Electrochemical investigation of the role of cl- on localized carbon dioxide corrosion behavior of mild steel
Electrochemical behavior of localized carbon dioxide (CO2) corrosion of X65 mild steel at 80°C in 0.1, 1.0, 10, and 20 wt% sodium chloride (NaCl) solutions have been investigated using electrochemical techniques including linear polarization resistance (LPR) and electrochemical impedance spectroscop...
| Main Authors: | , , , , |
|---|---|
| Format: | Journal Article |
| Published: |
NACE International
2013
|
| Online Access: | http://hdl.handle.net/20.500.11937/56418 |
| _version_ | 1848759870874976256 |
|---|---|
| author | Jiang, X. Nesic, S. Kinsella, Brian Brown, B. Young, D. |
| author_facet | Jiang, X. Nesic, S. Kinsella, Brian Brown, B. Young, D. |
| author_sort | Jiang, X. |
| building | Curtin Institutional Repository |
| collection | Online Access |
| description | Electrochemical behavior of localized carbon dioxide (CO2) corrosion of X65 mild steel at 80°C in 0.1, 1.0, 10, and 20 wt% sodium chloride (NaCl) solutions have been investigated using electrochemical techniques including linear polarization resistance (LPR) and electrochemical impedance spectroscopy (EIS). Surface morphology of specimens was observed using scanning electron microscopy (SEM). Pit depth and its corresponding 3D optical measurement were undertaken using infinite focus microscopy (IFM). The results showed that Cl- concentration had only a slight effect on general corrosion rate. It also revealed that increasing Cl- concentration did not accelerate the initiation of localized corrosion; localized corrosion rate did not change with increasing NaCl solution concentrations; and chemical dissolution of corrosion product film could initiate localized CO 2 corrosion. © 2013, NACE International. |
| first_indexed | 2025-11-14T10:06:46Z |
| format | Journal Article |
| id | curtin-20.500.11937-56418 |
| institution | Curtin University Malaysia |
| institution_category | Local University |
| last_indexed | 2025-11-14T10:06:46Z |
| publishDate | 2013 |
| publisher | NACE International |
| recordtype | eprints |
| repository_type | Digital Repository |
| spelling | curtin-20.500.11937-564182017-09-13T16:10:18Z Electrochemical investigation of the role of cl- on localized carbon dioxide corrosion behavior of mild steel Jiang, X. Nesic, S. Kinsella, Brian Brown, B. Young, D. Electrochemical behavior of localized carbon dioxide (CO2) corrosion of X65 mild steel at 80°C in 0.1, 1.0, 10, and 20 wt% sodium chloride (NaCl) solutions have been investigated using electrochemical techniques including linear polarization resistance (LPR) and electrochemical impedance spectroscopy (EIS). Surface morphology of specimens was observed using scanning electron microscopy (SEM). Pit depth and its corresponding 3D optical measurement were undertaken using infinite focus microscopy (IFM). The results showed that Cl- concentration had only a slight effect on general corrosion rate. It also revealed that increasing Cl- concentration did not accelerate the initiation of localized corrosion; localized corrosion rate did not change with increasing NaCl solution concentrations; and chemical dissolution of corrosion product film could initiate localized CO 2 corrosion. © 2013, NACE International. 2013 Journal Article http://hdl.handle.net/20.500.11937/56418 10.5006/0620 NACE International restricted |
| spellingShingle | Jiang, X. Nesic, S. Kinsella, Brian Brown, B. Young, D. Electrochemical investigation of the role of cl- on localized carbon dioxide corrosion behavior of mild steel |
| title | Electrochemical investigation of the role of cl- on localized carbon dioxide corrosion behavior of mild steel |
| title_full | Electrochemical investigation of the role of cl- on localized carbon dioxide corrosion behavior of mild steel |
| title_fullStr | Electrochemical investigation of the role of cl- on localized carbon dioxide corrosion behavior of mild steel |
| title_full_unstemmed | Electrochemical investigation of the role of cl- on localized carbon dioxide corrosion behavior of mild steel |
| title_short | Electrochemical investigation of the role of cl- on localized carbon dioxide corrosion behavior of mild steel |
| title_sort | electrochemical investigation of the role of cl- on localized carbon dioxide corrosion behavior of mild steel |
| url | http://hdl.handle.net/20.500.11937/56418 |