The environmental degradation of adhesive joint / Muhazli Muhammad and Rosli Yusof
Adhesive joints are expected to retain a significant proportion of their load bearing capacity for the entire duration of the service life of the bonded structure. However, service conditions can often involve exposure to combinations of static or fatigue load and hostile environment (marine, hot/we...
| Main Authors: | , |
|---|---|
| Format: | Student Project |
| Language: | English |
| Published: |
Faculty of Mechanical Engineering
1999
|
| Subjects: | |
| Online Access: | https://ir.uitm.edu.my/id/eprint/25776/ |
| _version_ | 1848806350876835840 |
|---|---|
| author | Muhammad, Muhazli Yusof, Rosli |
| author_facet | Muhammad, Muhazli Yusof, Rosli |
| author_sort | Muhammad, Muhazli |
| building | UiTM Institutional Repository |
| collection | Online Access |
| description | Adhesive joints are expected to retain a significant proportion of their load bearing capacity for the entire duration of the service life of the bonded structure. However, service conditions can often involve exposure to combinations of static or fatigue load and hostile environment (marine, hot/wet, weathering or chemical). It is therefore essential that the end user and the adhesive manufacture possess the necessary tools for selecting and characterising an adhesive system, to ensure reliability bond performance under hostile operating condition. Optimising joint performance requires an understanding on the failure mechanisms involved in environment degradation, and validated test methods and design methodologies suitable for predicting material degradation and life expectancy. The general consensus is that wider used of adhesive technology has been impeded by a lack of reliable test methods, accelerated ageing procedures, quantitative data and predictive analysis for determining durability of structural adhesive joints to hostile environments. |
| first_indexed | 2025-11-14T22:25:32Z |
| format | Student Project |
| id | uitm-25776 |
| institution | Universiti Teknologi MARA |
| institution_category | Local University |
| language | English |
| last_indexed | 2025-11-14T22:25:32Z |
| publishDate | 1999 |
| publisher | Faculty of Mechanical Engineering |
| recordtype | eprints |
| repository_type | Digital Repository |
| spelling | uitm-257762019-09-25T07:26:45Z https://ir.uitm.edu.my/id/eprint/25776/ The environmental degradation of adhesive joint / Muhazli Muhammad and Rosli Yusof Muhammad, Muhazli Yusof, Rosli Materials of engineering and construction Building materials Earthwork. Foundations Adhesive joints are expected to retain a significant proportion of their load bearing capacity for the entire duration of the service life of the bonded structure. However, service conditions can often involve exposure to combinations of static or fatigue load and hostile environment (marine, hot/wet, weathering or chemical). It is therefore essential that the end user and the adhesive manufacture possess the necessary tools for selecting and characterising an adhesive system, to ensure reliability bond performance under hostile operating condition. Optimising joint performance requires an understanding on the failure mechanisms involved in environment degradation, and validated test methods and design methodologies suitable for predicting material degradation and life expectancy. The general consensus is that wider used of adhesive technology has been impeded by a lack of reliable test methods, accelerated ageing procedures, quantitative data and predictive analysis for determining durability of structural adhesive joints to hostile environments. Faculty of Mechanical Engineering 1999 Student Project NonPeerReviewed text en https://ir.uitm.edu.my/id/eprint/25776/1/PPb_MUHAZLI%20MUHAMAD%20EM%2099_5.pdf Muhammad, Muhazli and Yusof, Rosli (1999) The environmental degradation of adhesive joint / Muhazli Muhammad and Rosli Yusof. (1999) [Student Project] <http://terminalib.uitm.edu.my/25776.pdf> (Unpublished) |
| spellingShingle | Materials of engineering and construction Building materials Earthwork. Foundations Muhammad, Muhazli Yusof, Rosli The environmental degradation of adhesive joint / Muhazli Muhammad and Rosli Yusof |
| title | The environmental degradation of adhesive joint / Muhazli Muhammad and Rosli Yusof |
| title_full | The environmental degradation of adhesive joint / Muhazli Muhammad and Rosli Yusof |
| title_fullStr | The environmental degradation of adhesive joint / Muhazli Muhammad and Rosli Yusof |
| title_full_unstemmed | The environmental degradation of adhesive joint / Muhazli Muhammad and Rosli Yusof |
| title_short | The environmental degradation of adhesive joint / Muhazli Muhammad and Rosli Yusof |
| title_sort | environmental degradation of adhesive joint / muhazli muhammad and rosli yusof |
| topic | Materials of engineering and construction Building materials Earthwork. Foundations |
| url | https://ir.uitm.edu.my/id/eprint/25776/ |