Structural, optical and morphological properties of pure and silver doped zinc oxide thin films by attuning the deposition layer
Pure Zinc oxide (ZnO) and silver doped ZnO (Ag/ZnO) thin films have potential applications in many optoelectronic devices. In this work, ZnO and Ag/ZnO thin films were prepared by a low-cost sol–gel method followed by a spin coating technique on glass substrates. Both ZnO and Ag/ZnO were spin-coated...
| Main Authors: | , |
|---|---|
| Format: | Conference or Workshop Item |
| Language: | English English |
| Published: |
Elsevier Ltd
2021
|
| Subjects: | |
| Online Access: | http://umpir.ump.edu.my/id/eprint/42382/ http://umpir.ump.edu.my/id/eprint/42382/1/Structural%2C%20optical%20and%20morphological%20properties%20of%20pure.pdf http://umpir.ump.edu.my/id/eprint/42382/2/Structural%2C%20optical%20and%20morphological%20properties%20of%20pure%20and%20silver%20doped%20zinc%20oxide%20thin%20films%20by%20attuning%20the%20deposition%20layer_ABS.pdf |
| Summary: | Pure Zinc oxide (ZnO) and silver doped ZnO (Ag/ZnO) thin films have potential applications in many optoelectronic devices. In this work, ZnO and Ag/ZnO thin films were prepared by a low-cost sol–gel method followed by a spin coating technique on glass substrates. Both ZnO and Ag/ZnO were spin-coated at various deposition layers (ranging from 3 to 11 deposition layers) to investigate the correlation of films’ thickness on the structural and optical properties. All the prepared films were subjected to an annealing temperature of 300 °C for 1 hr. The results showed that ZnO and Ag/ZnO XRD patterns had polycrystalline wurtzite structures with (101) direction domination. On the other hand, with the addition of silver dopant, the optical properties were improved at a transmittance value greater than 90% compared to ZnO (80% transmittance). FESEM results revealed that the ZnO thin film’s average grain measurement was about 65.4 nm, while Ag/ZnO exhibits grain measurement of approximately 69.3 nm. The surface morphologies showed that Ag/ZnO thin films exhibit a rougher surface due to the aggregation of silver nanoparticles. Despite the existence of agglomerated nanoparticles and higher deposition layer, the optical transmission of the Ag/ZnO is undistorted. |
|---|