Sem, Edax and UV-visible studies on the properties of Cu2S thin films.
Cu2S thin films were produced by simple chemical bath deposition technique at various bath temperatures ranging from 55 °C to 75 °C. For chemical bath deposited thin films, copper sulphate solution was employed as Cu2+ source while thiourea solution provided the S2- ions. The morphological, composit...
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English English |
| Published: |
2011
|
| Online Access: | http://psasir.upm.edu.my/id/eprint/24965/ http://psasir.upm.edu.my/id/eprint/24965/1/Sem.pdf |
| Summary: | Cu2S thin films were produced by simple chemical bath deposition technique at various bath temperatures ranging from 55 °C to 75 °C. For chemical bath deposited thin films, copper sulphate solution was employed as Cu2+ source while thiourea solution provided the S2- ions. The morphological, compositional and optical properties were investigated using scanning electron microscopy, energy dispersive analysis of X-ray and UV-Visible spectrophotometer, respectively. The grain size and average atomic ratio of Cu/S increased when the bath temperature was increased from 55 °C to 75 °C. The films deposited at 75 °C indicated high absorbance as compared with other bath temperatures. |
|---|