Decoration of TiO2 anatase nanoplates with silver nanoparticles on the {101} crystal facets and their photocatalytic behaviour
Ag nanoparticles were photodeposited on the {101} crystal facets of the TiO2 anatase nanoplates. This was achieved with the photoreduction of AgNO3 in methanol solution in which TiO2 anatase nanoplates were suspended while UVA irradiation was performed. The size range of the photodeposited silver na...
| Main Authors: | , , , |
|---|---|
| Format: | Journal Article |
| Published: |
Elsevier BV
2014
|
| Online Access: | http://hdl.handle.net/20.500.11937/51024 |
| Summary: | Ag nanoparticles were photodeposited on the {101} crystal facets of the TiO2 anatase nanoplates. This was achieved with the photoreduction of AgNO3 in methanol solution in which TiO2 anatase nanoplates were suspended while UVA irradiation was performed. The size range of the photodeposited silver nanoparticles was between 5 and 20nm. The manipulation of their size was achieved by controlling the UVA light irradiation period of time whereas the formation on the specific facet of the TiO2 anatase nanocrystal was managed by using methanol as a hole scavenger. The silver ions (Ag+) were photoreduced by the electrons that were photogenerated due to the TiO2 anatase nanoplates irradiation with UVA light. The photocatalytic activity of the nanocomposites was examined in NO oxidation, showing a higher photocatalytic activity and photonic efficiency in comparison to the pure TiO2 anatase nanoplates. © 2014 Elsevier B.V. |
|---|