Surface Erosion of Carbon Steel 1045 During Waterjet Peening
The present study investigates the effect of waterjet treatment on the surface characteristics of the carbon steel 1045. The effect of waterjet treatment parameters namely number of jet passes and pressure was investigated. An increase in the number of jet passes as well as pressure leads to a highe...
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Springer US
2014
|
| Subjects: | |
| Online Access: | http://umpir.ump.edu.my/id/eprint/6092/ http://umpir.ump.edu.my/id/eprint/6092/1/fkp-2014-azmir-Surface_Erosion_abs_only.pdf |
| _version_ | 1848817691945598976 |
|---|---|
| author | Azmir, Azhari Schindler, Christian Nkoumbou, Jhislain Kerscher, Eberhard |
| author_facet | Azmir, Azhari Schindler, Christian Nkoumbou, Jhislain Kerscher, Eberhard |
| author_sort | Azmir, Azhari |
| building | UMP Institutional Repository |
| collection | Online Access |
| description | The present study investigates the effect of waterjet treatment on the surface characteristics of the carbon steel 1045. The effect of waterjet treatment parameters namely number of jet passes and pressure was investigated. An increase in the number of jet passes as well as pressure leads to a higher roughness and more erosion of the surface. The damage features consist of various fracture mechanism modes occurred at the initial and evolved damage stage. The ferrite phase experienced more damage than the pearlite phase. However, the damage was more concentrated along the grain boundaries. The shearing force from the jet lateral flow raised the circumferential rim and created lateral cracks and sub-tunnels which might eventually be removed in the subsequent jet passes. The hardness of the treated specimens increased with an increase in the number of jet passes and pressure. |
| first_indexed | 2025-11-15T01:25:48Z |
| format | Article |
| id | ump-6092 |
| institution | Universiti Malaysia Pahang |
| institution_category | Local University |
| language | English |
| last_indexed | 2025-11-15T01:25:48Z |
| publishDate | 2014 |
| publisher | Springer US |
| recordtype | eprints |
| repository_type | Digital Repository |
| spelling | ump-60922018-01-23T01:06:09Z http://umpir.ump.edu.my/id/eprint/6092/ Surface Erosion of Carbon Steel 1045 During Waterjet Peening Azmir, Azhari Schindler, Christian Nkoumbou, Jhislain Kerscher, Eberhard TS Manufactures The present study investigates the effect of waterjet treatment on the surface characteristics of the carbon steel 1045. The effect of waterjet treatment parameters namely number of jet passes and pressure was investigated. An increase in the number of jet passes as well as pressure leads to a higher roughness and more erosion of the surface. The damage features consist of various fracture mechanism modes occurred at the initial and evolved damage stage. The ferrite phase experienced more damage than the pearlite phase. However, the damage was more concentrated along the grain boundaries. The shearing force from the jet lateral flow raised the circumferential rim and created lateral cracks and sub-tunnels which might eventually be removed in the subsequent jet passes. The hardness of the treated specimens increased with an increase in the number of jet passes and pressure. Springer US 2014 Article PeerReviewed application/pdf en http://umpir.ump.edu.my/id/eprint/6092/1/fkp-2014-azmir-Surface_Erosion_abs_only.pdf Azmir, Azhari and Schindler, Christian and Nkoumbou, Jhislain and Kerscher, Eberhard (2014) Surface Erosion of Carbon Steel 1045 During Waterjet Peening. Journal of Materials Engineering and Performance, 23 (5). pp. 1870-1880. ISSN 1059-9495. (Published) http://dx.doi.org/10.1007/s11665-014-0932-9 DOI: 10.1007/s11665-014-0932-9 |
| spellingShingle | TS Manufactures Azmir, Azhari Schindler, Christian Nkoumbou, Jhislain Kerscher, Eberhard Surface Erosion of Carbon Steel 1045 During Waterjet Peening |
| title | Surface Erosion of Carbon Steel 1045 During Waterjet Peening |
| title_full | Surface Erosion of Carbon Steel 1045 During Waterjet Peening |
| title_fullStr | Surface Erosion of Carbon Steel 1045 During Waterjet Peening |
| title_full_unstemmed | Surface Erosion of Carbon Steel 1045 During Waterjet Peening |
| title_short | Surface Erosion of Carbon Steel 1045 During Waterjet Peening |
| title_sort | surface erosion of carbon steel 1045 during waterjet peening |
| topic | TS Manufactures |
| url | http://umpir.ump.edu.my/id/eprint/6092/ http://umpir.ump.edu.my/id/eprint/6092/ http://umpir.ump.edu.my/id/eprint/6092/ http://umpir.ump.edu.my/id/eprint/6092/1/fkp-2014-azmir-Surface_Erosion_abs_only.pdf |