The effects of water vapor on high temperature oxidation of Fe-Cr-Ni alloy at 1073k
Void formation in oxide scale during high temperature oxidation is a common phenomenon. Over a long period of time voids will affect the mechanical property of scales by influencing the cracking and spalling. Voids formed in dry environment are different than that of formed in humid environment. Wit...
| Main Authors: | , |
|---|---|
| Format: | Monograph |
| Language: | English |
| Published: |
s.n.
2012
|
| Subjects: | |
| Online Access: | http://irep.iium.edu.my/32502/ http://irep.iium.edu.my/32502/1/EDW-B0906-333..pdf |
| _version_ | 1848780573097590784 |
|---|---|
| author | Ani, Mohd Hanafi Othman, Raihan |
| author_facet | Ani, Mohd Hanafi Othman, Raihan |
| author_sort | Ani, Mohd Hanafi |
| building | IIUM Repository |
| collection | Online Access |
| description | Void formation in oxide scale during high temperature oxidation is a common phenomenon. Over a long period of time voids will affect the mechanical property of scales by influencing the cracking and spalling. Voids formed in dry environment are different than that of formed in humid environment. With the presence of water vapor in humid environment the formation of void will increase, thus greater number of void compared to that in dry environment |
| first_indexed | 2025-11-14T15:35:49Z |
| format | Monograph |
| id | iium-32502 |
| institution | International Islamic University Malaysia |
| institution_category | Local University |
| language | English |
| last_indexed | 2025-11-14T15:35:49Z |
| publishDate | 2012 |
| publisher | s.n. |
| recordtype | eprints |
| repository_type | Digital Repository |
| spelling | iium-325022015-05-18T02:01:25Z http://irep.iium.edu.my/32502/ The effects of water vapor on high temperature oxidation of Fe-Cr-Ni alloy at 1073k Ani, Mohd Hanafi Othman, Raihan TA Engineering (General). Civil engineering (General) TK Electrical engineering. Electronics Nuclear engineering Void formation in oxide scale during high temperature oxidation is a common phenomenon. Over a long period of time voids will affect the mechanical property of scales by influencing the cracking and spalling. Voids formed in dry environment are different than that of formed in humid environment. With the presence of water vapor in humid environment the formation of void will increase, thus greater number of void compared to that in dry environment s.n. 2012-01-04 Monograph NonPeerReviewed application/pdf en http://irep.iium.edu.my/32502/1/EDW-B0906-333..pdf Ani, Mohd Hanafi and Othman, Raihan (2012) The effects of water vapor on high temperature oxidation of Fe-Cr-Ni alloy at 1073k. Research Report. s.n., Kuala Lumpur. (Unpublished) EDW B0906-333 |
| spellingShingle | TA Engineering (General). Civil engineering (General) TK Electrical engineering. Electronics Nuclear engineering Ani, Mohd Hanafi Othman, Raihan The effects of water vapor on high temperature oxidation of Fe-Cr-Ni alloy at 1073k |
| title | The effects of water vapor on high temperature oxidation of Fe-Cr-Ni alloy at 1073k |
| title_full | The effects of water vapor on high temperature oxidation of Fe-Cr-Ni alloy at 1073k |
| title_fullStr | The effects of water vapor on high temperature oxidation of Fe-Cr-Ni alloy at 1073k |
| title_full_unstemmed | The effects of water vapor on high temperature oxidation of Fe-Cr-Ni alloy at 1073k |
| title_short | The effects of water vapor on high temperature oxidation of Fe-Cr-Ni alloy at 1073k |
| title_sort | effects of water vapor on high temperature oxidation of fe-cr-ni alloy at 1073k |
| topic | TA Engineering (General). Civil engineering (General) TK Electrical engineering. Electronics Nuclear engineering |
| url | http://irep.iium.edu.my/32502/ http://irep.iium.edu.my/32502/ http://irep.iium.edu.my/32502/1/EDW-B0906-333..pdf |