Corrosion at Sulphide Inclusions in Stainless Steel
Auger analysis was performed using a high resolution scanning auger electron microscope and auger electron spectroscopy. Elemental auger contour maps for corroded sulphide inclusions in stainless steel were presented. It was found that the copper enriched-manganese sulphide inclusions were uniformly...
| Main Author: | |
|---|---|
| Format: | Article |
| Language: | English English |
| Published: |
Universiti Putra Malaysia Press
1996
|
| Online Access: | http://psasir.upm.edu.my/id/eprint/3210/ http://psasir.upm.edu.my/id/eprint/3210/1/Corrosion_at_Sulphide_Inclusions_in_Stainless_Steel.pdf |
| _version_ | 1848839466412670976 |
|---|---|
| author | Daud, A. R. |
| author_facet | Daud, A. R. |
| author_sort | Daud, A. R. |
| building | UPM Institutional Repository |
| collection | Online Access |
| description | Auger analysis was performed using a high resolution scanning auger electron microscope and auger electron spectroscopy. Elemental auger contour maps for corroded sulphide inclusions in stainless steel were presented. It was found that the copper enriched-manganese sulphide inclusions were uniformly corroded, which might be due to CU2S deposition on the surface of corroding inclusions. In contrast, manganese sulphide inclusions containing less copper were non-uniformly attacked, resulting in the formation of deep microcrevices at their edges. |
| first_indexed | 2025-11-15T07:11:54Z |
| format | Article |
| id | upm-3210 |
| institution | Universiti Putra Malaysia |
| institution_category | Local University |
| language | English English |
| last_indexed | 2025-11-15T07:11:54Z |
| publishDate | 1996 |
| publisher | Universiti Putra Malaysia Press |
| recordtype | eprints |
| repository_type | Digital Repository |
| spelling | upm-32102013-05-27T07:06:28Z http://psasir.upm.edu.my/id/eprint/3210/ Corrosion at Sulphide Inclusions in Stainless Steel Daud, A. R. Auger analysis was performed using a high resolution scanning auger electron microscope and auger electron spectroscopy. Elemental auger contour maps for corroded sulphide inclusions in stainless steel were presented. It was found that the copper enriched-manganese sulphide inclusions were uniformly corroded, which might be due to CU2S deposition on the surface of corroding inclusions. In contrast, manganese sulphide inclusions containing less copper were non-uniformly attacked, resulting in the formation of deep microcrevices at their edges. Universiti Putra Malaysia Press 1996 Article PeerReviewed application/pdf en http://psasir.upm.edu.my/id/eprint/3210/1/Corrosion_at_Sulphide_Inclusions_in_Stainless_Steel.pdf Daud, A. R. (1996) Corrosion at Sulphide Inclusions in Stainless Steel. Pertanika Journal of Science & Technology, 4 (2). pp. 201-207. ISSN 0128-7680 English |
| spellingShingle | Daud, A. R. Corrosion at Sulphide Inclusions in Stainless Steel |
| title | Corrosion at Sulphide Inclusions in Stainless Steel |
| title_full | Corrosion at Sulphide Inclusions in Stainless Steel |
| title_fullStr | Corrosion at Sulphide Inclusions in Stainless Steel |
| title_full_unstemmed | Corrosion at Sulphide Inclusions in Stainless Steel |
| title_short | Corrosion at Sulphide Inclusions in Stainless Steel |
| title_sort | corrosion at sulphide inclusions in stainless steel |
| url | http://psasir.upm.edu.my/id/eprint/3210/ http://psasir.upm.edu.my/id/eprint/3210/1/Corrosion_at_Sulphide_Inclusions_in_Stainless_Steel.pdf |