Effect of Co0.5Ni0.5Fe2O4 nanoparticles addition in ag-sheathed Bi-2223 superconductor tapes prepared by co-precipitation method
Effect of complex magnetic oxide Co0.5Ni0.5Fe2O4 (CNFO) nanoparticles addition in (Bi1.6Pb0.4)Sr2Ca2Cu3O10 (Bi-2223) superconductor tapes was investigated. Ultrafine Bi-2223 powder precursor was prepared via co-precipitation method and was added with 0.01 – 0.05 wt.% Co0.5Ni0.5Fe2O4 nanoparticles du...
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Trans Tech Publications
2020
|
| Subjects: | |
| Online Access: | http://umpir.ump.edu.my/id/eprint/30464/ http://umpir.ump.edu.my/id/eprint/30464/1/2.1%20Effect%20of%20Co0.5Ni0.5Fe2O4%20nanoparticles%20addition%20in%20ag-sheathed%20Bi-2223.docx.pdf |
| Summary: | Effect of complex magnetic oxide Co0.5Ni0.5Fe2O4 (CNFO) nanoparticles addition in (Bi1.6Pb0.4)Sr2Ca2Cu3O10 (Bi-2223) superconductor tapes was investigated. Ultrafine Bi-2223 powder precursor was prepared via co-precipitation method and was added with 0.01 – 0.05 wt.% Co0.5Ni0.5Fe2O4 nanoparticles during the final heating stage. The sample with 0.01 wt.% addition, Bi-2223(CNFO)0.01 was found to have the highest critical current density, Jc. This sample were then chosen to be fabricated into Ag-sheathed superconductor tapes using the powder-in-tube (PIT) method. The tapes were sintered for 50 and 100 h at 845 °C. The phase, microstructure and Jc of the samples were determined by powder X-ray diffraction (XRD), scanning electron microscopy (SEM) and four point probe, respectively. Jc of Ag-sheathed Bi-2223(CNFO)0.01 tapes sintered for 100 h was 19830 A/cm2 at 30 K and 3970 A/cm2 at 77 K compared to tapes without addition which showed a much lower Jc (6370 A/cm2 at 30 K). This study showed that CNFO nanoparticles could act as an effective flux pinning centers to enhance the critical current density in the Bi-2223 superconductor. |
|---|