Mechanical and physical properties of acacia mangium spp forwood cement board relation to particle size and cement ratio / Mohamad Dzulhelme Hairuddin
ABSTRACT Mechanical and Physical properties of Acacia Mangium for wood cement board relation to particle size and cement This research was performed to determine the properties of wood cement board (WCB) made from Acacia mangium Wood.The different wood of particle size (0.5mm,1.0mm and 2.0mm) a...
| Main Author: | |
|---|---|
| Format: | Student Project |
| Language: | English |
| Published: |
Faculty of Applied Sciences
2015
|
| Subjects: | |
| Online Access: | https://ir.uitm.edu.my/id/eprint/19978/ |
| _version_ | 1848804903745486848 |
|---|---|
| author | Hairuddin, Mohamad Dzulhelme |
| author_facet | Hairuddin, Mohamad Dzulhelme |
| author_sort | Hairuddin, Mohamad Dzulhelme |
| building | UiTM Institutional Repository |
| collection | Online Access |
| description | ABSTRACT
Mechanical and Physical properties of Acacia Mangium for wood
cement board relation to particle size and cement
This research was performed to determine the properties of wood cement
board (WCB) made from Acacia mangium Wood.The different wood of
particle size (0.5mm,1.0mm and 2.0mm) and Wood cement ratio (1:25 and
1:30) was applied.The target of board density was 1300kg m3.The physical
(water absorption test and thickness swelling) and mechanical (bending test
and internal bending test) properties of the WCB were evaluated.From the
research, it showed that there is no significant different in physical and
mechanical properties of WeB except for internal bonding in different test
using the particle size.The result for modulus of rupture(MOR),water
absorption and thickness swelling meet the requirement standard of
MS544:2001.The application of different wood cement ratio also showed
same result pattern,where there is different no significant for all
testing.However wood cement ration 1:2.5 force feeds better (MOR) then
compared to 1:3.0.Higher content cement causes a general decrease in
MOR,WA and TS.
Keyword: Acacia mangium wood |
| first_indexed | 2025-11-14T22:02:32Z |
| format | Student Project |
| id | uitm-19978 |
| institution | Universiti Teknologi MARA |
| institution_category | Local University |
| language | English |
| last_indexed | 2025-11-14T22:02:32Z |
| publishDate | 2015 |
| publisher | Faculty of Applied Sciences |
| recordtype | eprints |
| repository_type | Digital Repository |
| spelling | uitm-199782019-05-15T05:08:42Z https://ir.uitm.edu.my/id/eprint/19978/ Mechanical and physical properties of acacia mangium spp forwood cement board relation to particle size and cement ratio / Mohamad Dzulhelme Hairuddin Hairuddin, Mohamad Dzulhelme Plant gene isolation S Agriculture (General) ABSTRACT Mechanical and Physical properties of Acacia Mangium for wood cement board relation to particle size and cement This research was performed to determine the properties of wood cement board (WCB) made from Acacia mangium Wood.The different wood of particle size (0.5mm,1.0mm and 2.0mm) and Wood cement ratio (1:25 and 1:30) was applied.The target of board density was 1300kg m3.The physical (water absorption test and thickness swelling) and mechanical (bending test and internal bending test) properties of the WCB were evaluated.From the research, it showed that there is no significant different in physical and mechanical properties of WeB except for internal bonding in different test using the particle size.The result for modulus of rupture(MOR),water absorption and thickness swelling meet the requirement standard of MS544:2001.The application of different wood cement ratio also showed same result pattern,where there is different no significant for all testing.However wood cement ration 1:2.5 force feeds better (MOR) then compared to 1:3.0.Higher content cement causes a general decrease in MOR,WA and TS. Keyword: Acacia mangium wood Faculty of Applied Sciences 2015 Student Project NonPeerReviewed text en https://ir.uitm.edu.my/id/eprint/19978/1/PPb_MOHAMAD%20DZULHELME%20HAIRUDDIN%20AS%20C%2015_5.pdf.PDF Hairuddin, Mohamad Dzulhelme (2015) Mechanical and physical properties of acacia mangium spp forwood cement board relation to particle size and cement ratio / Mohamad Dzulhelme Hairuddin. (2015) [Student Project] <http://terminalib.uitm.edu.my/19978.pdf> (Unpublished) |
| spellingShingle | Plant gene isolation S Agriculture (General) Hairuddin, Mohamad Dzulhelme Mechanical and physical properties of acacia mangium spp forwood cement board relation to particle size and cement ratio / Mohamad Dzulhelme Hairuddin |
| title | Mechanical and physical properties of acacia mangium spp
forwood cement board relation to particle size and
cement ratio / Mohamad Dzulhelme Hairuddin |
| title_full | Mechanical and physical properties of acacia mangium spp
forwood cement board relation to particle size and
cement ratio / Mohamad Dzulhelme Hairuddin |
| title_fullStr | Mechanical and physical properties of acacia mangium spp
forwood cement board relation to particle size and
cement ratio / Mohamad Dzulhelme Hairuddin |
| title_full_unstemmed | Mechanical and physical properties of acacia mangium spp
forwood cement board relation to particle size and
cement ratio / Mohamad Dzulhelme Hairuddin |
| title_short | Mechanical and physical properties of acacia mangium spp
forwood cement board relation to particle size and
cement ratio / Mohamad Dzulhelme Hairuddin |
| title_sort | mechanical and physical properties of acacia mangium spp
forwood cement board relation to particle size and
cement ratio / mohamad dzulhelme hairuddin |
| topic | Plant gene isolation S Agriculture (General) |
| url | https://ir.uitm.edu.my/id/eprint/19978/ |