Photoluminescence characteristic of magnesium Boro-Tellurite doped Eu3+ Ceramic
The series samples of xTeO2-(70-x)B2O3-30MgO with 0≤x≤30 mol% have been prepared via the solid-state reaction method. The composition sample of 30TeO2-40B2O3-30MgO were chosen as a doped sample in the composition of 100-y(30TeO2-40B2O3-30MgO)-yEu3+ with 0.2≤y≤2 mol% and were heated at 750oC. The XRD...
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Universiti Kebangsaan Malaysia
2015
|
| Online Access: | http://journalarticle.ukm.my/9272/ http://journalarticle.ukm.my/9272/1/19_Nur_zu_Ira_Bohari.pdf |
| _version_ | 1848812032361496576 |
|---|---|
| author | Nur Zu Ira Bohari, R. Hussin, Zuhairi Ibrahim, Hendrik O. Lintang, |
| author_facet | Nur Zu Ira Bohari, R. Hussin, Zuhairi Ibrahim, Hendrik O. Lintang, |
| author_sort | Nur Zu Ira Bohari, |
| building | UKM Institutional Repository |
| collection | Online Access |
| description | The series samples of xTeO2-(70-x)B2O3-30MgO with 0≤x≤30 mol% have been prepared via the solid-state reaction method. The composition sample of 30TeO2-40B2O3-30MgO were chosen as a doped sample in the composition of 100-y(30TeO2-40B2O3-30MgO)-yEu3+ with 0.2≤y≤2 mol% and were heated at 750oC. The XRD results showed that the major phase was Mg(Te2O5) while MgO(B2O3)2, MgTe6O13, Mg2(B2O5) and MgB4O7 was observed as a minor phase. The small phase of EuB2O4 and Eu2Te4O11 were detected by XRD when the composition of 30TeO2-40B2O3-30MgO were doped with 1.5% of Eu3+. The EDX analysis of 30TeO2-40B2O3-30MgO doped with 1.5% Eu3+ sample was confirmed the presence of boron (B), magnesium (Mg), tellurium (Te), oxygen (O) and europium (Eu) elements. From the FESEM images, the surface morphology of doped 1.5% Eu3+ samples was agglomerated compared with the undoped sample. The average diameter of the grain size is in the range of 50-100 μm. The emission spectra of the Eu3+-doped 30TeO2-40B2O3-30MgO ceramic consists of intense and sharp lines ranging from 550-725 nm. The luminescence spectra showed that the emission intensity of 30TeO2-40B2O3-30MgO doped with Eu3+ was enhanced with the increase of Eu3+ ion from 0.2 to 1.5 mol%, which resulted in enhancement of the red emission of the samples. The longest decay time for 30TeO2-40B2O3-30MgO doped with 1.5 mol % Eu3+ was 0.892 ms. |
| first_indexed | 2025-11-14T23:55:51Z |
| format | Article |
| id | oai:generic.eprints.org:9272 |
| institution | Universiti Kebangasaan Malaysia |
| institution_category | Local University |
| language | English |
| last_indexed | 2025-11-14T23:55:51Z |
| publishDate | 2015 |
| publisher | Universiti Kebangsaan Malaysia |
| recordtype | eprints |
| repository_type | Digital Repository |
| spelling | oai:generic.eprints.org:92722016-12-14T06:49:25Z http://journalarticle.ukm.my/9272/ Photoluminescence characteristic of magnesium Boro-Tellurite doped Eu3+ Ceramic Nur Zu Ira Bohari, R. Hussin, Zuhairi Ibrahim, Hendrik O. Lintang, The series samples of xTeO2-(70-x)B2O3-30MgO with 0≤x≤30 mol% have been prepared via the solid-state reaction method. The composition sample of 30TeO2-40B2O3-30MgO were chosen as a doped sample in the composition of 100-y(30TeO2-40B2O3-30MgO)-yEu3+ with 0.2≤y≤2 mol% and were heated at 750oC. The XRD results showed that the major phase was Mg(Te2O5) while MgO(B2O3)2, MgTe6O13, Mg2(B2O5) and MgB4O7 was observed as a minor phase. The small phase of EuB2O4 and Eu2Te4O11 were detected by XRD when the composition of 30TeO2-40B2O3-30MgO were doped with 1.5% of Eu3+. The EDX analysis of 30TeO2-40B2O3-30MgO doped with 1.5% Eu3+ sample was confirmed the presence of boron (B), magnesium (Mg), tellurium (Te), oxygen (O) and europium (Eu) elements. From the FESEM images, the surface morphology of doped 1.5% Eu3+ samples was agglomerated compared with the undoped sample. The average diameter of the grain size is in the range of 50-100 μm. The emission spectra of the Eu3+-doped 30TeO2-40B2O3-30MgO ceramic consists of intense and sharp lines ranging from 550-725 nm. The luminescence spectra showed that the emission intensity of 30TeO2-40B2O3-30MgO doped with Eu3+ was enhanced with the increase of Eu3+ ion from 0.2 to 1.5 mol%, which resulted in enhancement of the red emission of the samples. The longest decay time for 30TeO2-40B2O3-30MgO doped with 1.5 mol % Eu3+ was 0.892 ms. Universiti Kebangsaan Malaysia 2015-09 Article PeerReviewed application/pdf en http://journalarticle.ukm.my/9272/1/19_Nur_zu_Ira_Bohari.pdf Nur Zu Ira Bohari, and R. Hussin, and Zuhairi Ibrahim, and Hendrik O. Lintang, (2015) Photoluminescence characteristic of magnesium Boro-Tellurite doped Eu3+ Ceramic. Sains Malaysiana, 44 (9). pp. 1357-1362. ISSN 0126-6039 http://www.ukm.my/jsm/malay_journals/jilid44bil9_2015/KandunganJilid44Bil9_2015.html |
| spellingShingle | Nur Zu Ira Bohari, R. Hussin, Zuhairi Ibrahim, Hendrik O. Lintang, Photoluminescence characteristic of magnesium Boro-Tellurite doped Eu3+ Ceramic |
| title | Photoluminescence characteristic of magnesium
Boro-Tellurite doped Eu3+ Ceramic |
| title_full | Photoluminescence characteristic of magnesium
Boro-Tellurite doped Eu3+ Ceramic |
| title_fullStr | Photoluminescence characteristic of magnesium
Boro-Tellurite doped Eu3+ Ceramic |
| title_full_unstemmed | Photoluminescence characteristic of magnesium
Boro-Tellurite doped Eu3+ Ceramic |
| title_short | Photoluminescence characteristic of magnesium
Boro-Tellurite doped Eu3+ Ceramic |
| title_sort | photoluminescence characteristic of magnesium
boro-tellurite doped eu3+ ceramic |
| url | http://journalarticle.ukm.my/9272/ http://journalarticle.ukm.my/9272/ http://journalarticle.ukm.my/9272/1/19_Nur_zu_Ira_Bohari.pdf |