Design and fabrication of an improved crack growth testing apparatus with stress corrosion cracking (SCC) study
A study of Stress Corrosion Cracking od SCC is a main part of this project. Ammonia tank is related with the SCC problem especially at -33°C. Stress Corrosion Cracking occurs relatively slow but due to certain solution will increase the SCC effect.
| Main Author: | |
|---|---|
| Format: | Final Year Project Report / IMRAD |
| Language: | English |
| Published: |
Universiti Malaysia Sarawak, UNIMAS
2006
|
| Subjects: | |
| Online Access: | http://ir.unimas.my/id/eprint/2798/ http://ir.unimas.my/id/eprint/2798/3/Ibrahim%20full.pdf |
| _version_ | 1848835073685585920 |
|---|---|
| author | Ibrahim Manai, Abdul Hakim |
| author_facet | Ibrahim Manai, Abdul Hakim |
| author_sort | Ibrahim Manai, Abdul Hakim |
| building | UNIMAS Institutional Repository |
| collection | Online Access |
| description | A study of Stress Corrosion Cracking od SCC is a main part of this project. Ammonia tank is related with the SCC problem especially at -33°C. Stress Corrosion Cracking occurs relatively slow but due to certain solution will increase the SCC effect. |
| first_indexed | 2025-11-15T06:02:04Z |
| format | Final Year Project Report / IMRAD |
| id | unimas-2798 |
| institution | Universiti Malaysia Sarawak |
| institution_category | Local University |
| language | English |
| last_indexed | 2025-11-15T06:02:04Z |
| publishDate | 2006 |
| publisher | Universiti Malaysia Sarawak, UNIMAS |
| recordtype | eprints |
| repository_type | Digital Repository |
| spelling | unimas-27982023-06-19T08:36:20Z http://ir.unimas.my/id/eprint/2798/ Design and fabrication of an improved crack growth testing apparatus with stress corrosion cracking (SCC) study Ibrahim Manai, Abdul Hakim TJ Mechanical engineering and machinery A study of Stress Corrosion Cracking od SCC is a main part of this project. Ammonia tank is related with the SCC problem especially at -33°C. Stress Corrosion Cracking occurs relatively slow but due to certain solution will increase the SCC effect. Universiti Malaysia Sarawak, UNIMAS 2006 Final Year Project Report / IMRAD NonPeerReviewed text en http://ir.unimas.my/id/eprint/2798/3/Ibrahim%20full.pdf Ibrahim Manai, Abdul Hakim (2006) Design and fabrication of an improved crack growth testing apparatus with stress corrosion cracking (SCC) study. [Final Year Project Report / IMRAD] (Unpublished) |
| spellingShingle | TJ Mechanical engineering and machinery Ibrahim Manai, Abdul Hakim Design and fabrication of an improved crack growth testing apparatus with stress corrosion cracking (SCC) study |
| title | Design and fabrication of an improved crack growth testing apparatus with stress corrosion cracking (SCC) study |
| title_full | Design and fabrication of an improved crack growth testing apparatus with stress corrosion cracking (SCC) study |
| title_fullStr | Design and fabrication of an improved crack growth testing apparatus with stress corrosion cracking (SCC) study |
| title_full_unstemmed | Design and fabrication of an improved crack growth testing apparatus with stress corrosion cracking (SCC) study |
| title_short | Design and fabrication of an improved crack growth testing apparatus with stress corrosion cracking (SCC) study |
| title_sort | design and fabrication of an improved crack growth testing apparatus with stress corrosion cracking (scc) study |
| topic | TJ Mechanical engineering and machinery |
| url | http://ir.unimas.my/id/eprint/2798/ http://ir.unimas.my/id/eprint/2798/3/Ibrahim%20full.pdf |