Degree of hydration and compressive strength of conditioned samples made of normal and blended cement system
In this paper; results of the degree of hydration of the pastes and the compressive strength of the 50 mm cubes prepared with the 100% cement and fly ash blended cement was determined. 24 hours after casting mortar cubes and the paste samples were cured for 28 days in the fog room. After 28 days...
| Main Author: | |
|---|---|
| Format: | Citation Index Journal |
| Language: | English |
| Published: |
Springer
2011
|
| Subjects: | |
| Online Access: | http://scholars.utp.edu.my/id/eprint/1582/ http://scholars.utp.edu.my/id/eprint/1582/1/KSCE-S-10-00176.pdf |
| _version_ | 1848659138657124352 |
|---|---|
| author | Shafiq, N. |
| author_facet | Shafiq, N. |
| author_sort | Shafiq, N. |
| building | UTP Institutional Repository |
| collection | Online Access |
| description | In this paper; results of the degree of hydration of the pastes and the compressive strength of
the 50 mm cubes prepared with the 100% cement and fly ash blended cement was determined. 24
hours after casting mortar cubes and the paste samples were cured for 28 days in the fog room. After
28 days curing; a set of 3 cubes and a paste sample was dried in the 100%, 75%, 65%, 40% and 12%
ambient relative humidity at the constant temperature of 27oC. Drying conditions showed significant
affects on the compressive strength and the degree of hydration. Highest compressive strength of 70
MPa was measured of mortar cubes dried in 100% RH; similarly 97% degree of hydration was
determined for 100% cement samples dried in the 100% RH. For mortar cubes dried in 12% RH, the
compressive strength was measured between 47 and 53 MPa. The similar paste samples showed the
maximum degree of hydration as 81%. |
| first_indexed | 2025-11-13T07:25:40Z |
| format | Citation Index Journal |
| id | oai:scholars.utp.edu.my:1582 |
| institution | Universiti Teknologi Petronas |
| institution_category | Local University |
| language | English |
| last_indexed | 2025-11-13T07:25:40Z |
| publishDate | 2011 |
| publisher | Springer |
| recordtype | eprints |
| repository_type | Digital Repository |
| spelling | oai:scholars.utp.edu.my:15822017-01-19T08:22:28Z http://scholars.utp.edu.my/id/eprint/1582/ Degree of hydration and compressive strength of conditioned samples made of normal and blended cement system Shafiq, N. TA Engineering (General). Civil engineering (General) In this paper; results of the degree of hydration of the pastes and the compressive strength of the 50 mm cubes prepared with the 100% cement and fly ash blended cement was determined. 24 hours after casting mortar cubes and the paste samples were cured for 28 days in the fog room. After 28 days curing; a set of 3 cubes and a paste sample was dried in the 100%, 75%, 65%, 40% and 12% ambient relative humidity at the constant temperature of 27oC. Drying conditions showed significant affects on the compressive strength and the degree of hydration. Highest compressive strength of 70 MPa was measured of mortar cubes dried in 100% RH; similarly 97% degree of hydration was determined for 100% cement samples dried in the 100% RH. For mortar cubes dried in 12% RH, the compressive strength was measured between 47 and 53 MPa. The similar paste samples showed the maximum degree of hydration as 81%. Springer 2011-09 Citation Index Journal PeerReviewed application/pdf en http://scholars.utp.edu.my/id/eprint/1582/1/KSCE-S-10-00176.pdf Shafiq, N. (2011) Degree of hydration and compressive strength of conditioned samples made of normal and blended cement system. [Citation Index Journal] http://www.springer.com/12205 10.1007/s12295-11-193 10.1007/s12295-11-193 10.1007/s12295-11-193 |
| spellingShingle | TA Engineering (General). Civil engineering (General) Shafiq, N. Degree of hydration and compressive strength of conditioned samples made of normal and blended cement system |
| title | Degree of hydration and compressive strength of conditioned samples made of normal and
blended cement system |
| title_full | Degree of hydration and compressive strength of conditioned samples made of normal and
blended cement system |
| title_fullStr | Degree of hydration and compressive strength of conditioned samples made of normal and
blended cement system |
| title_full_unstemmed | Degree of hydration and compressive strength of conditioned samples made of normal and
blended cement system |
| title_short | Degree of hydration and compressive strength of conditioned samples made of normal and
blended cement system |
| title_sort | degree of hydration and compressive strength of conditioned samples made of normal and
blended cement system |
| topic | TA Engineering (General). Civil engineering (General) |
| url | http://scholars.utp.edu.my/id/eprint/1582/ http://scholars.utp.edu.my/id/eprint/1582/ http://scholars.utp.edu.my/id/eprint/1582/ http://scholars.utp.edu.my/id/eprint/1582/1/KSCE-S-10-00176.pdf |