Crystalline TiO2 protective layer with graded oxygen defects for efficient and stable silicon-based photocathode
© 2018, The Author(s). The trade-offs between photoelectrode efficiency and stability significantly hinder the practical application of silicon-based photoelectrochemical devices. Here, we report a facile approach to decouple the trade-offs of silicon-based photocathodes by employing crystalline TiO...
| Main Authors: | , , , , , , |
|---|---|
| Format: | Journal Article |
| Published: |
Macmillan Publishers Limited
2018
|
| Online Access: | http://purl.org/au-research/grants/arc/DP180100568 http://hdl.handle.net/20.500.11937/71373 |
| Summary: | © 2018, The Author(s). The trade-offs between photoelectrode efficiency and stability significantly hinder the practical application of silicon-based photoelectrochemical devices. Here, we report a facile approach to decouple the trade-offs of silicon-based photocathodes by employing crystalline TiO2 with graded oxygen defects as protection layer. The crystalline protection layer provides high-density structure and enhances stability, and at the same time oxygen defects allow the carrier transport with low resistance as required for high efficiency. The silicon-based photocathode with black TiO2 shows a limiting current density of ~35.3 mA cm-2 and durability of over 100 h at 10 mA cm-2 in 1.0 M NaOH electrolyte, while none of photoelectrochemical behavior is observed in crystalline TiO2 protection layer. These findings have significant suggestions for further development of silicon-based, III–V compounds and other photoelectrodes and offer the possibility for achieving highly efficient and durable photoelectrochemical devices. |
|---|