Effects of sintering time and temperature to the characteristics of FeCrAl powder compacts formed at elevated temperature
This paper presents the outcomes of an experimental investigation on the effect of sintering schedule, i.e., holding time and temperature to the final properties of FeCrAl powder compacts prepared through uniaxial die compaction process at above room temperature. The feedstock was prepared by mec...
| Main Authors: | , , , |
|---|---|
| Format: | Proceeding Paper |
| Language: | English English English |
| Published: |
American Scientific Publishers
2018
|
| Subjects: | |
| Online Access: | http://irep.iium.edu.my/64419/ http://irep.iium.edu.my/64419/1/64419_Effects%20of%20sintering%20time%20and%20temperature%20to%20the%20characteristics_conference%20article.pdf http://irep.iium.edu.my/64419/2/64419_Effects%20of%20sintering%20time%20and%20temperature%20to%20the%20characteristics_scopus.pdf http://irep.iium.edu.my/64419/13/64419_Effects%20of%20sintering%20time%20and%20temperature%20to%20the%20characteristics%20of%20FeCrAl%20powder_WoS.pdf |
| _version_ | 1848786214632554496 |
|---|---|
| author | Rahman, Md Mujibur Rahman, Haolia Y. Awang, M. A.A. Sopyan, Lis |
| author_facet | Rahman, Md Mujibur Rahman, Haolia Y. Awang, M. A.A. Sopyan, Lis |
| author_sort | Rahman, Md Mujibur |
| building | IIUM Repository |
| collection | Online Access |
| description | This paper presents the outcomes of an experimental investigation on the effect of
sintering schedule, i.e., holding time and temperature to the final properties of FeCrAl powder
compacts prepared through uniaxial die compaction process at above room temperature. The
feedstock was prepared by mechanically mixing iron powder ASC 100.29 with chromium (22
wt%) and aluminium (11 wt%) for 30 min at room temperature. A cylindrical shape die was
filled with the powder mass and heated for one hour for uniform heating of the die assembly
together with the powder mass. Once the temperature reached to the setup temperature, i.e.,
150ºC, the powder mass was formed by applying an axial pressure of 425 MPa simultaneously
from upward and downward directions. The as-pressed green compacts were then cooled to
room temperature and subsequently sintered in argon gas fired furnace at a rate of 5ºC/min for
three different holding times, i.e., 30, 60, and 90 min at three different sintering temperatures,
i.e., 800, 900, and 1000ºC. The sintered samples were characterized for their density, electrical
resistivity, bending strength, and microstructure. The results revealed that the sample sintered
at 1000ºC for 90 min achieved the better characteristics. |
| first_indexed | 2025-11-14T17:05:29Z |
| format | Proceeding Paper |
| id | iium-64419 |
| institution | International Islamic University Malaysia |
| institution_category | Local University |
| language | English English English |
| last_indexed | 2025-11-14T17:05:29Z |
| publishDate | 2018 |
| publisher | American Scientific Publishers |
| recordtype | eprints |
| repository_type | Digital Repository |
| spelling | iium-644192018-08-02T08:44:25Z http://irep.iium.edu.my/64419/ Effects of sintering time and temperature to the characteristics of FeCrAl powder compacts formed at elevated temperature Rahman, Md Mujibur Rahman, Haolia Y. Awang, M. A.A. Sopyan, Lis TA Engineering (General). Civil engineering (General) TA170 Environmental engineering. Sustainable engineering TS Manufactures This paper presents the outcomes of an experimental investigation on the effect of sintering schedule, i.e., holding time and temperature to the final properties of FeCrAl powder compacts prepared through uniaxial die compaction process at above room temperature. The feedstock was prepared by mechanically mixing iron powder ASC 100.29 with chromium (22 wt%) and aluminium (11 wt%) for 30 min at room temperature. A cylindrical shape die was filled with the powder mass and heated for one hour for uniform heating of the die assembly together with the powder mass. Once the temperature reached to the setup temperature, i.e., 150ºC, the powder mass was formed by applying an axial pressure of 425 MPa simultaneously from upward and downward directions. The as-pressed green compacts were then cooled to room temperature and subsequently sintered in argon gas fired furnace at a rate of 5ºC/min for three different holding times, i.e., 30, 60, and 90 min at three different sintering temperatures, i.e., 800, 900, and 1000ºC. The sintered samples were characterized for their density, electrical resistivity, bending strength, and microstructure. The results revealed that the sample sintered at 1000ºC for 90 min achieved the better characteristics. American Scientific Publishers 2018 Proceeding Paper PeerReviewed application/pdf en http://irep.iium.edu.my/64419/1/64419_Effects%20of%20sintering%20time%20and%20temperature%20to%20the%20characteristics_conference%20article.pdf application/pdf en http://irep.iium.edu.my/64419/2/64419_Effects%20of%20sintering%20time%20and%20temperature%20to%20the%20characteristics_scopus.pdf application/pdf en http://irep.iium.edu.my/64419/13/64419_Effects%20of%20sintering%20time%20and%20temperature%20to%20the%20characteristics%20of%20FeCrAl%20powder_WoS.pdf Rahman, Md Mujibur and Rahman, Haolia Y. and Awang, M. A.A. and Sopyan, Lis (2018) Effects of sintering time and temperature to the characteristics of FeCrAl powder compacts formed at elevated temperature. In: "International Conference on Advances in Manufacturing and Materials Engineering 2017, ICAMME 2017", 8-9 August 2017, International Islamic University Malaysia (IIUM), Gombak Campus, Kuala Lumpur. http://iopscience.iop.org/article/10.1088/1757-899X/290/1/012009/meta 10.1088/1757-899X/290/1/012009 |
| spellingShingle | TA Engineering (General). Civil engineering (General) TA170 Environmental engineering. Sustainable engineering TS Manufactures Rahman, Md Mujibur Rahman, Haolia Y. Awang, M. A.A. Sopyan, Lis Effects of sintering time and temperature to the characteristics of FeCrAl powder compacts formed at elevated temperature |
| title | Effects of sintering time and temperature to the characteristics of FeCrAl powder compacts formed at elevated temperature |
| title_full | Effects of sintering time and temperature to the characteristics of FeCrAl powder compacts formed at elevated temperature |
| title_fullStr | Effects of sintering time and temperature to the characteristics of FeCrAl powder compacts formed at elevated temperature |
| title_full_unstemmed | Effects of sintering time and temperature to the characteristics of FeCrAl powder compacts formed at elevated temperature |
| title_short | Effects of sintering time and temperature to the characteristics of FeCrAl powder compacts formed at elevated temperature |
| title_sort | effects of sintering time and temperature to the characteristics of fecral powder compacts formed at elevated temperature |
| topic | TA Engineering (General). Civil engineering (General) TA170 Environmental engineering. Sustainable engineering TS Manufactures |
| url | http://irep.iium.edu.my/64419/ http://irep.iium.edu.my/64419/ http://irep.iium.edu.my/64419/ http://irep.iium.edu.my/64419/1/64419_Effects%20of%20sintering%20time%20and%20temperature%20to%20the%20characteristics_conference%20article.pdf http://irep.iium.edu.my/64419/2/64419_Effects%20of%20sintering%20time%20and%20temperature%20to%20the%20characteristics_scopus.pdf http://irep.iium.edu.my/64419/13/64419_Effects%20of%20sintering%20time%20and%20temperature%20to%20the%20characteristics%20of%20FeCrAl%20powder_WoS.pdf |