The influence of samarium doping in Bi1.6 (Pb0.4)Sr2- xSmxCa2Cu3Oy prepared by coprecipitation method
The influence of Sm doping on the phase formation, normal state properties and microstructure development of Bi-2223 superconductors was systematically investigated. Samarium was incorporated in the strontium site with x ranging from 0.00 to 0.30 prepared via coprecipitation technique. The four poin...
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Malaysian Solid State Science and Technology Society
2003
|
| Online Access: | http://psasir.upm.edu.my/id/eprint/42206/ http://psasir.upm.edu.my/id/eprint/42206/1/The%20influence%20of%20samarium%20doping%20in%20Bi1.6%20%28Pb0.4%29Sr2-%20xSmxCa2Cu3Oy%20prepared%20by%20coprecipitation%20method.pdf |
| Summary: | The influence of Sm doping on the phase formation, normal state properties and microstructure development of Bi-2223 superconductors was systematically investigated. Samarium was incorporated in the strontium site with x ranging from 0.00 to 0.30 prepared via coprecipitation technique. The four point probe measurements showed the loss in metallic behaviour for the samples with Sm doped above x=0.2. XRD results showed the decrease of the volume percentage of the 2223 phase followed by increasing in the density of the lattice. The SEM micrographs showed the decrease in the grain size for all samples containing samarium. The temperature dependence of ac susceptibility data shows the shifting towards lower temperature as the Sm concentration increases presence of low Tconset phase. The imaginary component, χ”, shows a decrease in the intergranular coupling peak, Tp, towards lower temperature as the Sm concentration increases. Samarium did not enhance the Tc(R=0) but gradually decreases its value from 102. K to 52 K for x=0.00 to x=0.20 respectively. |
|---|