Influence of wood flour and modifier contents on the physical and mechanical properties of wood flour-recycle polypropylene composites
The objectives of this research was to evaluate the physical and mechanical properties of composites of Wood Flour (WF) and Recycle Polypropylene (RPP) prepared under various WF contents, WF sizes and modifier contents. WF from mixed-soft wood species and Eucalyptus deglupta Blume species were used...
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English English |
| Published: |
Asian Network for Scientific Information
2006
|
| Online Access: | http://psasir.upm.edu.my/id/eprint/7419/ http://psasir.upm.edu.my/id/eprint/7419/1/Influence%20of%20wood%20flour%20and%20modifier%20contents%20on%20the%20physical%20and%20mechanical%20properties%20of%20wood%20flour.pdf |
| _version_ | 1848840589800374272 |
|---|---|
| author | Febrianto, Fauzi Setyawati, Dina Karina, Myrtha Bakar, Edi Suhaimi Hadi, Yusuf Sudo |
| author_facet | Febrianto, Fauzi Setyawati, Dina Karina, Myrtha Bakar, Edi Suhaimi Hadi, Yusuf Sudo |
| author_sort | Febrianto, Fauzi |
| building | UPM Institutional Repository |
| collection | Online Access |
| description | The objectives of this research was to evaluate the physical and mechanical properties of composites of Wood Flour (WF) and Recycle Polypropylene (RPP) prepared under various WF contents, WF sizes and modifier contents. WF from mixed-soft wood species and Eucalyptus deglupta Blume species were used as filler. The composites composed of 0-70% WF, 0-70% Polypropylene (PP) or RPP, various sizes of WF (60-80; 80-100 and < 120 mesh), various contents of MAH modifier (0, 1, 2.5, 5, 7.5 and 10%) and 15% Dicumyl Peroxide (DCP) initiator (based on MAH weight). Kneading conditions were set at 170 °C, 10-50 rpm for 15 min. The physical and mechanical properties of composites were greatly affected by WF content, WF size and modifier content. The greater the WF loading resulted in the greater was the reduction of tensile strength and breaking elongation values and at the same time the greater was the increasing of Young`s modulus value. The smaller the WF size resulted in the greater the tensile strength of composites. Addition of MAH modifier improved the physical and mechanical properties of composites. WF-RPP composites with 120 mesh WF size and 2.5% MA modifier had tensile strength, breaking elongation and Young`s modulus about 2.15, 2.27 and 1.18 times, respectively higher compared with composites free-MAH modifier and absorbed considerably less water. Scanning Electron Microscope (SEM) indicated that addition of MAH improved the adhesion between WF and RPP. |
| first_indexed | 2025-11-15T07:29:45Z |
| format | Article |
| id | upm-7419 |
| institution | Universiti Putra Malaysia |
| institution_category | Local University |
| language | English English |
| last_indexed | 2025-11-15T07:29:45Z |
| publishDate | 2006 |
| publisher | Asian Network for Scientific Information |
| recordtype | eprints |
| repository_type | Digital Repository |
| spelling | upm-74192015-10-06T07:27:13Z http://psasir.upm.edu.my/id/eprint/7419/ Influence of wood flour and modifier contents on the physical and mechanical properties of wood flour-recycle polypropylene composites Febrianto, Fauzi Setyawati, Dina Karina, Myrtha Bakar, Edi Suhaimi Hadi, Yusuf Sudo The objectives of this research was to evaluate the physical and mechanical properties of composites of Wood Flour (WF) and Recycle Polypropylene (RPP) prepared under various WF contents, WF sizes and modifier contents. WF from mixed-soft wood species and Eucalyptus deglupta Blume species were used as filler. The composites composed of 0-70% WF, 0-70% Polypropylene (PP) or RPP, various sizes of WF (60-80; 80-100 and < 120 mesh), various contents of MAH modifier (0, 1, 2.5, 5, 7.5 and 10%) and 15% Dicumyl Peroxide (DCP) initiator (based on MAH weight). Kneading conditions were set at 170 °C, 10-50 rpm for 15 min. The physical and mechanical properties of composites were greatly affected by WF content, WF size and modifier content. The greater the WF loading resulted in the greater was the reduction of tensile strength and breaking elongation values and at the same time the greater was the increasing of Young`s modulus value. The smaller the WF size resulted in the greater the tensile strength of composites. Addition of MAH modifier improved the physical and mechanical properties of composites. WF-RPP composites with 120 mesh WF size and 2.5% MA modifier had tensile strength, breaking elongation and Young`s modulus about 2.15, 2.27 and 1.18 times, respectively higher compared with composites free-MAH modifier and absorbed considerably less water. Scanning Electron Microscope (SEM) indicated that addition of MAH improved the adhesion between WF and RPP. Asian Network for Scientific Information 2006 Article PeerReviewed application/pdf en http://psasir.upm.edu.my/id/eprint/7419/1/Influence%20of%20wood%20flour%20and%20modifier%20contents%20on%20the%20physical%20and%20mechanical%20properties%20of%20wood%20flour.pdf Febrianto, Fauzi and Setyawati, Dina and Karina, Myrtha and Bakar, Edi Suhaimi and Hadi, Yusuf Sudo (2006) Influence of wood flour and modifier contents on the physical and mechanical properties of wood flour-recycle polypropylene composites. Journal of Biological Sciences, 6 (2). pp. 337-343. ISSN 1727-3048 http://dx.doi.org/10.3923/jbs.2006.337.343 10.3923/jbs.2006.337.343 English |
| spellingShingle | Febrianto, Fauzi Setyawati, Dina Karina, Myrtha Bakar, Edi Suhaimi Hadi, Yusuf Sudo Influence of wood flour and modifier contents on the physical and mechanical properties of wood flour-recycle polypropylene composites |
| title | Influence of wood flour and modifier contents on the physical and mechanical properties of wood flour-recycle polypropylene composites |
| title_full | Influence of wood flour and modifier contents on the physical and mechanical properties of wood flour-recycle polypropylene composites |
| title_fullStr | Influence of wood flour and modifier contents on the physical and mechanical properties of wood flour-recycle polypropylene composites |
| title_full_unstemmed | Influence of wood flour and modifier contents on the physical and mechanical properties of wood flour-recycle polypropylene composites |
| title_short | Influence of wood flour and modifier contents on the physical and mechanical properties of wood flour-recycle polypropylene composites |
| title_sort | influence of wood flour and modifier contents on the physical and mechanical properties of wood flour-recycle polypropylene composites |
| url | http://psasir.upm.edu.my/id/eprint/7419/ http://psasir.upm.edu.my/id/eprint/7419/ http://psasir.upm.edu.my/id/eprint/7419/ http://psasir.upm.edu.my/id/eprint/7419/1/Influence%20of%20wood%20flour%20and%20modifier%20contents%20on%20the%20physical%20and%20mechanical%20properties%20of%20wood%20flour.pdf |