Stress analysis on the reinforcement particles of the metal matrix composite by Raman spectroscopy
In this research, the stress state of the reinforcing SiC particles in a hybrid MMC is investigated by micro Raman spectroscopy. The experiment was carried out in situ in the Raman spectroscopy. Experimental results show that cracks due to monotonic loading propagates by the debonding of the particl...
| Main Authors: | , |
|---|---|
| Format: | Conference or Workshop Item |
| Language: | English |
| Published: |
IOP Publishing
2017
|
| Subjects: | |
| Online Access: | http://umpir.ump.edu.my/id/eprint/23343/ http://umpir.ump.edu.my/id/eprint/23343/1/Stress%20analysis%20on%20the%20reinforcement%20particles%20of%20the%20metal%20matrix%20composite%20by%20Raman%20spectroscopy.docx |
| _version_ | 1848821781401436160 |
|---|---|
| author | Iqbal, AKM Asif Arai, Yoshio |
| author_facet | Iqbal, AKM Asif Arai, Yoshio |
| author_sort | Iqbal, AKM Asif |
| building | UMP Institutional Repository |
| collection | Online Access |
| description | In this research, the stress state of the reinforcing SiC particles in a hybrid MMC is investigated by micro Raman spectroscopy. The experiment was carried out in situ in the Raman spectroscopy. Experimental results show that cracks due to monotonic loading propagates by the debonding of the particle/matrix interface and particle fracture. Moreover, secondary cracks form in front of the main crack tip coalesce with the main crack in subsequent loading and final failure occurs. A high decrease in stress (several hundred in MPa) is observed with the interfacial debonding at the interface and with the particle fracture on the particle. The critical tensile stresses for particle-matrix interface debonding and particle fracture develop in hybrid MMC are also estimated during the crack propagation. |
| first_indexed | 2025-11-15T02:30:48Z |
| format | Conference or Workshop Item |
| id | ump-23343 |
| institution | Universiti Malaysia Pahang |
| institution_category | Local University |
| language | English |
| last_indexed | 2025-11-15T02:30:48Z |
| publishDate | 2017 |
| publisher | IOP Publishing |
| recordtype | eprints |
| repository_type | Digital Repository |
| spelling | ump-233432018-12-21T07:56:03Z http://umpir.ump.edu.my/id/eprint/23343/ Stress analysis on the reinforcement particles of the metal matrix composite by Raman spectroscopy Iqbal, AKM Asif Arai, Yoshio TS Manufactures In this research, the stress state of the reinforcing SiC particles in a hybrid MMC is investigated by micro Raman spectroscopy. The experiment was carried out in situ in the Raman spectroscopy. Experimental results show that cracks due to monotonic loading propagates by the debonding of the particle/matrix interface and particle fracture. Moreover, secondary cracks form in front of the main crack tip coalesce with the main crack in subsequent loading and final failure occurs. A high decrease in stress (several hundred in MPa) is observed with the interfacial debonding at the interface and with the particle fracture on the particle. The critical tensile stresses for particle-matrix interface debonding and particle fracture develop in hybrid MMC are also estimated during the crack propagation. IOP Publishing 2017 Conference or Workshop Item PeerReviewed pdf en http://umpir.ump.edu.my/id/eprint/23343/1/Stress%20analysis%20on%20the%20reinforcement%20particles%20of%20the%20metal%20matrix%20composite%20by%20Raman%20spectroscopy.docx Iqbal, AKM Asif and Arai, Yoshio (2017) Stress analysis on the reinforcement particles of the metal matrix composite by Raman spectroscopy. In: 4th Asia Pacific Conference on Manufacturing Systems and the 3rd International Manufacturing Engineering Conference, APCOMS-iMEC 2017 , 7-8 December 2017 , Yogyakarta, Indonesia. pp. 1-7., 319 (1). ISSN 1757-8981 (Print), 1757-899X (Online) (Published) http://iopscience.iop.org/article/10.1088/1757-899X/319/1/012065/meta |
| spellingShingle | TS Manufactures Iqbal, AKM Asif Arai, Yoshio Stress analysis on the reinforcement particles of the metal matrix composite by Raman spectroscopy |
| title | Stress analysis on the reinforcement particles of the metal matrix composite by Raman spectroscopy |
| title_full | Stress analysis on the reinforcement particles of the metal matrix composite by Raman spectroscopy |
| title_fullStr | Stress analysis on the reinforcement particles of the metal matrix composite by Raman spectroscopy |
| title_full_unstemmed | Stress analysis on the reinforcement particles of the metal matrix composite by Raman spectroscopy |
| title_short | Stress analysis on the reinforcement particles of the metal matrix composite by Raman spectroscopy |
| title_sort | stress analysis on the reinforcement particles of the metal matrix composite by raman spectroscopy |
| topic | TS Manufactures |
| url | http://umpir.ump.edu.my/id/eprint/23343/ http://umpir.ump.edu.my/id/eprint/23343/ http://umpir.ump.edu.my/id/eprint/23343/1/Stress%20analysis%20on%20the%20reinforcement%20particles%20of%20the%20metal%20matrix%20composite%20by%20Raman%20spectroscopy.docx |