Defect Detection on Welding Joint using Acoustic Emission Technology
This study was carried out as an initial study to investigate the potential of acoustic emission technology to to detect the welding defects on steel. Two pieces of mild steels were welded together in the middle part of steel. The welding specimen was made with defects and without defects. This wa...
| Main Authors: | , , |
|---|---|
| Format: | Conference or Workshop Item |
| Language: | English |
| Published: |
2013
|
| Subjects: | |
| Online Access: | http://umpir.ump.edu.my/id/eprint/6160/ http://umpir.ump.edu.my/id/eprint/6160/1/Defect_Detection_on_Welding_Joint_using_Acoustic_Emission_Technology.pdf |
| _version_ | 1848817710841987072 |
|---|---|
| author | Miminorazeansuhaila, Loman Che Ku Eddy Nizwan, Che Ku Husin Norshalawati, Mat Yusof |
| author_facet | Miminorazeansuhaila, Loman Che Ku Eddy Nizwan, Che Ku Husin Norshalawati, Mat Yusof |
| author_sort | Miminorazeansuhaila, Loman |
| building | UMP Institutional Repository |
| collection | Online Access |
| description | This study was carried out as an initial study to
investigate the potential of acoustic emission technology to to detect the welding defects on steel. Two pieces of mild steels were welded together in the middle part of steel. The welding specimen was made with defects and without defects. This was purposely done to compare the difference that might be existed between these two types of specimen. The piezoelectric sensor was located on both of the welding specimens while specimens were pressurised to promote cracks. During the experimental work, the acoustic emission signatures were acquired using the AE node acoustic emission data acquisition system. The signals were analysed using the AEWin software in order to verify the defects. Comparison made from the analysis showed that there were differences between the welding specimen with defects and without defects. From the analysis done, it shows that the welding specimen with defect produced higher value of acoustic emission parameter such as peak amplitude and RMS.
|
| first_indexed | 2025-11-15T01:26:06Z |
| format | Conference or Workshop Item |
| id | ump-6160 |
| institution | Universiti Malaysia Pahang |
| institution_category | Local University |
| language | English |
| last_indexed | 2025-11-15T01:26:06Z |
| publishDate | 2013 |
| recordtype | eprints |
| repository_type | Digital Repository |
| spelling | ump-61602015-03-03T09:28:33Z http://umpir.ump.edu.my/id/eprint/6160/ Defect Detection on Welding Joint using Acoustic Emission Technology Miminorazeansuhaila, Loman Che Ku Eddy Nizwan, Che Ku Husin Norshalawati, Mat Yusof TJ Mechanical engineering and machinery This study was carried out as an initial study to investigate the potential of acoustic emission technology to to detect the welding defects on steel. Two pieces of mild steels were welded together in the middle part of steel. The welding specimen was made with defects and without defects. This was purposely done to compare the difference that might be existed between these two types of specimen. The piezoelectric sensor was located on both of the welding specimens while specimens were pressurised to promote cracks. During the experimental work, the acoustic emission signatures were acquired using the AE node acoustic emission data acquisition system. The signals were analysed using the AEWin software in order to verify the defects. Comparison made from the analysis showed that there were differences between the welding specimen with defects and without defects. From the analysis done, it shows that the welding specimen with defect produced higher value of acoustic emission parameter such as peak amplitude and RMS. 2013 Conference or Workshop Item PeerReviewed application/pdf en http://umpir.ump.edu.my/id/eprint/6160/1/Defect_Detection_on_Welding_Joint_using_Acoustic_Emission_Technology.pdf Miminorazeansuhaila, Loman and Che Ku Eddy Nizwan, Che Ku Husin and Norshalawati, Mat Yusof (2013) Defect Detection on Welding Joint using Acoustic Emission Technology. In: International Conference on Innovations in Engineering and Technology (ICIET'2013) , 25-26 December 2013 , Bangkok, Thailand. pp. 154-157.. (Published) http://dx.doi.org/10.15242/IIE.E1213597 |
| spellingShingle | TJ Mechanical engineering and machinery Miminorazeansuhaila, Loman Che Ku Eddy Nizwan, Che Ku Husin Norshalawati, Mat Yusof Defect Detection on Welding Joint using Acoustic Emission Technology |
| title | Defect Detection on Welding Joint using Acoustic Emission Technology |
| title_full | Defect Detection on Welding Joint using Acoustic Emission Technology |
| title_fullStr | Defect Detection on Welding Joint using Acoustic Emission Technology |
| title_full_unstemmed | Defect Detection on Welding Joint using Acoustic Emission Technology |
| title_short | Defect Detection on Welding Joint using Acoustic Emission Technology |
| title_sort | defect detection on welding joint using acoustic emission technology |
| topic | TJ Mechanical engineering and machinery |
| url | http://umpir.ump.edu.my/id/eprint/6160/ http://umpir.ump.edu.my/id/eprint/6160/ http://umpir.ump.edu.my/id/eprint/6160/1/Defect_Detection_on_Welding_Joint_using_Acoustic_Emission_Technology.pdf |