The effect of incorporating lithium fluoride on the compressive strength and diametric tensile strength of glass ionomer cement
Experimental glass ionomer cement was prepared for the purpose of this study. Twenty disk specimens (16mm diameter x 10mm height) of test-GIC were prepared for the diametral tensile strength (DTS) test and twenty cylindrical specimens (6 mm diameter x 16mm height) were prepared for the compressive s...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English English |
| Published: |
Trans Tech Publications Ltd., Switzerland
2011
|
| Subjects: | |
| Online Access: | http://irep.iium.edu.my/5642/ http://irep.iium.edu.my/5642/1/The_Effect_of_Incorporating_Lithium_Fluoride_on_the_Compressive_Strength_and_Diametric_Tensile_Strength_of_Glass_Ionomer_Cement.pdf http://irep.iium.edu.my/5642/4/The_Effect_of_Incorporating_Lithium_Fluoride.pdf |
| _version_ | 1848776540376006656 |
|---|---|
| author | Mustafa, Ammar A. Al-Khateeb, Khalid A. Saeed Ismail, Ahmad Faris |
| author_facet | Mustafa, Ammar A. Al-Khateeb, Khalid A. Saeed Ismail, Ahmad Faris |
| author_sort | Mustafa, Ammar A. |
| building | IIUM Repository |
| collection | Online Access |
| description | Experimental glass ionomer cement was prepared for the purpose of this study. Twenty disk specimens (16mm diameter x 10mm height) of test-GIC were prepared for the diametral tensile strength (DTS) test and twenty cylindrical specimens (6 mm diameter x 16mm height) were prepared for the compressive strength (CS) test. Specimens were stored in an artificial saliva at 37º C and (50±10%) of relative humidity in an incubator until testing. Five specimens of each GIC were submitted to CS and DTS test in each period, namely 1 hour, 24 hours, 7 days and 28 days. The specimens were tested in a Universal Testing Machine (Instron 1122, Instron corp., High Wycombe, U.K.) at a crosshead speed of 1.0mm/min for CS and 0.5mm/min for the DTS test until failure occurred. The results have revealed that incorporation of lithium fluoride in the formula of the test GIC might impart an increase in the mechanical properties of the GICs |
| first_indexed | 2025-11-14T14:31:43Z |
| format | Article |
| id | iium-5642 |
| institution | International Islamic University Malaysia |
| institution_category | Local University |
| language | English English |
| last_indexed | 2025-11-14T14:31:43Z |
| publishDate | 2011 |
| publisher | Trans Tech Publications Ltd., Switzerland |
| recordtype | eprints |
| repository_type | Digital Repository |
| spelling | iium-56422020-06-30T07:01:15Z http://irep.iium.edu.my/5642/ The effect of incorporating lithium fluoride on the compressive strength and diametric tensile strength of glass ionomer cement Mustafa, Ammar A. Al-Khateeb, Khalid A. Saeed Ismail, Ahmad Faris RK Dentistry TP248.13 Biotechnology Experimental glass ionomer cement was prepared for the purpose of this study. Twenty disk specimens (16mm diameter x 10mm height) of test-GIC were prepared for the diametral tensile strength (DTS) test and twenty cylindrical specimens (6 mm diameter x 16mm height) were prepared for the compressive strength (CS) test. Specimens were stored in an artificial saliva at 37º C and (50±10%) of relative humidity in an incubator until testing. Five specimens of each GIC were submitted to CS and DTS test in each period, namely 1 hour, 24 hours, 7 days and 28 days. The specimens were tested in a Universal Testing Machine (Instron 1122, Instron corp., High Wycombe, U.K.) at a crosshead speed of 1.0mm/min for CS and 0.5mm/min for the DTS test until failure occurred. The results have revealed that incorporation of lithium fluoride in the formula of the test GIC might impart an increase in the mechanical properties of the GICs Trans Tech Publications Ltd., Switzerland 2011-06 Article PeerReviewed application/pdf en http://irep.iium.edu.my/5642/1/The_Effect_of_Incorporating_Lithium_Fluoride_on_the_Compressive_Strength_and_Diametric_Tensile_Strength_of_Glass_Ionomer_Cement.pdf application/pdf en http://irep.iium.edu.my/5642/4/The_Effect_of_Incorporating_Lithium_Fluoride.pdf Mustafa, Ammar A. and Al-Khateeb, Khalid A. Saeed and Ismail, Ahmad Faris (2011) The effect of incorporating lithium fluoride on the compressive strength and diametric tensile strength of glass ionomer cement. Advanced Materials Research, 264. pp. 508-512. ISSN 1662-8985 http://www.scientific.net/AMR.264-265.508 10.4028/www.scientific.net/AMR.264-265.508 |
| spellingShingle | RK Dentistry TP248.13 Biotechnology Mustafa, Ammar A. Al-Khateeb, Khalid A. Saeed Ismail, Ahmad Faris The effect of incorporating lithium fluoride on the compressive strength and diametric tensile strength of glass ionomer cement |
| title | The effect of incorporating lithium fluoride on the compressive strength and diametric tensile strength of glass ionomer cement |
| title_full | The effect of incorporating lithium fluoride on the compressive strength and diametric tensile strength of glass ionomer cement |
| title_fullStr | The effect of incorporating lithium fluoride on the compressive strength and diametric tensile strength of glass ionomer cement |
| title_full_unstemmed | The effect of incorporating lithium fluoride on the compressive strength and diametric tensile strength of glass ionomer cement |
| title_short | The effect of incorporating lithium fluoride on the compressive strength and diametric tensile strength of glass ionomer cement |
| title_sort | effect of incorporating lithium fluoride on the compressive strength and diametric tensile strength of glass ionomer cement |
| topic | RK Dentistry TP248.13 Biotechnology |
| url | http://irep.iium.edu.my/5642/ http://irep.iium.edu.my/5642/ http://irep.iium.edu.my/5642/ http://irep.iium.edu.my/5642/1/The_Effect_of_Incorporating_Lithium_Fluoride_on_the_Compressive_Strength_and_Diametric_Tensile_Strength_of_Glass_Ionomer_Cement.pdf http://irep.iium.edu.my/5642/4/The_Effect_of_Incorporating_Lithium_Fluoride.pdf |