Ethanolic mangifera indica leaves extract as green corrosion inhibitor
Mangifera indica (MI) or mango leaf as a green corrosion inhibitor for copper has been studied. The MI was extracted in ethanol solvent and prepared at different concentrations of 0, 0.4, 0.6 and 0.8 mg/ml in 1 M HCl solutions to imitate the corrosive environment. The as-prepared MI extract analyzed...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Penerbit Akademia Baru
2023
|
| Subjects: | |
| Online Access: | http://umpir.ump.edu.my/id/eprint/37633/ http://umpir.ump.edu.my/id/eprint/37633/1/Ethanolic%20mangifera%20indica%20leaves%20extract%20as%20green%20corrosion%20inhibitor.pdf |
| Summary: | Mangifera indica (MI) or mango leaf as a green corrosion inhibitor for copper has been studied. The MI was extracted in ethanol solvent and prepared at different concentrations of 0, 0.4, 0.6 and 0.8 mg/ml in 1 M HCl solutions to imitate the corrosive environment. The as-prepared MI extract analyzed by UV-Vis Spectrophotometer shows a shoulder peak at about 370 nm, resulting from the π → π* and n → π* electronic transition of aromatic C=C and carbonyl (C=O) functional groups. A Fourier transform infrared spectroscopy (FTIR) found that the MI extract exhibits aromatic C=C, C=O groups of phenolic compounds, C-OH, and C-O stretching vibrations. The electrochemical impedance spectroscopy (EIS) and Tafel plot analysis evaluate that the optimum corrosion inhibition of copper was achieved at 0.6 mg/ml concentration. The result is supported by a positive shift in the corrosion potential, Ecorr, lower corrosion current, Icorr and corrosion rate (CR) at-0.233 V, 4.39 µA/cm2 and 0.05 mm/yr, respectively. The surface morphology of the copper substrate after the corrosion test evaluated using metallurgical microscopy shows tremendous corrosion inhibition due to the adsorption of the molecules from the MI extracts. |
|---|