Properties of cement board made from various sizes of oil palm trunk strands / Nurnabilah Hanee Che Ab Rahim
Wood cement board (WCB) is a combination of organic and inorganic material, wood with cement. For this experiment WCB use oil palm strands as organic material and Portland cement as the inorganic material. The aims of this experiment were to determine the physical and mechanical properties of the...
| Main Author: | |
|---|---|
| Format: | Student Project |
| Language: | English |
| Published: |
Faculty of Applied Sciences
2016
|
| Subjects: | |
| Online Access: | https://ir.uitm.edu.my/id/eprint/22624/ |
| _version_ | 1848805541443272704 |
|---|---|
| author | Che Ab Rahim, Nurnabilah Hanee |
| author_facet | Che Ab Rahim, Nurnabilah Hanee |
| author_sort | Che Ab Rahim, Nurnabilah Hanee |
| building | UiTM Institutional Repository |
| collection | Online Access |
| description | Wood cement board (WCB) is a combination of organic and inorganic material,
wood with cement. For this experiment WCB use oil palm strands as organic
material and Portland cement as the inorganic material. The aims of this
experiment were to determine the physical and mechanical properties of the
cement board of different densities using oil palm strands with different size. For
this experiment the WCB dimension was 450mm x 450mm x 12mm. The
additive component used in WCB was aluminum sulphate (1.5%) and sodium
silicate (3%). The tests done were bending strength (modulus of elasticity (MOE)
and modulus of rupture (MOR», water absorption, thickness swelling and screw
withdrawal. The results showed that the WCB with density of 1300kg/m3 have
higher mechanical strength than 1100kg/m3 and 900kg/m3 boards. As for the
study of water absorption (WA) board with a density of 900kg/m3 with size of
30mm have highest absorption compared to others. The best mechanical
strength was for density 1300kg/m3 with 50mm strand size with MOE 1315.6
MPa and MOR 4.6 MPa. |
| first_indexed | 2025-11-14T22:12:40Z |
| format | Student Project |
| id | uitm-22624 |
| institution | Universiti Teknologi MARA |
| institution_category | Local University |
| language | English |
| last_indexed | 2025-11-14T22:12:40Z |
| publishDate | 2016 |
| publisher | Faculty of Applied Sciences |
| recordtype | eprints |
| repository_type | Digital Repository |
| spelling | uitm-226242019-02-04T08:08:15Z https://ir.uitm.edu.my/id/eprint/22624/ Properties of cement board made from various sizes of oil palm trunk strands / Nurnabilah Hanee Che Ab Rahim Che Ab Rahim, Nurnabilah Hanee Production management. Operations management Wood technology. Lumber Engineered wood. Fiberboard, particle board, etc. Wood cement board (WCB) is a combination of organic and inorganic material, wood with cement. For this experiment WCB use oil palm strands as organic material and Portland cement as the inorganic material. The aims of this experiment were to determine the physical and mechanical properties of the cement board of different densities using oil palm strands with different size. For this experiment the WCB dimension was 450mm x 450mm x 12mm. The additive component used in WCB was aluminum sulphate (1.5%) and sodium silicate (3%). The tests done were bending strength (modulus of elasticity (MOE) and modulus of rupture (MOR», water absorption, thickness swelling and screw withdrawal. The results showed that the WCB with density of 1300kg/m3 have higher mechanical strength than 1100kg/m3 and 900kg/m3 boards. As for the study of water absorption (WA) board with a density of 900kg/m3 with size of 30mm have highest absorption compared to others. The best mechanical strength was for density 1300kg/m3 with 50mm strand size with MOE 1315.6 MPa and MOR 4.6 MPa. Faculty of Applied Sciences 2016 Student Project NonPeerReviewed text en https://ir.uitm.edu.my/id/eprint/22624/1/PPb_NURNABILAH%20HANEE%20CHE%20AB%20RAHIM%20AS%20C%2016_5.PDF Che Ab Rahim, Nurnabilah Hanee (2016) Properties of cement board made from various sizes of oil palm trunk strands / Nurnabilah Hanee Che Ab Rahim. (2016) [Student Project] <http://terminalib.uitm.edu.my/22624.pdf> (Unpublished) |
| spellingShingle | Production management. Operations management Wood technology. Lumber Engineered wood. Fiberboard, particle board, etc. Che Ab Rahim, Nurnabilah Hanee Properties of cement board made from various sizes of oil palm trunk strands / Nurnabilah Hanee Che Ab Rahim |
| title | Properties of cement board made from various sizes of oil
palm trunk strands / Nurnabilah Hanee Che Ab Rahim |
| title_full | Properties of cement board made from various sizes of oil
palm trunk strands / Nurnabilah Hanee Che Ab Rahim |
| title_fullStr | Properties of cement board made from various sizes of oil
palm trunk strands / Nurnabilah Hanee Che Ab Rahim |
| title_full_unstemmed | Properties of cement board made from various sizes of oil
palm trunk strands / Nurnabilah Hanee Che Ab Rahim |
| title_short | Properties of cement board made from various sizes of oil
palm trunk strands / Nurnabilah Hanee Che Ab Rahim |
| title_sort | properties of cement board made from various sizes of oil
palm trunk strands / nurnabilah hanee che ab rahim |
| topic | Production management. Operations management Wood technology. Lumber Engineered wood. Fiberboard, particle board, etc. |
| url | https://ir.uitm.edu.my/id/eprint/22624/ |