Mechanistic Model of Stress Corrosion Cracking (SCC) of Carbon Steel in Acidic Solution with Presence of H2s
In oil and gas industrial environments, H2S gas is one of the corrosive species which should be a main concern in designing infrastructure made of carbon steel. Combination between the corrosive environment and stress condition will cause degradation of carbon steel increase un...
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
IOP Publishing
2013
|
| Subjects: | |
| Online Access: | http://umpir.ump.edu.my/id/eprint/4125/ http://umpir.ump.edu.my/id/eprint/4125/1/P327.pdf |
| _version_ | 1848817336040030208 |
|---|---|
| author | Asmara, Y. P. Juliawati, Alias Ahmad Shahrizan, Sulaiman Jamiluddin, Jaafar |
| author_facet | Asmara, Y. P. Juliawati, Alias Ahmad Shahrizan, Sulaiman Jamiluddin, Jaafar |
| author_sort | Asmara, Y. P. |
| building | UMP Institutional Repository |
| collection | Online Access |
| description | In oil and gas industrial environments, H2S gas is one of the corrosive species which should be a main concern in designing infrastructure made of carbon steel. Combination between the corrosive environment and stress condition will cause degradation of carbon steel increase unpredictably due to their simultaneous effects. This paper will design a model that involves electrochemical and mechanical theories to study crack growth rate under presence of H2S gas. Combination crack and corrosion propagation of carbon steel, with different hydrogen concentration has been investigated. The results indicated that high concentration of hydrogen ions showed a higher crack propagation rate. The comparison between corrosion prediction models and corrosion model developed by researchers used to verify the model accuracy showed a good agreement. |
| first_indexed | 2025-11-15T01:20:09Z |
| format | Article |
| id | ump-4125 |
| institution | Universiti Malaysia Pahang |
| institution_category | Local University |
| language | English |
| last_indexed | 2025-11-15T01:20:09Z |
| publishDate | 2013 |
| publisher | IOP Publishing |
| recordtype | eprints |
| repository_type | Digital Repository |
| spelling | ump-41252019-07-17T02:26:00Z http://umpir.ump.edu.my/id/eprint/4125/ Mechanistic Model of Stress Corrosion Cracking (SCC) of Carbon Steel in Acidic Solution with Presence of H2s Asmara, Y. P. Juliawati, Alias Ahmad Shahrizan, Sulaiman Jamiluddin, Jaafar TJ Mechanical engineering and machinery In oil and gas industrial environments, H2S gas is one of the corrosive species which should be a main concern in designing infrastructure made of carbon steel. Combination between the corrosive environment and stress condition will cause degradation of carbon steel increase unpredictably due to their simultaneous effects. This paper will design a model that involves electrochemical and mechanical theories to study crack growth rate under presence of H2S gas. Combination crack and corrosion propagation of carbon steel, with different hydrogen concentration has been investigated. The results indicated that high concentration of hydrogen ions showed a higher crack propagation rate. The comparison between corrosion prediction models and corrosion model developed by researchers used to verify the model accuracy showed a good agreement. IOP Publishing 2013-07-01 Article PeerReviewed application/pdf en http://umpir.ump.edu.my/id/eprint/4125/1/P327.pdf Asmara, Y. P. and Juliawati, Alias and Ahmad Shahrizan, Sulaiman and Jamiluddin, Jaafar (2013) Mechanistic Model of Stress Corrosion Cracking (SCC) of Carbon Steel in Acidic Solution with Presence of H2s. IOP Conference Series: Materials Science and Engineering, 50 (1). pp. 1-10. ISSN 1757-8981 (Print), 1757-899X (Online). (Published) http://dx.doi.org/10.1088/1757-899X/50/1/012072 DOI: 10.1088/1757-899X/50/1/012072 |
| spellingShingle | TJ Mechanical engineering and machinery Asmara, Y. P. Juliawati, Alias Ahmad Shahrizan, Sulaiman Jamiluddin, Jaafar Mechanistic Model of Stress Corrosion Cracking (SCC) of Carbon Steel in Acidic Solution with Presence of H2s |
| title | Mechanistic Model of Stress Corrosion Cracking (SCC) of Carbon Steel in Acidic Solution with Presence of H2s |
| title_full | Mechanistic Model of Stress Corrosion Cracking (SCC) of Carbon Steel in Acidic Solution with Presence of H2s |
| title_fullStr | Mechanistic Model of Stress Corrosion Cracking (SCC) of Carbon Steel in Acidic Solution with Presence of H2s |
| title_full_unstemmed | Mechanistic Model of Stress Corrosion Cracking (SCC) of Carbon Steel in Acidic Solution with Presence of H2s |
| title_short | Mechanistic Model of Stress Corrosion Cracking (SCC) of Carbon Steel in Acidic Solution with Presence of H2s |
| title_sort | mechanistic model of stress corrosion cracking (scc) of carbon steel in acidic solution with presence of h2s |
| topic | TJ Mechanical engineering and machinery |
| url | http://umpir.ump.edu.my/id/eprint/4125/ http://umpir.ump.edu.my/id/eprint/4125/ http://umpir.ump.edu.my/id/eprint/4125/ http://umpir.ump.edu.my/id/eprint/4125/1/P327.pdf |