Effect of the poly l-lactic acid coating on the corrosion of Magnesium in Hank’s solution
To control the corrosion rate, the Magnesium (Mg) was coated with poly (l-lactic acid) (PLLA) using electrospinning technique. The effectiveness of the PLLA coating on the high purity Magnesium (HP Mg) and alloy AZ91 were tested in Hank’s solution immersion test. The corrosion behaviour of Mg coated...
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Penerbit Universiti Kebangsaan Malaysia
2018
|
| Online Access: | http://journalarticle.ukm.my/11993/ http://journalarticle.ukm.my/11993/1/20%20Atikah%20Wan%20Nafi.pdf |
| _version_ | 1848812880550428672 |
|---|---|
| author | Atikah Wan Nafi, Amalina Afifi, Nor Ishida Zainal Abidin, Noor Hidayah Abdul Aziz, Katayoon Kalantari, |
| author_facet | Atikah Wan Nafi, Amalina Afifi, Nor Ishida Zainal Abidin, Noor Hidayah Abdul Aziz, Katayoon Kalantari, |
| author_sort | Atikah Wan Nafi, |
| building | UKM Institutional Repository |
| collection | Online Access |
| description | To control the corrosion rate, the Magnesium (Mg) was coated with poly (l-lactic acid) (PLLA) using electrospinning technique. The effectiveness of the PLLA coating on the high purity Magnesium (HP Mg) and alloy AZ91 were tested in Hank’s solution immersion test. The corrosion behaviour of Mg coated PLLA was studied through hydrogen evolution, weight loss and scanning electron microscope (SEM) before, during and after samples were immersed. The solution was maintained at pH 7 by bubbling CO2 gas. The results showed that surface treatment on Mg by coating with PLLA had reduced the rate of corrosion during the immersion test. The PLLA coating was also characterized and the coating adhesion was evaluated. |
| first_indexed | 2025-11-15T00:09:19Z |
| format | Article |
| id | oai:generic.eprints.org:11993 |
| institution | Universiti Kebangasaan Malaysia |
| institution_category | Local University |
| language | English |
| last_indexed | 2025-11-15T00:09:19Z |
| publishDate | 2018 |
| publisher | Penerbit Universiti Kebangsaan Malaysia |
| recordtype | eprints |
| repository_type | Digital Repository |
| spelling | oai:generic.eprints.org:119932018-08-17T09:05:05Z http://journalarticle.ukm.my/11993/ Effect of the poly l-lactic acid coating on the corrosion of Magnesium in Hank’s solution Atikah Wan Nafi, Amalina Afifi, Nor Ishida Zainal Abidin, Noor Hidayah Abdul Aziz, Katayoon Kalantari, To control the corrosion rate, the Magnesium (Mg) was coated with poly (l-lactic acid) (PLLA) using electrospinning technique. The effectiveness of the PLLA coating on the high purity Magnesium (HP Mg) and alloy AZ91 were tested in Hank’s solution immersion test. The corrosion behaviour of Mg coated PLLA was studied through hydrogen evolution, weight loss and scanning electron microscope (SEM) before, during and after samples were immersed. The solution was maintained at pH 7 by bubbling CO2 gas. The results showed that surface treatment on Mg by coating with PLLA had reduced the rate of corrosion during the immersion test. The PLLA coating was also characterized and the coating adhesion was evaluated. Penerbit Universiti Kebangsaan Malaysia 2018-01 Article PeerReviewed application/pdf en http://journalarticle.ukm.my/11993/1/20%20Atikah%20Wan%20Nafi.pdf Atikah Wan Nafi, and Amalina Afifi, and Nor Ishida Zainal Abidin, and Noor Hidayah Abdul Aziz, and Katayoon Kalantari, (2018) Effect of the poly l-lactic acid coating on the corrosion of Magnesium in Hank’s solution. Sains Malaysiana, 47 (1). pp. 169-179. ISSN 0126-6039 http://www.ukm.my/jsm/english_journals/vol47num1_2018/contentsVol47num1_2018.html |
| spellingShingle | Atikah Wan Nafi, Amalina Afifi, Nor Ishida Zainal Abidin, Noor Hidayah Abdul Aziz, Katayoon Kalantari, Effect of the poly l-lactic acid coating on the corrosion of Magnesium in Hank’s solution |
| title | Effect of the poly l-lactic acid coating on the corrosion of Magnesium in Hank’s solution |
| title_full | Effect of the poly l-lactic acid coating on the corrosion of Magnesium in Hank’s solution |
| title_fullStr | Effect of the poly l-lactic acid coating on the corrosion of Magnesium in Hank’s solution |
| title_full_unstemmed | Effect of the poly l-lactic acid coating on the corrosion of Magnesium in Hank’s solution |
| title_short | Effect of the poly l-lactic acid coating on the corrosion of Magnesium in Hank’s solution |
| title_sort | effect of the poly l-lactic acid coating on the corrosion of magnesium in hank’s solution |
| url | http://journalarticle.ukm.my/11993/ http://journalarticle.ukm.my/11993/ http://journalarticle.ukm.my/11993/1/20%20Atikah%20Wan%20Nafi.pdf |