The influence of ageing on the impact damage of carbon epoxy composites
This study looks into the influence of ageing on the carbon epoxy composite when impact is applied. Three different stacking sequences were investigated, one sequence with the classic lay-up, whereas the other two have quasiisotropic and quasi-homogeneous behaviour. The specimens were aged up to 2...
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English English |
| Published: |
Elsevier
2011
|
| Subjects: | |
| Online Access: | http://irep.iium.edu.my/4220/ http://irep.iium.edu.my/4220/1/the_influence_of_ageing_on_the_impact_damage_of_carbon_epoxy_composite.pdf http://irep.iium.edu.my/4220/4/The_Influence_of_Ageing_on_the_Impact_Damage_of_Carbon.pdf |
| _version_ | 1848776293569527808 |
|---|---|
| author | Mokhtar, Hanan Sicot, Olivier Rousseau, Jérôme Aminanda, Yulfian Aivazzadeh, Shahram |
| author_facet | Mokhtar, Hanan Sicot, Olivier Rousseau, Jérôme Aminanda, Yulfian Aivazzadeh, Shahram |
| author_sort | Mokhtar, Hanan |
| building | IIUM Repository |
| collection | Online Access |
| description | This study looks into the influence of ageing on the carbon epoxy composite when impact is applied. Three different
stacking sequences were investigated, one sequence with the classic lay-up, whereas the other two have quasiisotropic
and quasi-homogeneous behaviour. The specimens were aged up to 2100h (3 months) in a climatic chamber with a temperature of 70°C and relative humidity of 85%. The mass was measured regularly during the hygrothermal ageing treatment. The mass was always measured directly after exiting the climatic chamber and it was noted that for each stacking sequence, the same regular increase in mass is observed until stabilisation. The specimens were then impacted and the damage was evaluated via ultrasonic analysis (C-scan). The damage due to impact was not greatly influenced by ageing, but influences the morphology of the damage in the composite |
| first_indexed | 2025-11-14T14:27:47Z |
| format | Article |
| id | iium-4220 |
| institution | International Islamic University Malaysia |
| institution_category | Local University |
| language | English English |
| last_indexed | 2025-11-14T14:27:47Z |
| publishDate | 2011 |
| publisher | Elsevier |
| recordtype | eprints |
| repository_type | Digital Repository |
| spelling | iium-42202012-04-25T03:51:51Z http://irep.iium.edu.my/4220/ The influence of ageing on the impact damage of carbon epoxy composites Mokhtar, Hanan Sicot, Olivier Rousseau, Jérôme Aminanda, Yulfian Aivazzadeh, Shahram TJ Mechanical engineering and machinery This study looks into the influence of ageing on the carbon epoxy composite when impact is applied. Three different stacking sequences were investigated, one sequence with the classic lay-up, whereas the other two have quasiisotropic and quasi-homogeneous behaviour. The specimens were aged up to 2100h (3 months) in a climatic chamber with a temperature of 70°C and relative humidity of 85%. The mass was measured regularly during the hygrothermal ageing treatment. The mass was always measured directly after exiting the climatic chamber and it was noted that for each stacking sequence, the same regular increase in mass is observed until stabilisation. The specimens were then impacted and the damage was evaluated via ultrasonic analysis (C-scan). The damage due to impact was not greatly influenced by ageing, but influences the morphology of the damage in the composite Elsevier 2011 Article PeerReviewed application/pdf en http://irep.iium.edu.my/4220/1/the_influence_of_ageing_on_the_impact_damage_of_carbon_epoxy_composite.pdf application/pdf en http://irep.iium.edu.my/4220/4/The_Influence_of_Ageing_on_the_Impact_Damage_of_Carbon.pdf Mokhtar, Hanan and Sicot, Olivier and Rousseau, Jérôme and Aminanda, Yulfian and Aivazzadeh, Shahram (2011) The influence of ageing on the impact damage of carbon epoxy composites. Procedia Engineering, 10. pp. 2615-2620. ISSN 1877-7058 http://www.sciencedirect.com/science/article/pii/S1877705811006242 10.1016/j.proeng.2011.04.436 |
| spellingShingle | TJ Mechanical engineering and machinery Mokhtar, Hanan Sicot, Olivier Rousseau, Jérôme Aminanda, Yulfian Aivazzadeh, Shahram The influence of ageing on the impact damage of carbon epoxy composites |
| title | The influence of ageing on the impact damage of carbon epoxy composites |
| title_full | The influence of ageing on the impact damage of carbon epoxy composites |
| title_fullStr | The influence of ageing on the impact damage of carbon epoxy composites |
| title_full_unstemmed | The influence of ageing on the impact damage of carbon epoxy composites |
| title_short | The influence of ageing on the impact damage of carbon epoxy composites |
| title_sort | influence of ageing on the impact damage of carbon epoxy composites |
| topic | TJ Mechanical engineering and machinery |
| url | http://irep.iium.edu.my/4220/ http://irep.iium.edu.my/4220/ http://irep.iium.edu.my/4220/ http://irep.iium.edu.my/4220/1/the_influence_of_ageing_on_the_impact_damage_of_carbon_epoxy_composite.pdf http://irep.iium.edu.my/4220/4/The_Influence_of_Ageing_on_the_Impact_Damage_of_Carbon.pdf |