Stress Measurement During Crack Propagation In Metal Matrix Composites Using Micro-Raman Spectroscopy
The measurement of stress in the SiC particles during crack propagation was investigated by micro raman spectroscopy. The experiment was carried out in situ in the Raman spectroscopy. Experimental results showed that cracks due to monotonic loading propagated by the debonding of the particle/matrix...
| Main Authors: | , |
|---|---|
| Format: | Conference or Workshop Item |
| Language: | English English |
| Published: |
2016
|
| Subjects: | |
| Online Access: | http://umpir.ump.edu.my/id/eprint/14055/ http://umpir.ump.edu.my/id/eprint/14055/1/Stress%20Measurement%20During%20Crack%20Propagation%20In%20Metal%20Matrix%20Composites%20Using%20Micro-Raman%20Spectroscopy.pdf http://umpir.ump.edu.my/id/eprint/14055/7/fkp-2016-asif-Stress%20Measurement%20During%20Crack%20Propagation.pdf |
| _version_ | 1848819627847581696 |
|---|---|
| author | Iqbal, AKM Asif Arai, Yoshio |
| author_facet | Iqbal, AKM Asif Arai, Yoshio |
| author_sort | Iqbal, AKM Asif |
| building | UMP Institutional Repository |
| collection | Online Access |
| description | The measurement of stress in the SiC particles during crack propagation was investigated by micro raman spectroscopy. The experiment was carried out in situ in the Raman spectroscopy. Experimental results showed that cracks due to monotonic loading propagated by the debonding of the particle/matrix interface and particle fracture. A high decrease in stress was observed with the interfacial debonding at the interface and with the particle fracture on the particle. Moreover, the critical tensile stresses for particle-matrix interface debonding and particle fracture developed in hybrid MMC were also estimated during the crack propagation. |
| first_indexed | 2025-11-15T01:56:34Z |
| format | Conference or Workshop Item |
| id | ump-14055 |
| institution | Universiti Malaysia Pahang |
| institution_category | Local University |
| language | English English |
| last_indexed | 2025-11-15T01:56:34Z |
| publishDate | 2016 |
| recordtype | eprints |
| repository_type | Digital Repository |
| spelling | ump-140552018-02-23T03:35:31Z http://umpir.ump.edu.my/id/eprint/14055/ Stress Measurement During Crack Propagation In Metal Matrix Composites Using Micro-Raman Spectroscopy Iqbal, AKM Asif Arai, Yoshio TS Manufactures The measurement of stress in the SiC particles during crack propagation was investigated by micro raman spectroscopy. The experiment was carried out in situ in the Raman spectroscopy. Experimental results showed that cracks due to monotonic loading propagated by the debonding of the particle/matrix interface and particle fracture. A high decrease in stress was observed with the interfacial debonding at the interface and with the particle fracture on the particle. Moreover, the critical tensile stresses for particle-matrix interface debonding and particle fracture developed in hybrid MMC were also estimated during the crack propagation. 2016 Conference or Workshop Item NonPeerReviewed application/pdf en http://umpir.ump.edu.my/id/eprint/14055/1/Stress%20Measurement%20During%20Crack%20Propagation%20In%20Metal%20Matrix%20Composites%20Using%20Micro-Raman%20Spectroscopy.pdf application/pdf en http://umpir.ump.edu.my/id/eprint/14055/7/fkp-2016-asif-Stress%20Measurement%20During%20Crack%20Propagation.pdf Iqbal, AKM Asif and Arai, Yoshio (2016) Stress Measurement During Crack Propagation In Metal Matrix Composites Using Micro-Raman Spectroscopy. In: 17th European Conference on Composite Materials (ECCM17) , 26-30 June 2016 , Munich, Germany. pp. 1-8.. (Unpublished) (Unpublished) |
| spellingShingle | TS Manufactures Iqbal, AKM Asif Arai, Yoshio Stress Measurement During Crack Propagation In Metal Matrix Composites Using Micro-Raman Spectroscopy |
| title | Stress Measurement During Crack Propagation In Metal Matrix Composites Using Micro-Raman Spectroscopy |
| title_full | Stress Measurement During Crack Propagation In Metal Matrix Composites Using Micro-Raman Spectroscopy |
| title_fullStr | Stress Measurement During Crack Propagation In Metal Matrix Composites Using Micro-Raman Spectroscopy |
| title_full_unstemmed | Stress Measurement During Crack Propagation In Metal Matrix Composites Using Micro-Raman Spectroscopy |
| title_short | Stress Measurement During Crack Propagation In Metal Matrix Composites Using Micro-Raman Spectroscopy |
| title_sort | stress measurement during crack propagation in metal matrix composites using micro-raman spectroscopy |
| topic | TS Manufactures |
| url | http://umpir.ump.edu.my/id/eprint/14055/ http://umpir.ump.edu.my/id/eprint/14055/1/Stress%20Measurement%20During%20Crack%20Propagation%20In%20Metal%20Matrix%20Composites%20Using%20Micro-Raman%20Spectroscopy.pdf http://umpir.ump.edu.my/id/eprint/14055/7/fkp-2016-asif-Stress%20Measurement%20During%20Crack%20Propagation.pdf |