Construction of a crack growth testing apparatus associated with stress corrosion cracking (SCC) study
A case study of Stress Corrosion Cracking or SCC is a part of this project title. Stress corrosion cracking (SCC) can be divided into three important keywords to differentiate the mechanism which is tending to cause the fracture mechanism over the metallic material. SCC is caused by three conditions...
| Main Author: | |
|---|---|
| Format: | Final Year Project Report / IMRAD |
| Language: | English English |
| Published: |
University Malaysia Sarawak, UNIMAS.
2005
|
| Subjects: | |
| Online Access: | http://ir.unimas.my/id/eprint/2790/ http://ir.unimas.my/id/eprint/2790/1/Construction%20of%20a%20crack%20growth%20testing%20apparatus%20associated%20with%20stress%20corrosion%20cracking%20%28SCC%29%20study.pdf http://ir.unimas.my/id/eprint/2790/8/Peter%20Anderson.pdf |
| _version_ | 1848835071248695296 |
|---|---|
| author | Peter Anderson, anak Joseph |
| author_facet | Peter Anderson, anak Joseph |
| author_sort | Peter Anderson, anak Joseph |
| building | UNIMAS Institutional Repository |
| collection | Online Access |
| description | A case study of Stress Corrosion Cracking or SCC is a part of this project title. Stress corrosion cracking (SCC) can be divided into three important keywords to differentiate the mechanism which is tending to cause the fracture mechanism over the metallic material. SCC is caused by three conditions such as types of environment, types of materials and types of stress. Continuous research was encouraged to solve this problem from time to time in order to recognize main problem in obtaining the best solution. |
| first_indexed | 2025-11-15T06:02:02Z |
| format | Final Year Project Report / IMRAD |
| id | unimas-2790 |
| institution | Universiti Malaysia Sarawak |
| institution_category | Local University |
| language | English English |
| last_indexed | 2025-11-15T06:02:02Z |
| publishDate | 2005 |
| publisher | University Malaysia Sarawak, UNIMAS. |
| recordtype | eprints |
| repository_type | Digital Repository |
| spelling | unimas-27902024-02-28T09:01:56Z http://ir.unimas.my/id/eprint/2790/ Construction of a crack growth testing apparatus associated with stress corrosion cracking (SCC) study Peter Anderson, anak Joseph TJ Mechanical engineering and machinery A case study of Stress Corrosion Cracking or SCC is a part of this project title. Stress corrosion cracking (SCC) can be divided into three important keywords to differentiate the mechanism which is tending to cause the fracture mechanism over the metallic material. SCC is caused by three conditions such as types of environment, types of materials and types of stress. Continuous research was encouraged to solve this problem from time to time in order to recognize main problem in obtaining the best solution. University Malaysia Sarawak, UNIMAS. 2005 Final Year Project Report / IMRAD NonPeerReviewed text en http://ir.unimas.my/id/eprint/2790/1/Construction%20of%20a%20crack%20growth%20testing%20apparatus%20associated%20with%20stress%20corrosion%20cracking%20%28SCC%29%20study.pdf text en http://ir.unimas.my/id/eprint/2790/8/Peter%20Anderson.pdf Peter Anderson, anak Joseph (2005) Construction of a crack growth testing apparatus associated with stress corrosion cracking (SCC) study. [Final Year Project Report / IMRAD] (Unpublished) |
| spellingShingle | TJ Mechanical engineering and machinery Peter Anderson, anak Joseph Construction of a crack growth testing apparatus associated with stress corrosion cracking (SCC) study |
| title | Construction of a crack growth testing apparatus associated with stress corrosion cracking (SCC) study |
| title_full | Construction of a crack growth testing apparatus associated with stress corrosion cracking (SCC) study |
| title_fullStr | Construction of a crack growth testing apparatus associated with stress corrosion cracking (SCC) study |
| title_full_unstemmed | Construction of a crack growth testing apparatus associated with stress corrosion cracking (SCC) study |
| title_short | Construction of a crack growth testing apparatus associated with stress corrosion cracking (SCC) study |
| title_sort | construction of a crack growth testing apparatus associated with stress corrosion cracking (scc) study |
| topic | TJ Mechanical engineering and machinery |
| url | http://ir.unimas.my/id/eprint/2790/ http://ir.unimas.my/id/eprint/2790/1/Construction%20of%20a%20crack%20growth%20testing%20apparatus%20associated%20with%20stress%20corrosion%20cracking%20%28SCC%29%20study.pdf http://ir.unimas.my/id/eprint/2790/8/Peter%20Anderson.pdf |