Non-interpenetrated metal-organic frameworks based on copper(II) paddlewheel and oligoparaxylene-isophthalate linkers: synthesis, structure and gas adsorption
Two metal–organic framework materials, MFM-130 and MFM-131 (MFM = Manchester Framework Material), have been synthesized using two oligoparaxylene (OPX) tetracarboxylate linkers containing four and five aromatic rings, respectively. Both fof-type non-interpenetrated networks contain Kagomé lattice la...
| Main Authors: | , , , , , , , , , |
|---|---|
| Format: | Article |
| Published: |
American Chemical Society
2016
|
| Subjects: | |
| Online Access: | https://eprints.nottingham.ac.uk/32412/ |
| _version_ | 1848794401488240640 |
|---|---|
| author | Yan, Yong Juricek, Michal Coudert, Francois-Xavier Vermeulan, Nicolaas A. Grunder, Sergio Dailly, Anne Lewis, William Blake, Alexander J. Stoddart, J. Fraser Schröder, Martin |
| author_facet | Yan, Yong Juricek, Michal Coudert, Francois-Xavier Vermeulan, Nicolaas A. Grunder, Sergio Dailly, Anne Lewis, William Blake, Alexander J. Stoddart, J. Fraser Schröder, Martin |
| author_sort | Yan, Yong |
| building | Nottingham Research Data Repository |
| collection | Online Access |
| description | Two metal–organic framework materials, MFM-130 and MFM-131 (MFM = Manchester Framework Material), have been synthesized using two oligoparaxylene (OPX) tetracarboxylate linkers containing four and five aromatic rings, respectively. Both fof-type non-interpenetrated networks contain Kagomé lattice layers comprising [Cu2(COO)4] paddlewheel units and isophthalates, which are pillared by the OPX linkers. Desolvated MFM-130, MFM-130a, shows permanent porosity (BET surface area of 2173 m2/g, pore volume of 1.0 cm3/g), high H2 storage capacity at 77 K (5.3 wt% at 20 bar and 2.2 wt% at 1 bar), and a higher CH4 adsorption uptake (163 cm3(STP)/cm3 (35 bar and 298 K)) compared with its structural analogue, NOTT-103. MFM-130a also shows impressive selective adsorption of C2H2, C2H4, and C2H6 over CH4 at room temperature, indicating its potential for separation of C2 hydrocarbons from CH4. The single-crystal structure of MFM-131 confirms that the methyl substituents of the paraxylene units block the windows in the Kagomé lattice layer of the framework, effectively inhibiting network interpenetration in MFM-131. This situation is to be contrasted with that of the doubly interpenetrated oligophenylene analogue, NOTT-104. Calculation of the mechanical properties of these two MOFs confirms and explains the instability of MFM-131 upon desolvation in contrast to the behavior of MFM-130. The incorporation of paraxylene units, therefore, provides an efficient method for preventing network interpenetration as well as accessing new functional materials with modified and selective sorption properties for gas substrates. |
| first_indexed | 2025-11-14T19:15:36Z |
| format | Article |
| id | nottingham-32412 |
| institution | University of Nottingham Malaysia Campus |
| institution_category | Local University |
| last_indexed | 2025-11-14T19:15:36Z |
| publishDate | 2016 |
| publisher | American Chemical Society |
| recordtype | eprints |
| repository_type | Digital Repository |
| spelling | nottingham-324122020-05-04T17:34:44Z https://eprints.nottingham.ac.uk/32412/ Non-interpenetrated metal-organic frameworks based on copper(II) paddlewheel and oligoparaxylene-isophthalate linkers: synthesis, structure and gas adsorption Yan, Yong Juricek, Michal Coudert, Francois-Xavier Vermeulan, Nicolaas A. Grunder, Sergio Dailly, Anne Lewis, William Blake, Alexander J. Stoddart, J. Fraser Schröder, Martin Two metal–organic framework materials, MFM-130 and MFM-131 (MFM = Manchester Framework Material), have been synthesized using two oligoparaxylene (OPX) tetracarboxylate linkers containing four and five aromatic rings, respectively. Both fof-type non-interpenetrated networks contain Kagomé lattice layers comprising [Cu2(COO)4] paddlewheel units and isophthalates, which are pillared by the OPX linkers. Desolvated MFM-130, MFM-130a, shows permanent porosity (BET surface area of 2173 m2/g, pore volume of 1.0 cm3/g), high H2 storage capacity at 77 K (5.3 wt% at 20 bar and 2.2 wt% at 1 bar), and a higher CH4 adsorption uptake (163 cm3(STP)/cm3 (35 bar and 298 K)) compared with its structural analogue, NOTT-103. MFM-130a also shows impressive selective adsorption of C2H2, C2H4, and C2H6 over CH4 at room temperature, indicating its potential for separation of C2 hydrocarbons from CH4. The single-crystal structure of MFM-131 confirms that the methyl substituents of the paraxylene units block the windows in the Kagomé lattice layer of the framework, effectively inhibiting network interpenetration in MFM-131. This situation is to be contrasted with that of the doubly interpenetrated oligophenylene analogue, NOTT-104. Calculation of the mechanical properties of these two MOFs confirms and explains the instability of MFM-131 upon desolvation in contrast to the behavior of MFM-130. The incorporation of paraxylene units, therefore, provides an efficient method for preventing network interpenetration as well as accessing new functional materials with modified and selective sorption properties for gas substrates. American Chemical Society 2016-03-01 Article PeerReviewed Yan, Yong, Juricek, Michal, Coudert, Francois-Xavier, Vermeulan, Nicolaas A., Grunder, Sergio, Dailly, Anne, Lewis, William, Blake, Alexander J., Stoddart, J. Fraser and Schröder, Martin (2016) Non-interpenetrated metal-organic frameworks based on copper(II) paddlewheel and oligoparaxylene-isophthalate linkers: synthesis, structure and gas adsorption. Journal of the American Chemical Society, 138 (10). pp. 3371-3381. ISSN 1520-5126 metal-organic framework Shear modulus copper methane hydrogen hydrocarbon gas storage http://pubs.acs.org/doi/abs/10.1021/jacs.5b12312 doi:10.1021/jacs.5b12312 doi:10.1021/jacs.5b12312 |
| spellingShingle | metal-organic framework Shear modulus copper methane hydrogen hydrocarbon gas storage Yan, Yong Juricek, Michal Coudert, Francois-Xavier Vermeulan, Nicolaas A. Grunder, Sergio Dailly, Anne Lewis, William Blake, Alexander J. Stoddart, J. Fraser Schröder, Martin Non-interpenetrated metal-organic frameworks based on copper(II) paddlewheel and oligoparaxylene-isophthalate linkers: synthesis, structure and gas adsorption |
| title | Non-interpenetrated metal-organic frameworks based on copper(II) paddlewheel and oligoparaxylene-isophthalate linkers: synthesis, structure and gas adsorption |
| title_full | Non-interpenetrated metal-organic frameworks based on copper(II) paddlewheel and oligoparaxylene-isophthalate linkers: synthesis, structure and gas adsorption |
| title_fullStr | Non-interpenetrated metal-organic frameworks based on copper(II) paddlewheel and oligoparaxylene-isophthalate linkers: synthesis, structure and gas adsorption |
| title_full_unstemmed | Non-interpenetrated metal-organic frameworks based on copper(II) paddlewheel and oligoparaxylene-isophthalate linkers: synthesis, structure and gas adsorption |
| title_short | Non-interpenetrated metal-organic frameworks based on copper(II) paddlewheel and oligoparaxylene-isophthalate linkers: synthesis, structure and gas adsorption |
| title_sort | non-interpenetrated metal-organic frameworks based on copper(ii) paddlewheel and oligoparaxylene-isophthalate linkers: synthesis, structure and gas adsorption |
| topic | metal-organic framework Shear modulus copper methane hydrogen hydrocarbon gas storage |
| url | https://eprints.nottingham.ac.uk/32412/ https://eprints.nottingham.ac.uk/32412/ https://eprints.nottingham.ac.uk/32412/ |