Construction of a crack growth testing apparatus associated with stress corrosion cracking (SCC) study
A case study of Stress Corrosion Cracking or SCC is a part of this project title. Stress corrosion cracking (SCC) can be divided into three important keywords to differentiate the mechanism which is tending to cause the fracture mechanism over the metallic material. SCC is caused by three conditions...
| Main Author: | |
|---|---|
| Format: | Final Year Project Report / IMRAD |
| Language: | English English |
| Published: |
University Malaysia Sarawak, UNIMAS.
2005
|
| Subjects: | |
| Online Access: | http://ir.unimas.my/id/eprint/2790/ http://ir.unimas.my/id/eprint/2790/1/Construction%20of%20a%20crack%20growth%20testing%20apparatus%20associated%20with%20stress%20corrosion%20cracking%20%28SCC%29%20study.pdf http://ir.unimas.my/id/eprint/2790/8/Peter%20Anderson.pdf |
| Summary: | A case study of Stress Corrosion Cracking or SCC is a part of this project title. Stress corrosion cracking (SCC) can be divided into three important keywords to differentiate the mechanism which is tending to cause the fracture mechanism over the metallic material. SCC is caused by three conditions such as types of environment, types of materials and types of stress. Continuous research was encouraged to solve this problem from time to time in order to recognize main problem in obtaining the best solution. |
|---|