Degree of hydration of OPC and OPC/FA pastes dried in different relative humidity
In this research; the degree of hydration of the pastes and the compressive strength of the 50 mm cubes prepared with the 100% cement and fly ash blended cement was determined. 24 hours after casting mortar cubes and the paste samples were cured for 28 days in the fog room. After 28 days curing;...
| Main Authors: | , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
2010
|
| Subjects: | |
| Online Access: | http://scholars.utp.edu.my/id/eprint/2959/ http://scholars.utp.edu.my/id/eprint/2959/1/92-360-1-PB.pdf |
| _version_ | 1848659332228448256 |
|---|---|
| author | Shafiq, Nasir Nuruddin, Fadhil |
| author_facet | Shafiq, Nasir Nuruddin, Fadhil |
| author_sort | Shafiq, Nasir |
| building | UTP Institutional Repository |
| collection | Online Access |
| description | In this research; the degree of hydration of the pastes and the compressive strength of the 50
mm cubes prepared with the 100% cement and fly ash blended cement was determined. 24
hours after casting mortar cubes and the paste samples were cured for 28 days in the fog
room. After 28 days curing; a set of 3 cubes and a paste sample was dried in the 100%,
75%, 65%, 40% and 12% ambient relative humidity at the constant temperature of 27oC.
Drying conditions showed significant effects on the compressive strength and the degree of
hydration. Highest compressive strength of 70 MPa was measured for mortar cubes dried in
100% RH; similarly 97% degree of hydration was determined for 100% cement samples
dried in the 100% RH. For mortar cubes dried in 12% RH, the compressive strength was
measured between 47 and 53 MPa. The similar paste samples showed the maximum degree
of hydration as 81%. In conclusion, drying conditions have significant effects on the degree
of hydration of cement pastes, therefore other properties are also affected such as
compressive strength. |
| first_indexed | 2025-11-13T07:28:44Z |
| format | Article |
| id | oai:scholars.utp.edu.my:2959 |
| institution | Universiti Teknologi Petronas |
| institution_category | Local University |
| language | English |
| last_indexed | 2025-11-13T07:28:44Z |
| publishDate | 2010 |
| recordtype | eprints |
| repository_type | Digital Repository |
| spelling | oai:scholars.utp.edu.my:29592017-01-19T08:23:51Z http://scholars.utp.edu.my/id/eprint/2959/ Degree of hydration of OPC and OPC/FA pastes dried in different relative humidity Shafiq, Nasir Nuruddin, Fadhil TA Engineering (General). Civil engineering (General) In this research; the degree of hydration of the pastes and the compressive strength of the 50 mm cubes prepared with the 100% cement and fly ash blended cement was determined. 24 hours after casting mortar cubes and the paste samples were cured for 28 days in the fog room. After 28 days curing; a set of 3 cubes and a paste sample was dried in the 100%, 75%, 65%, 40% and 12% ambient relative humidity at the constant temperature of 27oC. Drying conditions showed significant effects on the compressive strength and the degree of hydration. Highest compressive strength of 70 MPa was measured for mortar cubes dried in 100% RH; similarly 97% degree of hydration was determined for 100% cement samples dried in the 100% RH. For mortar cubes dried in 12% RH, the compressive strength was measured between 47 and 53 MPa. The similar paste samples showed the maximum degree of hydration as 81%. In conclusion, drying conditions have significant effects on the degree of hydration of cement pastes, therefore other properties are also affected such as compressive strength. 2010-09 Article PeerReviewed application/pdf en http://scholars.utp.edu.my/id/eprint/2959/1/92-360-1-PB.pdf Shafiq, Nasir and Nuruddin, Fadhil (2010) Degree of hydration of OPC and OPC/FA pastes dried in different relative humidity. Concrete Research Letter. |
| spellingShingle | TA Engineering (General). Civil engineering (General) Shafiq, Nasir Nuruddin, Fadhil Degree of hydration of OPC and OPC/FA pastes dried in different relative humidity |
| title | Degree of hydration of OPC and OPC/FA pastes dried in different relative humidity |
| title_full | Degree of hydration of OPC and OPC/FA pastes dried in different relative humidity |
| title_fullStr | Degree of hydration of OPC and OPC/FA pastes dried in different relative humidity |
| title_full_unstemmed | Degree of hydration of OPC and OPC/FA pastes dried in different relative humidity |
| title_short | Degree of hydration of OPC and OPC/FA pastes dried in different relative humidity |
| title_sort | degree of hydration of opc and opc/fa pastes dried in different relative humidity |
| topic | TA Engineering (General). Civil engineering (General) |
| url | http://scholars.utp.edu.my/id/eprint/2959/ http://scholars.utp.edu.my/id/eprint/2959/1/92-360-1-PB.pdf |