Analysis of end crack in boiler tube

QR Code

Analysis of end crack in boiler tube

Boiler tube failures usually result in frequent forced outages, and ultimately in costly extended outages for major tubing replacement in a plant. There are several failure modes that may occur in a boiler tube, i.e. stress-corrosion cracking, pitting, water-side corrosion, fire-side corrosion, f...

Full description

Bibliographic Details
Main Authors:	Begum, Shahida, Karim, A.N. Mustafizul, Nainer, Mohamed Ansari M., Sevah, Sukhana
Format:	Article
Language:	English
Published:	Trans Tech Publications Ltd., Switzerland 2012
Subjects:	TJ Mechanical engineering and machinery
Online Access:	http://irep.iium.edu.my/26754/ http://irep.iium.edu.my/26754/1/AMR_Boiler_Crack%2325.pdf

Similar Items

Investigation on wall thinning and creep damage in boiler tube due to scale formation
by: Begum, Shahida, et al.
Published: (2012)

Wall thinning and creep damage analysis in boiler tube and optimization of operating conditions
by: Begum, Shahida, et al.
Published: (2013)

Development of iterative analytical procedure for boiler tube analysis in matlab
by: Ang, Wei Bing
Published: (2013)

Evaluation of high temperature boiler tubed using iterative analytical approach
by: Lim, Edwin Chui Seng
Published: (2013)

Study of mitigation of superheater tube failure & maintenance of an industrial boiler / Sri Ganesh Elangkovan
by: Sri Ganesh , Elangkovan
Published: (2019)

Analysis of gauge glass failure possibility for boiler
by: Nur Farida, Ismail
Published: (2007)

The thermal performance study of biomass field-erected water tube boilers using analytical model / Sivabalan Tanapala
by: Sivabalan , Tanapala
Published: (2013)

Study the energy recovery in acrylic boiler /
by: Ummu Atirah , Hanipah
Published: (2012)

Analysis on losses and boiler efficiency to find optimum cooling water flowrate
by: Mohd Shahrulnizam, Abu Seman
Published: (2007)

Fatigue Crack Growth Analysis of Semielliptical Surface Crack
by: M. R. M., Akramin, et al.
Published: (2014)

Thermal analysis of the steam boiler for the sterilization plant at Pepper Marketing Board (PMB) Kuching
by: Junaidi, E.
Published: (1999)

Modelling of crack propagation for embedded crack structure
by: H. A., Haziq A., et al.
Published: (2020)

Tool wear and surface roughness aspects in heat assisted end milling of AISI D2 hardened steel
by: Amin, A. K. M. Nurul, et al.
Published: (2011)

Prediction of tool life in end milling of hardened steel AISI D2
by: Lajis, M.A., et al.
Published: (2008)

Crack analysis using extended finite element method with virtual crack closure technique
by: Wong, Ee Fun
Published: (2016)

The effect of water-side scale formation to heat transfer process and boiler efficiency
by: Faiq Nur, Abdul Halim
Published: (2007)

Sampling model in engineering analysis software for surface cracked structure
by: Mohd Akramin, Mohd Romlay, et al.
Published: (2018)

3D analysis of creep voids in hydrogen reformer tubes
by: Wahab, A.A., et al.
Published: (2005)

Development of surface roughness prediction model using response surface methodology in high speed end milling of AISI H13 tool steel
by: Hafiz, A. K. M., et al.
Published: (2007)

Analysis and prediction of surface crack growth under fatigue loading
by: Mohd Akramin, Mohd Romlay, et al.
Published: (2025)

Improved tool life in end milling Ti-6Al-4V through workpiece preheating
by: Turnad, L. Ginta, et al.
Published: (2009)

Improved tool life in end milling Ti-6A1-4V through workpiece preheating
by: Ginta, Turnad Lenggo, et al.
Published: (2009)

Elicitation of conditional probability table (CPT) for risk analysis of biomass boiler in energy plant
by: Ahmad Nur Fikry, Zainuddin, et al.
Published: (2022)

Simulation and Fabrication of Open-Type Boiler of Fish Cracker Production Line
by: Mohd Zaidi, Sidek, et al.
Published: (2015)

Preheated machining in end milling of hardened steel AISI D2
by: Lajis, M. A., et al.
Published: (2008)

Crack tip stress intensity factors for a crack emanating from a sharp notch
by: S., Karuppanan, et al.
Published: (2008)

Thermal and Fluid Dynamic Analysis of Compact Fin-and-Tube Heat Exchangers for Automotive Applications
by: Adam, A. Y., et al.
Published: (2018)

3D Analysis of Creep Void Formation in Steam-Methane Reformer Tubes
by: Wahab, A.A.
Published: (2007)

Hybrid Finite Element And Monte Carlo Analysis Of Cracked Pipe
by: Mohd Akramin, Mohd Romlay, et al.
Published: (2010)

Finite element analysis of bending tests for fatigue cracking assessment
by: Muhamad Husnain, Mohd Noh, et al.
Published: (2025)

Fatigue crack growth analysis using Bootstrap S‑version finite element model
by: M. R. M., Akramin, et al.
Published: (2020)

Crack tip stress intensity factors for a crack emanating from a semi-infinite notch with application to the avoidance of fatigue in complete contacts
by: S., Karuppanan, et al.
Published: (2009)

Development And Characterization Of Biomass Steam Boiler For Externally Fired Micro Gas Turbine (EFMGT) System
by: Azman, Amirul Azim
Published: (2018)

Effect of tube inclination angle on the thermal and fluid dynamic performance of flat tube heat exchanger
by: Ahmed Yousif Adam, Mohammed
Published: (2017)

Construction of a crack growth testing apparatus associated with stress corrosion cracking (SCC) study
by: Peter Anderson, anak Joseph
Published: (2005)

Design and fabrication of an improved crack growth testing apparatus with stress corrosion cracking (SCC) study
by: Ibrahim Manai, Abdul Hakim
Published: (2006)

Prediction of Fatigue Crack Growth for Semi-Elliptical Surface Cracks using S-version Fem under Tension Loading
by: M. S., Shaari, et al.
Published: (2016)

Crack Analysis Using Extended Finite Element Method With Virtual Crack Closure Technique
by: Wong , Ee Fun
Published: (2016)

Fatigue crack growth mechanisms of cast Ti-48Al (at. %) alloy
by: Hamad, S., et al.
Published: (2000)

Burst pressure prediction of multiple cracks in pipelines
by: Norhaida, Ab. Razak, et al.
Published: (2013)