sItes either
temperature for 30 hours soaking time were studied For Sn-free sample. heat
treatment improved the superconducting transition temperature, TC(RI)) from 100
K to 104 K, when the sintered sample was annealed at 820°C The highest Tc(R=0)
of 104 K was observed for sintered sample (x=0 02) with simultaneous doping
The heat treatment improved the Tc(R=0) from 60 K to 94 K or sample doped 111
Ca site when re-sintered at 855°C and from 66 K to 100 K for sample doped with
Sn in Cu site when annealed at 840°C For simultaneous doping, the T C(R 0) dId
not change significantly after heat treatment except for sample with x=0 05 that
showed drastic improvement of T C(R=U) from 64 K (sintered) to above 100 K
From XRD analysis, the volume of 2223 phase decreased as the Sn
concentration increased A ll samples with Sn concentration above x=0 10
contall1ed unknown peaks which con respond to the non-superconducting phase
although the lattice parameter of the samples shortened, the crystallographic
structure remained in the tetragonal form. |
| first_indexed | 2025-11-15T07:35:11Z |
| format | Thesis |
| id | upm-8657 |
| institution | Universiti Putra Malaysia |
| institution_category | Local University |
| language | English English |
| last_indexed | 2025-11-15T07:35:11Z |
| publishDate | 1999 |
| recordtype | eprints |
| repository_type | Digital Repository |
| spelling | upm-86572023-12-14T00:24:15Z http://psasir.upm.edu.my/id/eprint/8657/ Effect of stanum doping and heat treatment on Bi-Sr-Ca-Cu-O superconducting ceramics Hashim @ Ismail, Azhan The influence of Sn doping in calcium (Ca) and copper (Cu) sItes either temperature for 30 hours soaking time were studied For Sn-free sample. heat treatment improved the superconducting transition temperature, TC(RI)) from 100 K to 104 K, when the sintered sample was annealed at 820°C The highest Tc(R=0) of 104 K was observed for sintered sample (x=0 02) with simultaneous doping The heat treatment improved the Tc(R=0) from 60 K to 94 K or sample doped 111 Ca site when re-sintered at 855°C and from 66 K to 100 K for sample doped with Sn in Cu site when annealed at 840°C For simultaneous doping, the T C(R 0) dId not change significantly after heat treatment except for sample with x=0 05 that showed drastic improvement of T C(R=U) from 64 K (sintered) to above 100 K From XRD analysis, the volume of 2223 phase decreased as the Sn concentration increased A ll samples with Sn concentration above x=0 10 contall1ed unknown peaks which con respond to the non-superconducting phase although the lattice parameter of the samples shortened, the crystallographic structure remained in the tetragonal form. 1999-12 Thesis NonPeerReviewed text en http://psasir.upm.edu.my/id/eprint/8657/1/FSAS_1999_12_IR.pdf Hashim @ Ismail, Azhan (1999) Effect of stanum doping and heat treatment on Bi-Sr-Ca-Cu-O superconducting ceramics. Doctoral thesis, Universiti Putra Malaysia. Ceramic superconductor English |
| spellingShingle | Ceramic superconductor Hashim @ Ismail, Azhan Effect of stanum doping and heat treatment on Bi-Sr-Ca-Cu-O superconducting ceramics |
| title | Effect of stanum doping and heat treatment on Bi-Sr-Ca-Cu-O superconducting ceramics |
| title_full | Effect of stanum doping and heat treatment on Bi-Sr-Ca-Cu-O superconducting ceramics |
| title_fullStr | Effect of stanum doping and heat treatment on Bi-Sr-Ca-Cu-O superconducting ceramics |
| title_full_unstemmed | Effect of stanum doping and heat treatment on Bi-Sr-Ca-Cu-O superconducting ceramics |
| title_short | Effect of stanum doping and heat treatment on Bi-Sr-Ca-Cu-O superconducting ceramics |
| title_sort | effect of stanum doping and heat treatment on bi-sr-ca-cu-o superconducting ceramics |
| topic | Ceramic superconductor |
| url | http://psasir.upm.edu.my/id/eprint/8657/ http://psasir.upm.edu.my/id/eprint/8657/1/FSAS_1999_12_IR.pdf |